Abstract
Gigi tiruan adalah untuk memperbaiki atau mengembalikan fungsi efisiensi pengunyahan, meningkatkan pengucapan dan memperbaiki estetika. Gigi tiruan yang baik adalah dapat bertahan di tempatnya selama mungkin dan dapat berfungsi sebagaimana mestinya. Gigi tiruan yang menjadi pilihan utama pasien adalah Gigi Tiruan Resin akrilik dengan latar belakang ekonomi menengah ke bawah. Beberapa upaya yang dapat dilakukan untuk menambah kekuatan tekan pada bahan basis gigi tiruan Resin akrilik diantaranya dengan penambahan bahan pengisi ke dalam bahan basis gigi tiruan resin akrilik. Bahan Pengisi memiliki beberapa jenis menurut ukuran dan sumber antara lain mikro parktikel, nanopartikel dan anorganik serta organik. Maka dari itu kekuatan tekan sangat penting untuk gigi tiruan supaya tidak mudah patah saat terjatuh dan mengunyah makanan. Tujuan: Untuk mengetahui kekuatan tekan self-cured dan heat-cured acrylic pada berbagai penambahan bahan pengisi. Metode : Desain penelitian yang akan digunakan dalam penelitian ini yaitu kajian literatur dengan menggunakan kaidah penulisan PRISMA{Preferred Reporting Items for Systematic Reviews and Meta Analysis). Hasil: hasil pengukuran kekuatan tekan rata-rata dari berbagai brand heat cured-acrylic yaitu 22.72 (3.68) MPa sedangkan untuk self cured- acrylic yaitu 21.06 (3.13) MPa, setelah diisi bahan pengisi dengan menggunakan metode sintesa nanopartikel titanium dioksida kekuatan tekan heat cured adalah 215.001 MPa sedangkan kekuatan tekan self cured adalah 154.138 MPa. Kesimpulan: Nilai yang diperoleh heat cured lebih tinggi dari pada self cured. Namun dengan menggunakan metode lain nilai kekuatan tekan v antara heat cured dan self cured belum dapat dipastikan bahwa heat cured selalu lebih tinggi
English Abstract
Dentures are to improve or restore the function of masticatory efficiency, improve pronunciation and improve aesthetics. A good denture is able to stay in place as long as possible and can function as it should. The denture that is the patient's main choice is an acrylic resin denture with a middle to lower economic background. Several attempts can be made to increase the compressive strength of acrylic resin denture base materials, including by adding fillers to acrylic resin denture base materials. Fillers have several types according to size and source, including micro-particles, nanoparticles and inorganic and organic. Therefore compressive strength is very important for dentures so that they do not break easily when they fall and chew food. Objective: To determine the compressive strength of self- cured and heat-cured acrylic on various additions of fillers. Methods: The research design that will be used in this research is a literature review using the writing conventions of PRISMA (Preferred Reporting Items for Systematic Reviews and Meta Analysis). Result: the results of measuring the average compressive strength of various heat cured-acrylic brands were 22.72 (3.68) MPa while for self-cured-acrylic were 21.06 (3.13) MPa, after being filled with filler using the titanium dioxide nanoparticle synthesis method the heat cured compressive strength was 215,001 MPa while the compressive strength of self cured is 154.138 MPa. Conclusion: The value obtained by heat cured is higher than self cured. However, by using other methods the value of compressive strength between heat cured and self cured cannot be ascertained that heat cured is always higher.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0522140024 |
| Uncontrolled Keywords: | Gigi tiruan, Denture, Resin akrilik, Acrylic resin, Kekuatan tekan dan Compressive Strength, Gigi tiruan, Denture, Resin akrilik, Acrylic resin, Kekuatan tekan dan Compressive Strength. |
| Subjects: | 600 Technology (Applied sciences) > 617 Surgery, regional medicine, dentistry, ophthalmology, otology, audiology > 617.6 Dentistry |
| Divisions: | Fakultas Kedokteran Gigi > Kedokteran Gigi |
| Depositing User: | Sugeng Moelyono |
| Date Deposited: | 12 May 2023 01:28 |
| Last Modified: | 12 May 2023 01:28 |
| URI: | http://repository.ub.ac.id/id/eprint/199460 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Farhan Al Rasyid Munthe.pdf Restricted to Registered users only until 31 December 2024. Download (1MB) |
Actions (login required)
 |
View Item |