Pemanfaatan Serasah Daun Mangrove dengan Penambahan Polyvinyl Alcohol (PVA) sebagai Media Tanam Berbasis Hydrogel

Hasan, Mohamad Ibnu and Dr. Ir. Dwi Setijawati,, M.Kes. (2023) Pemanfaatan Serasah Daun Mangrove dengan Penambahan Polyvinyl Alcohol (PVA) sebagai Media Tanam Berbasis Hydrogel. Sarjana thesis, Universitas Brawijaya.

Abstract

Produksi serasah hutan mangrove di Indonesia diduga sekitar 40,40 C/ha/hari sampai 45,50 C/ha/hari dan sekitar 20,50 ton/ha/tahun sampai 29,35 ton/ha/tahun. Serasah mangrove menghasilkan bahan organik yang mengandung karbon (C), nitrogen (N), dan fosfor (P) yang dapat dimanfaatkan sebagai pupuk. Namun effisiensi irigasi tanpa penerapan teknologi masih tergolong sangat rendah, yaitu antara 30-50 persen. Alternatif lain yang digunakan untuk peningkatan efisiensi penggunaan irigasi pada lahan pertanian adalah dengan aplikasi teknologi polimer. Hydrogel merupakan polimer yang mampu menyerap dan melepas air tergantung stimulan eksternal yang diterima seperti pH, suhu, dan kelembaban media aplikasinya. Serasah daun mangrove dan Hydrogel dapat berpotensi untuk dimanfaatkan menjadi suatu produk inovatif, salah satunya adalah media tanam berbasis Hydrogel. Tujuan dari penelitian ini adalah untuk mengetahui apakah perbedaan konsentrasi PVA (Polyvinyl Alcohol) dan serasah daun mangrove berpengaruh terhadap karakteristik Hydrogel sebagai media tanam. Metode yang digunakan dalam penelitian adalah metode eksperimen dan menggunakan variabel bebas dan variabel terikat. Metode yang dilakukan meliputi proses pembuatan serasah daun mangrove, proses pembuatan Hydrogel, hingga dilakukan pengujian. Pengujian yang dilakukan yaitu uji daya serap air, uji fraksi gel, uji kadar air, uji WHC (Water Holding Capacity), uji NPK, dan uji pH. Selanjutnya dilakukan analisis data menggunakan Minitab 21. Kriteria penerimaan atau penolakan hipotesis statistik dapat dilihat dari nilai signifikansi atau p (probabilitas). Perlakuan tidak berpengaruh jika P>0.05 sedangkan jika P<0.05 maka perlakuan berpengaruh secara nyata, dimana tingkat kepercayaan 95% dan tingkat kesalahannya 5%. Jika didapatkan hasil yang berbeda nyata maka akan dilakukan uji lanjut tukey. Hasil penelitian menjelaskan bahwa pada pengujian daya serap air, uji fraksi gel, uji kadar air, WHC (Water Holding Capacity), pH dan uji NPK. Hasil yang didapatkan menunjukkan bahwa pengaruh penambahan serasah daun mangrove memberikan pengaruh berbeda nyata (P<0.05) terhadap produk Hydrogel. Pada pengujian NPK, hasil yang didapat pada pengujian N (Nitrogen) yaitu sebesar 2,93%, pada pengujian P (Fosfor) didapatkan hasil sebesar 3,16%, dan pada pengujian K (Kalium) hasil yang didapatkan yaitu sebesar 3,55%. Sedangkan pada uji pH, hasil tertinggi di dapatkan oleh perlakuan A4B1, A3B2, yaitu sebesar 7. Kesimpulan dari penelitian ini adalah Hasil analisis data menunjukkan bahwa penambahan serasah daun mangrove memberikan pengaruh dan berbeda nyata (P<0.05) terhadap Daya Serap Air, Fraksi Gel, Kadar Air maupun Water Holding Capacity (WHC) produk Hydrogel.

English Abstract

The production of mangrove forest litter in Indonesia is estimated to be around 40.40 C/ha/day to 45.50 C/ha/day and around 20.50 tonnes/ha/year to 29.35 tonnes/ha/year. Mangrove litter produces organic matter containing carbon (C), nitrogen (N) and phosphorus (P) which can be used as fertilizer. However, irrigation efficiency without the application of technology is still very low, namely between 30-50 percent. Another alternative used to increase the efficiency of irrigation use on agricultural land is the application of polymer technology. Hydrogel is a polymer that is able to absorb and release water depending on external stimuli such as pH, temperature, and humidity of the application medium. Mangrove leaf litter and Hydrogel have the potential to be used as innovative products, one of which is Hydrogel-based growing media. The purpose of this study was to determine whether differences in PVA (Polyvinyl Alcohol) concentrations and mangrove leaf litter affected the characteristics of Hydrogel as a planting medium. The method used in this research is an experimental method and uses independent variables and dependent variables. The method used includes the process of making mangrove leaf litter, the process of making Hydrogel, until testing is carried out. Tests carried out were water absorption test, gel fraction test, water content test, WHC (Water Holding Capacity) test, NPK test, and pH test. Furthermore, data analysis was carried out using Minitab 21. The criteria for accepting or rejecting the statistical hypothesis can be seen from the significance value or p (probability). The treatment has no effect if P>0.05 whereas if P<0.05 then the treatment has a significant effect, where the confidence level is 95% and the error rate is 5%. If significantly different results are obtained, a further Tukey test will be carried out. The results of the study explained that the water absorption test, gel fraction test, water content test, WHC (Water Holding Capacity), pH and NPK test. The results showed that the effect of adding mangrove leaf litter had a significantly different effect (P<0.05) on the Hydrogel product. In the NPK test, the results obtained in the N (Nitrogen) test were 2.93%, in the P (Phosphorus) test the results were 3.16%, and in the K (Potassium) test the results obtained were 3.55% . Whereas in the pH test, the highest results were obtained by treatments A4B1, A3B2, which was equal to 7. The conclusion of this study is that the results of data analysis showed that the addition of mangrove leaf litter had an effect and was significantly different (P<0.05) on the water absorption, gel fraction, water content and water holding capacity (WHC) of Hydrogel products.

Item Type: Thesis (Sarjana)
Identification Number: 0522080436
Subjects: 600 Technology (Applied sciences) > 639 Hunting, fishing & conservation > 639.2 Commercial fishing, whaling, sealing
Divisions: Fakultas Perikanan dan Ilmu Kelautan > Teknologi Hasil Perikanan
Depositing User: soegeng sugeng
Date Deposited: 30 May 2023 02:31
Last Modified: 30 May 2023 02:31
URI: http://repository.ub.ac.id/id/eprint/200634
[thumbnail of DALAM MASA EMBARGO] Text (DALAM MASA EMBARGO)
Mohamad Ibnu Hasan.pdf
Restricted to Registered users only until 31 December 2024.

Download (3MB)

Actions (login required)

View Item View Item