Sukadi, Zefanya Nicko and M.Si, Drg. Lalita El Milla (2022) Pengaruh Penambahan Nanofiller Hidroksiapatit dari Cangkang Telur Ayam terhadap Kekuatan Tarik Diametral RMGIC. Sarjana thesis, Universitas Brawijaya.
Abstract
Resin Modified Glass Ionomer Cement (RMGIC) merupakan modifikasi resin komposit dan Glass Ionomer Cement (GIC) konvensional untuk memadukan keunggulan ikatan geser resin komposit dengan pelepasan fluoride GIC. RMGIC memiliki sifat mekanik yang lebih unggul daripada GIC, salah satunya kekuatan tarik diametral yang penting untuk menghindari degradasi marginal dan fraktur. Namun, hal tersebut masih lebih rendah dibandingkan resin komposit. Untuk meningkatkan sifat mekanis tersebut dengan cara menambah nanofiller hidroksiapatit dari cangkang telur ayam. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan 5%, 8% dan 11% nanofiller hidroksiapatit dari cangkang telur ayam terhadap kekuatan tarik diametral RMGIC. Penelitian ini terdiri dari 4 kelompok sampel (kelompok kontrol, penambahan 5%, penambahan 8% dan penambahan 11%) dengan menggunakan 40 sampel masing-masing 10 buah untuk setiap kelompok. Sampel berbentuk tablet berdiameter 6 mm dan tinggi 3 mm. kekuatan tarik diametral diuji dengan menggunakan universal testing machine dengan beban kompresi maksimum 250 KgF pada kecepatan crosshead 0,5 mm/menit. Hasil pengukuran rata-rata kekuatan tarik diametral kelompok kontrol adalah 33,89 ± 5,10 Mpa, kelompok penambahan 5% adalah 24,27 ± 5,50 Mpa, kelompok penambahan 8% adalah 21,17 ± 3,66 MPa dan kelompok penambahan 11% adalah 22,41 ± 3,92 Mpa. Hasil uji One Way ANOVA diperoleh sig sebesar 0,000 yang menunjukkan terdapat perbedaan kekuatan tarik diametral RMGIC dengan atau tanpa penambahan 5%, 8% dan 11% nanofiller hidroksiapatit. Kesimpulan penelitian ini adalah terdapat pengaruh penambahan 5%, 8% dan 11% nanofiller hidroksiapatit dari cangkang telur ayam terdahap kekuatan tarik diametral RMGIC.
English Abstract
Resin Modified Glass Ionomer Cement (RMGIC) is a modified composite resin and conventional Glass Ionomer Cement (GIC) combines the advantages of shear bonding of composite resins with the release of GIC fluoride. RMGIC has superior mechanical properties than GIC, one of which is diametral tensile strength which is important to avoid marginal degradation and fracture. However, it is still lower than composite resin. To improve the mechanical properties by adding hydroxyapatite nanofiller from chicken egg shells. This study aims to determine the effect of the addition of 5%, 8% and 11% hydroxyapatite nanofiller from chicken egg shells on the diametral tensile strength of RMGIC. This study consisted of 4 sample groups (control group, 5% addition, 8% addition, and 11% addition) using 40 samples of 10 each for each group. Samples in the form of tablets with a diameter of 6 mm and a height of 3 mm. diametral tensile strength was tested using a universal testing machine with a maximum compression load of 250 KgF at a crosshead speed of 0.5 mm/min. The measurement results of the average diametral tensile strength of the control group were 33.89 ± 5.10 Mpa, the 5% addition group was 24.27 ± 5.50 Mpa, the 8% addition group was 21.17 ± 3.66 Mpa, and the 8% addition group 11% is 22.41 ± 3.92 Mpa. The results of the One Way ANOVA test obtained a sig of 0.000 which indicated that there were differences in the diametral tensile strength of RMGIC with or without the addition of 5%, 8% and 11% hydroxyapatite nanofiller. This study concluded that the addition of 5%, 8% and 11% hydroxyapatite nanofiller from chicken egg shells affected the diametral tensile strength of RMGIC.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0522140041 |
| Uncontrolled Keywords: | Resin Modified Glass Ionomer Cement (RMGIC), kekuatan tarik diametral, nanofiller hidroksiapatit, Resin Modified Glass Ionomer Cement (RMGIC), diametral tensile strength, hydroxyapatite nanofiller. |
| Subjects: | 600 Technology (Applied sciences) > 617 Surgery, regional medicine, dentistry, ophthalmology, otology, audiology > 617.6 Dentistry |
| Divisions: | Fakultas Kedokteran Gigi > Kedokteran Gigi |
| Depositing User: | Sugeng Moelyono |
| Date Deposited: | 15 May 2023 04:02 |
| Last Modified: | 15 May 2023 04:02 |
| URI: | http://repository.ub.ac.id/id/eprint/199554 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Zefanya Nicko Sukadi.pdf Restricted to Registered users only until 31 December 2024. Download (2MB) |
Actions (login required)
 |
View Item |