Pemanfaatan Ekstrak Kulit Nangka sebagai Inhibitor Korosi Ramah Lingkungan dalam Upaya Proteksi Logam dari Serangan Korosi.

Kusumaningrum, Ira and Prof. Dr. Ir. Rudy Soenoko, M.Eng. Sc. and Dr. Eng. Eko Siswanto, S,T., M.T. and Dr. Femiana Gapsari, S.T., M.T. (2022) Pemanfaatan Ekstrak Kulit Nangka sebagai Inhibitor Korosi Ramah Lingkungan dalam Upaya Proteksi Logam dari Serangan Korosi. Doktor thesis, Universitas Brawijaya.

Abstract

Logam merupakan material teknik yang paling banyak digunakan dan memegang peranan yang sangat penting dalam pesatnya perkembangan teknologi. Logam banyak dimanfaatkan untuk berbagai peralatan, komponen mesin, konstruksi dan lain-lain. Interaksi secara spontan antara logam dengan lingkungannya menyebabkan terjadinya degradasi logam atau yang disebut korosi. korosi logam dalam lingkungan basah melibatkan proses oksidasi pada anoda yang melepas elektron dan proses reduksi pada katoda yang menerima elektron. Kedua reaksi tersebut harus berjalan secara seimbang dan simultan serta memiliki laju reaksi yang sama melalui konduktor. Korosi dapat memberi dampak dalam bentuk bencana. Keselamatan merupakan pertimbangan penting, sehingga perlu dilakukan pengendalian korosi sejak tahap perencanaan hingga tahap pemakaian sebuah peralatan ataupun struktur. Pengendalian korosi dapat dilakukan dengan memodifikasi lingkungan. Penambahan inhibitor korosi ke dalam larutan elektrolit merupakan salah satu modifikasi terhadap lingkungan. Pada Penelitian disertasi ini, Ekstrak kulit nangka (EKN) dimanfaatkan sebagai inhibitor korosi guna melindungi logam dari serangan korosi. Konsep dari penelitian ini adalah inhibitor EKN yang ditambahkan ke dalam lingkungan korosif dapat menghambat laju reaksi anodik, reaksi katodik, atau reaksi anodik dan katodik. Perubahan potensial korosi setelah ditambah inhibitor ekstrak kulit nangka mengindikasikan bahwa proses korosi terhambat’ Mekanisme inhibitor EKN dalam menghambat laju korosi dapat dipelajari melalui proses adsorpsi inhibitor tersebut pada permukaan logam yang korosi. Molekul inhibitor EKN teradsorpsi pada permukaan logam melalui gaya tarik elektrostatik antara ion-ion ataupun dipol molekul inhibitor dengan permukaan logam yang bermuatan listrik. Adsorpsi ini disebut dengan adsorpsi secara fisika. Interaksi elektrostatik antara kation dan ion elektrolit yang telah teradsorpsi juga dapat terjadi ketika komponen terprotonasi dari molekul ekstrak kulit nangka teradsorpsi secara fisik. Proses adsorpsi ini membentuk lapisan adsorpsi yang dapat melindungi logam dari lingkungan korosif. Penelitian ini berhasil menunjukkan bahwa EKN dapat dijadikan inhibitor korosi yang dapat melindungi logam dari serangan korosi. Molekul-molekul EKN teradsorpsi pada permukaan baja karbon AISI 1037 ketika berada didalam larutan HCl 1 M. Molekul-molekul tersebut juga teradsorpsi pada permukaan tembaga ketika berada di dalam larutan HNO3. Hal yang sama juga terjadi pada permukaan kuningan ketika terendam dalam larutan NaCl 3.5%. Dengan demikian lapisan adsorpsi yang terbentuk dapat melindungi logam dari lingkungan korosifnya.

English Abstract

Metal is the most widely used engineering material and plays a very important role in the rapid development of technology. Metal is widely used for various equipment, machine components, construction and others. Spontaneous interaction between metals and their environment causes metal degradation or what is called corrosion. Metal corrosion in a wet environment involves an oxidation process at the anode which loses electrons and a reduction process at the cathode which accepts electrons. The two reactions must proceed in a balanced and simultaneous manner and have the same rate of reaction through the conductor. Corrosion can have an impact in the form of a disaster. Safety is an important consideration, so it is necessary to control corrosion from the initial stage to the stage of using the equipment or structure. Corrosion control can be done by modifying the environment. The addition of corrosion inhibitors in the electrolyte solution is one of the modifications to the environment. In this dissertation research, jackfruit peel extract (EKN) is used as a corrosion inhibitor to protect metals from corrosion attack. The concept of this research is that EKN inhibitors added to a corrosive environment can inhibit the rate of anodic reactions, cathodic reactions, or anodic and cathodic reactions. Changes in corrosion potential after adding jackfruit peel extract inhibitors that the corrosion process is inhibited' The mechanism of the EKN inhibitor in inhibiting the corrosion rate can be studied through the adsorption process of the inhibitor on the corroded metal surface. The EKN inhibitor molecule is adsorbed on the metal surface through electrostatic attraction between the ions or the dipole of the inhibitor molecule with an electrically charged metal surface. This adsorption is called physical adsorption. Electrostatic interactions between cations and electrolyte ions that have been adsorbed can also occur when the protonated components of jackfruit peel extract are physically adsorbed. This adsorption process is an adsorption layer that can protect the metal from the corrosive environment. This study succeeded in showing that EKN can be used as a corrosion inhibitor that can protect metals from corrosion attack. The EKN molecules were adsorbed on the surface of AISI 1037 carbon steel when in a 1 M HCl solution. The molecules were also adsorbed on the copper surface when in a HNO3 solution. The same thing happened to the brass surface when submerged in 3.5% NaCl solution. Thus the adsorption layer formed can protect from the corrosive environment.

Item Type:	Thesis (Doktor)
Identification Number:	0622070003
Uncontrolled Keywords:	laju korosi, efisiensi inhibitor, thermodinamika, aktivasi, adsorpsi .- corrosion rate, efficiency inhibitor, thermodynamics, activation, adsorption
Subjects:	600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering
Divisions:	S2/S3 > Doktor Teknik Mesin, Fakultas Teknik
Depositing User:	Endang Susworini
Date Deposited:	11 Apr 2023 01:17
Last Modified:	11 Apr 2023 01:17
URI:	http://repository.ub.ac.id/id/eprint/198109

Text (DALAM MASA EMBARGO) IRA KUSUMANINGRUM.pdf Restricted to Registered users only until 31 December 2024. Download (10MB)

Actions (login required)

View Item