Pengaruh Bombardir Partikel Bermuatan Terhadap Sifat Fisik Pelat Aluminium Dengan Dielektrik Gas Tetrafluoroetana Dalam Medan Tinggi DC Non-Homogen

Sabilli, Ibnu and Drs. Ir. Moch. Dhofir, M.T. and Ir. Mahfudz Shidiq, M.T. (2022) Pengaruh Bombardir Partikel Bermuatan Terhadap Sifat Fisik Pelat Aluminium Dengan Dielektrik Gas Tetrafluoroetana Dalam Medan Tinggi DC Non-Homogen. Sarjana thesis, Universitas Brawijaya.

Abstract

Buku skripsi ini menjelaskan hasil penelitian tentang pengaruh bombardir partikel ion positif terhadap sifat fisik pelat aluminium dengan dielektrik gas tetrafluoroetana menggunakan medan tinggi DC. Diawali dengan membahas teori terkait penelitian seperti Hukum Coulomb, efek polaritas, teorema medan dan energi kinetik partikel. Selanjutnya dilakukan pengambilan data berupa nilai tegangan korona, tegangan tembus dan tegangan uji pada variasi tekanan, jarak sela dan tegangan uji. Selanjutnya dilakukan pengambilan gambar struktur mikro permukaan pelat aluminium dengan Scanning Electron Microscope (SEM) untuk menunjukkan kerusakan akibat bombardir ion positif dengan pembesaran hingga 620 kali. Setiap satu kali pengukuran dilakukan pergantian elektroda pelat untuk melihat struktur mikro permukaan pelat akibat bombardir pada kondisi yang berbeda. Selanjutnya dilakukan analisis untuk mengetahui besar energi kinetik partikel ion sebelum menumbuk pelat aluminium. Variasi kondisi pengujian yang digunakan dalam pengujian tegangan korona dan tembus meliputi perubahan jarak sela 2,5 cm dan 5 cm, serta perubahan tekanan dielektrik gas tetrafluoroetana yang divariasi dari 555 mBar hingga tekanan normal. Bombardir partikel bermuatan dalam suatu kondisi ditemukan terjadi hanya jika nilai tegangan mampu menyebabkan ionisasi pada gas. Bombardir partikel terkuat terjadi dengan kecepatan ion 23.736,22 m/s dengan energi kinetik partikel 2,98 eV. Terdapat kerusakan pada permukaan pelat aluminium akibat bentuk geometris elektroda yang tidak homogen. Disimpulkan bahwa pada nilai tegangan yang sama, penurunan nilai tekanan menyebabkan jumlah molekul bebas dalam ruang semakin sedikit sehingga jarak bebas ion positif semakin besar dan ion mampu bergerak dengan kecepatan yang lebih tinggi. Kenaikan kecepatan ion berakibat pada kenaikan nilai energi kinetik ion positif.

English Abstract

This thesis book describes the results of research on the effect of positive ion particle bombardment on the physical properties of aluminum plates with tetrafluoroethane gas dielectric using a high DC field. It begins by discussing research�related theories such as Coulomb's law, polarity effects, field theorem, and particle kinetic energy. Furthermore, data collection in the form of corona voltage, breakdown voltage, and test voltage was carried out on variations in pressure, gap, and test voltage. Furthermore, the microstructure of the surface of the aluminum plate was taken with a Scanning Electron Microscope (SEM) to show the damage caused by positive ion bombardment with magnification up to 620 times. Each time a measurement is made, the plate electrode is changed to see the microstructure of the plate surface due to bombardment under different conditions. Furthermore, an analysis was carried out to determine the kinetic energy of the ion particles before hitting the aluminum plate. Variations of test conditions used in the corona and breakdown voltage tests include changes in the distance between 2.5 cm and 5 cm, as well as changes in the dielectric pressure of tetrafluoroethane gas which is varied from 555 mBar to normal pressure. The bombardment of charged particles under a given condition is found to occur only if the voltage value is capable of causing ionization of the gas. The strongest particle bombardment occurred with an ion velocity of 23,736.22 m/s with a particle kinetic energy of 2.98 eV. There is damage to the surface of the aluminum plate due to the inhomogeneous geometric shape of the electrode. It is concluded that at the same voltage value, decreasing the pressure value causes the number of free molecules in the space to decrease so that the free distance of positive ions is greater and the ions can move at a higher speed. The increase in ion velocity results in an increase in the value of the positive ion kinetic energy.

Item Type:	Thesis (Sarjana)
Identification Number:	0522070330
Uncontrolled Keywords:	Ionisasi, ion positif, bombardir partikel, gas tetrafluoroetana. .- Ionization, positive ions, particle bombardment, tetrafluoroethane gas.
Subjects:	600 Technology (Applied sciences) > 621 Applied physics > 621.3 Electrical, magnetic, optical, communications, computer engineering; electronics, lighting > 621.38 Electronics, communications engineering > 621.381 Electronics
Divisions:	Fakultas Teknik > Teknik Elektro
Depositing User:	Endang Susworini
Date Deposited:	06 Apr 2023 01:51
Last Modified:	06 Apr 2023 01:51
URI:	http://repository.ub.ac.id/id/eprint/198041

Text (DALAM MASA EMBARGO) Ibnu Sabilli.pdf Restricted to Registered users only until 31 December 2024. Download (4MB)

Actions (login required)

View Item