Manurung, Andreas and Dr. Putu Hadi Setyarini, ST., MT. and Prof. Dr. Ir. Rudy Soenoko, M. Eng.Sc. (2022) Pengaruh Variasi Katoda dalam Proses Anodizing pada Kekasaran Permukaan dan Sudut Kontak pada Aluminium 1038. Sarjana thesis, Universitas Brawijaya.
Abstract
Aluminium adalah logam kedua yang paling banyak tersedia di bumi dan menjadi salah satu material yang banyak digunakan dalam berbagai aplikasi. Aluminium banyak digunakan pada komponen otomotif, pengemasan makanan dan minuman, konstruksi bangunan, konduktor listrik, alat pertahanan dan kedirgantaraan, serta mesin dan perkakas lainnya. Ringan, mudah diproduksi, sifat fisik dan sifat mekanik yang dapat divariasikan sesuai kebutuhan merupakan sifat-sifat yang dimiliki oleh aluminium. Namun aluminium memiliki kekurangan yaitu tidak bisa menahan laju korosi akibat pengaruh destruktif lingkungan, kekuatan dan ketangguhan aluminium akan menurun akibat korosi tersebut. Diperlukan adanya proses anodizing untuk menambah ketahanan aluminium terhadap korosi. Anodizing adalah proses elektrokimia yang memengaruhi respon pertumbuhan lapisan alumina oksida (Al2O3) yang lebih tebal sehingga dapat meningkatkan sifat-sifat fisik dan kkimia dari aluminium tersebut. Maka tujuan dari penelitian ini untuk mengetahui pengaruh variasi katoda dalam proses anodizing terhadap kekasaran permukaan dan sudut kontak aluminium 1038. Katoda yang digunakan adalah aluminium, karbon, stainless steel, dan titanium. Metode yang digunakan dalam penelitian ini adalah eksperimental dimana kekasaran permukaan diukur dengan alat AFM Neos S8 dan sudut kontak menggunakan kamera. Hasil dari penelitian ini didapatkan bahwa pengaruh variasi katoda ditunjukkan dengan adanya perubahan permukaan pada aluminium. Hal ini dibuktikan dengan adanya perbedaan nilai kekasaran permukaan Sa melalui alat AFM dan terdapat perubahan nilai sudut kontak, sliding angle, dan sudut tetesan jarak jauh pada permukaan antara aluminium tanpa perlakuan dan aluminium dengan anodizing variasi katoda. Pada perlakuan anodizing dengan menggunakan katoda aluminium memiliki nilai Sa terendah sebesar 42.7 nm, sudut kontak tertinggi 87o, sliding angle 61o, dan sudut tetesan jarak jauh 53o. Hal ini menunjukkan bahwa didapatkan permukaan yang lebih halus dan memiliki sifat menolak air yang lebih baik dibandingkan spesimen lainnya
English Abstract
Aluminum is the second most widely available metal on earth and is one of the most widely used materials in a wide variety of applications. Aluminum is widely used in automotive components, food and beverage packaging, building construction, electrical conductors, defense and aerospace equipment, and other machinery and tools. Light weight, easy to manufacture, physical properties and mechanical properties that can be varied as needed are the properties possessed by aluminum. However, aluminum has the disadvantage that it cannot withstand the corrosion rate due to the destructive influence of the environment, the strength and toughness of aluminum will decrease due to the corrosion. Anodizing process is needed to increase aluminum's resistance to corrosion. Anodizing is an electrochemical process that affects the growth response of a thicker layer of alumina oxide (Al2O3) so that it can improve the physical and chemical properties of the aluminum. So the purpose of this study was to determine the effect of cathode variations in the anodizing process on the surface roughness and contact angle of aluminum 1038. The cathodes used were aluminum, carbon, stainless steel, and titanium. The method used in this research is experimental in which the surface roughness is measured with the AFM Neos S8 and the contact angle using a camera. The results of this study showed that the effect of cathode variation was indicated by the surface changes on the aluminum. This is evidenced by the difference in the value of the surface roughness Sa through the AFM tool and there is a change in the value of the contact angle, sliding angle, and long-distance drop angle on the surface between aluminum without treatment and aluminum with cathode variation anodizing. The anodizing treatment using aluminum cathode had the lowest Sa value of 42.7 nm, the highest contact angle of 87o, sliding angle of 61o, and long distance drop angle of 53o. This shows that a smoother surface is obtained and has better water repellent properties than other specimens.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0522070283 |
| Uncontrolled Keywords: | Aluminium 1038, Anodizing, Kekasaran Permukaan, Sudut Kontak, AFM Neos S8 .- Aluminum 1038, Anodizing, Surface Roughness, Contact Angle, AFM Neos S8 |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics 600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Endang Susworini |
| Date Deposited: | 03 Apr 2023 06:13 |
| Last Modified: | 03 Apr 2023 06:13 |
| URI: | http://repository.ub.ac.id/id/eprint/197829 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Andreas Manurung.pdf Restricted to Registered users only until 31 December 2024. Download (5MB) |
Actions (login required)
 |
View Item |