Pengaruh Penambahan Chitosan Terhadap Nilai Thermal Properties Pada Polylactic Acid (PLA) Untuk Aplikasi Biomaterial

Akbar, Farel Naufal and ST., MT., Dr. Putu Hadi Setyarini, and ST., MT., Dr. Purnami, (2023) Pengaruh Penambahan Chitosan Terhadap Nilai Thermal Properties Pada Polylactic Acid (PLA) Untuk Aplikasi Biomaterial. Sarjana thesis, Universitas Brawijaya.

Abstract

Biomaterial atau biomedical material dapat didefinisikan secara umum sebagai suatu material baik natural maupun buatan manusia (sintetis) yang digunakan sebagai peralatan medis (medical devices) dan berinteraksi dengan sistem biologis dengan tujuan untuk memperbaiki (repair), memulihkan (restore), mengoreksi ketidak normalan, meningkatkan fungsi atau mengganti (replace) bagian tubuh yang mengalami kehilangan fungsi karena suatu penyakit atau trauma. Adanya interaksi dengan sistem biologis mengharuskan setiap bahan biomaterial memiliki sifat biokompatibilitas yaitu kemampuan suatu material untuk bekerja selaras dengan tubuh tanpa menimbulkan efek lain yang berbahaya. Polylactidacid (PLA) merupakan kategori plastik yang bio-based dan bio-degradable. Kitosan juga memiliki sifat osteokonduktivitas tinggi yang baik untuk meningkatkan regenerasi tulang. Penelitian tentang efektivitas penggunaan biomaterial kitosan dalam menunjang proses penyembuhan luka. Dalam penelitian ini, PLA dicampur dengan kitosan melalui proses ekstrusi untuk membuat filamen. Selanjutnya dilakukan proses injeksi molding untuk mendapatkan bentuk spesimen yang dibutuhkan. Pada proses injeksi molding menggunakan suhu nozzle 175 ˚C dengan tekanan 8 bar. Dilakukan pengujian thermogravimetric analysis (TGA), konduktivitas termal dan struktur mikro. Pada pengujian TGA didapatkan hasil temperatur degradasi, temperatur dekomposisi dan residu akhir pengujian yang menyimpulkan ketahanan termal paling optimal pada komposisi 4% Kitosan. Serta dengan pengujian konduktivitas termal membuktikan dengan penambahan kitosan pada campuran menurunkan nilai konduktivitas termal.

English Abstract

Biomaterials or biomedical materials can be defined in general as a material both natural and man-made (synthetic) that is used as medical devices and interacts with biological systems with the aim of repairing, restoring, correcting abnormalities, improve function or replace (replace) body parts that have lost function due to an illness or trauma. The existence of interactions with biological systems requires that every biomaterial material has biocompatibility properties, namely the ability of a material to work in harmony with the body without causing other harmful effects. Polylactidacid (PLA) is a category of plastic that is bio-based and bio-degradable. Chitosan also has high osteoconductivity properties which are good for increasing bone regeneration. Research on the effectiveness of using chitosan biomaterials in supporting the wound healing process. In this study, PLA was mixed with chitosan through an extrusion process to make filaments. Furthermore, the injection molding process is carried out to obtain the required specimen shape. The injection molding process uses a nozzle temperature of 175 ˚C with a pressure of 8 bar. Thermogravimetric analysis (TGA), thermal conductivity and microstructure tests were carried out. In the TGA test, the results of the degradation temperature, decomposition temperature and residue at the end of the test concluded that the optimal thermal resistance was at 4% chitosan composition. As well as by testing the thermal conductivity proves that the addition of chitosan to the mixture reduces the value of thermal conductivity.

Item Type:	Thesis (Sarjana)
Identification Number:	0522070444
Uncontrolled Keywords:	Polylactic Acid, Chitosan, Biomaterial, Injeksi Molding, Thermogravimetric Analysis, Konduktivitas Termal, Scanning Electron Microscope.
Subjects:	600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	PKN 02 UB
Date Deposited:	07 Jun 2023 02:40
Last Modified:	07 Jun 2023 02:40
URI:	http://repository.ub.ac.id/id/eprint/201026

Text (DALAM MASA EMBARGO) FAREL NAUFAL AKBAR.pdf Restricted to Registered users only until 31 December 2024. Download (2MB)

Actions (login required)

View Item