Khaqqi, Sabila Azmil and Drs. Ir. Moch. Dhofir, M.T., and Prof. Dr. Ir. Rini Nur Hasanah, ST., M.Sc., IPU. ASEAN Eng., IEE (2023) Pengaruh Sinar Ultraviolet Dan Lapisan Bahan Silicon Rubber Pada Isolator Polyethylene Terhadap Sudut Kontak Dan Arus Bocor Dalam Kondisi Kering Dan Basah,. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini menguraikan tentang pengaruh variasi sinar ultraviolet, lapisan silicon rubber pada isolator terhadap tingkat arus bocor dan sudut kontak , dalam penelitian ini isolator terbuat dari polyethylene dengan dua variasi sudut yaitu sudut 120° dan 150° dimana terdapat dua isolator dengan kondisi berbeda yaitu pelapisan dan tanpa pelapisan. Metode penelitian yang digunakan adalah dengan mengambil data arus bocor dan sudut kontak secara langsung di Laboratorium Teknik Tegangan Tinggi Universitas Brawijaya, pengujian dilakukan dengan menggunakan tegangan AC dengan variasi tegangan uji 2 kV, 4 kV, 5 kV, 6 kV, 8 kV, 10 kV, 12 kV,14 kV, 15 kV, 20 kVdan 25 kV. Pengujian yang dilakukan menggunakan 2 kondisi untuk masing-masing isolator yaitu sebelum dan sesudah penyinaran sinar ultraviolet dengan variasi 12 dan 14 jam yang selanjutnya di uji pada kondisi kering dan kondisi basah dengan variasi debit pembasahan 10, 30, dan 60 mL/s yang mengacu pada tren curah hujan di Indonesia. Pengujian sudut kontak pada isolator menggunakan variasi penyinaran 0 jam, 2 jam, 4 jam, 6 jam, 8 jam, 10 jam, 12 jam, dan 14 jam. Hasil yang didapat dalam penelitian ini antara lain mengetahui tingkat arus bocor pada masing-masing isolator terutama membandingkan atara kondisi kering dan adanya kondisi basah dengan kenaikan debit pembasahan sehingga diketahui besar resistansi permukaan dan juga rugi daya yang ditimbulkan oleh isolator. Hasil yang didapat dari penelitian ini antara lain penambahan pelapisan menyebabkan meningkatnya sudut kontak serta berukurangnya arus bocor dan semakin besar penambahan sudut sirip maka akan menyebabkan kenaikan tingkat arus bocor, selain itu debit pembasahan juga berpengaruh terhadap arus bocor, dimana kenaikan tingkat arus bocor isolator berbanding lurus dengan penambahan debit pembasahan.
English Abstract
This study describes the effect of variations in ultraviolet light, the silicon rubber coating on the insulator on the level of leakage current and the contact angle, in this study the insulator is made of polyethylene with two variations of angles, namely angles of 120° and 150° where there are two insulators with different conditions, namely coating and no lining. The research method used is to take data on leakage current and contact angle directly at the High Voltage Engineering Laboratory, University of Brawijaya, the test is carried out using AC voltage with a variation of the test voltage of 2 kV, 4 kV, 5 kV, 6 kV, 8 kV, 10 kV , 12 kV, 14 kV, 15 kV, 20 kV and 25 kV. Tests were carried out using 2 conditions for each insulator, namely before and after ultraviolet light irradiation with variations of 12 and 14 hours which were then tested in dry conditions and wet conditions with variations in wetting discharge 10, 30, and 60 mL/s which refers to Rainfall trend in Indonesia. Testing the contact angle on the insulator using irradiation variations of 0, 2, 4, 6, 8, 10, 12, and 14 hours. The results obtained in this study include knowing the level of leakage current in each insulator, especially comparing dry conditions and the presence of wet conditions with an increase in wetting discharge so that the surface resistance is known and also the power loss caused by the insulator. The results obtained from this study include the addition of coating causing an increase in the contact angle and the size of the leak and the greater the addition of the fin angle will cause an increase in the leakage current level, besides that the wetting current discharge also affects the leakage current, where the increase in the insulator leakage current level is directly proportional with the addition of wetting discharge.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | '0523070140 |
| Uncontrolled Keywords: | Isolator polyethylene, sudut kontak, arus bocor, ultraviolet, silicone rubber, kondisi basah dan kering |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.3 Electrical, magnetic, optical, communications, computer engineering; electronics, lighting > 621.38 Electronics, communications engineering > 621.381 Electronics |
| Divisions: | Fakultas Teknik > Teknik Elektro |
| Depositing User: | Endang Susworini |
| Date Deposited: | 28 Jul 2023 03:39 |
| Last Modified: | 28 Jul 2023 03:39 |
| URI: | http://repository.ub.ac.id/id/eprint/202194 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Sabila Azmil Khaqqi.pdf Restricted to Registered users only until 31 December 2025. Download (3MB) |
Actions (login required)
 |
View Item |