Abed, Ahmed Wisam and Redi Bintarto, ST., M.Eng.Pract. and Moch. Syamsul Ma’arif, ST., MT (2022) The Effect Of Velocity Of Fluid Metal On Defect Characteristics Of Sand-Casting Product. Sarjana thesis, Universitas Brawijaya.
Abstract
Pekerjaan ini melibatkan analisis pengecoran dari mekanika fluida dalam hubungannya dengan cacat porositas. Sistem gating memainkan peran penting dalam proses pengecoran Manufaktur. Itu sistem penuangan memiliki berbagai elemen seperti cangkir tuang, Gates, Fountains, Runners, Riser dan Ingates. Fungsi dari sistem gating adalah untuk menyediakan logam cair memasuki cetakan rongga melalui berbagai elemen sistem gating. Pengecoran adalah proses pembentukan logam yang digunakan untuk menghasilkan bagian cor. Proses pengecoran tersebut tergantung dari bahan, jenis pola, bentuk, dll. Pasir pengecoran, pengecoran investasi, pengecoran mati, pengecoran pemerasan dan busa teknologi busa yang hilang pengecoran. Laporan ini mengadopsi metode pengecoran pasir. proses penuangan untuk pembuatan coran kecil hingga besar, bentuk kompleks, bagian presisi, dan banyak lagi. Pengecoran yang sempurna adalah prasyarat penting untuk kekuatannya. Perancangan sistem gating yang efektif dan efisien adalah suatu keharusan untuk pengecoran tanpa cacat. Ada berbagai cacat seperti pori-pori, lubang kecil, dan pori-pori Pengisian tidak lengkap yang dapat terjadi dengan pengecoran pasir. Perangkat lunak simulasi seperti Magma Soft dan Nova Flow Solid digunakan untuk memprediksi kemungkinan cacat pada coran. Itu Kemungkinan penggunaan simulasi untuk meningkatkan kualitas produk dan meningkatkan produktivitas. itu juga membantu Mengurangi memo tingkat dengan mengidentifikasi dan mengendalikan kesalahan. Turbulensi permukaan selama pengisian cetakan memicu entrainment film oksida, yang tampaknya merusak kesehatan pengecoran akhir. Sistem nonpressurized dan bottom-gating telah digunakan untuk itu menghindari cacat pengecoran tersebut dengan mengurangi kecepatan permukaan logam cair. Namun, studi terbaru menunjukkan bahwa kecepatan depan lelehan di pintu masuk cetakan dapat melebihi nilai kritis dalam sistem nonpressurized dan bottom-gating. Oleh karena itu, sebuah penelitian adalah dilakukan simulasi numerik pola aliran lelehan pada nonpressurized dan bottom-gating sistem.
English Abstract
This work involves analysing the casting from fluids mechanics in conjunction with porosity defect. Gating system plays an important role in casting Manufacturing process. The pouring system has various elements such as pouring cups, Gates, Fountains, Runners, Risers and Ingates. The function of the gating system is to provide Molten metal enters the mold cavity through various elements of the gating system. Casting is a metal forming process used to produce cast parts. That Casting process depends on material, pattern type, shape, etc. Sand casting, investment casting, die casting, squeeze casting and lost foam technology foam casting. This report adopts the sand-casting method. pouring process for the manufacture of small to large castings, complex shapes, precision parts, and many more. A flawless casting is an important prerequisite for its strength. That Effective and efficient gating system design is a must for zero defects casting. There are various defects such as pores, pinholes, and pores Incomplete filling that can occur with sand casting. Simulation software such as Magma Soft and Nova Flow Solid are used to predict possible defects in castings. That Possible uses of simulation to improve product quality and increase productivity. it also helps Reduce scrap rates by identifying and controlling errors. Surface turbulence during the filling of the mold triggers the entrainment of oxide films, which appears to be detrimental to the soundness of the final casting. Nonpressurized and bottom-gating systems have been employed in order to avoid such casting defects by reducing the surface velocity of the liquid metal. However, recent studies have shown that the melt front velocity in the mold entrance may exceed the critical value in the nonpressurized and bottom-gating systems. Therefore, a study was conducted.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0522070273 |
| Uncontrolled Keywords: | Pengecoran Pasir, Kecepatan, Cacat, Sistem Gerbang, Logam Cair, Cetakan, Simulasi .- Sand Casting, Velocity, Defects, Gating System, Molten Metal, Mold, Simulation |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Endang Susworini |
| Date Deposited: | 03 Apr 2023 02:58 |
| Last Modified: | 03 Apr 2023 02:58 |
| URI: | http://repository.ub.ac.id/id/eprint/197806 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Ahmed Wisam Abed.pdf Restricted to Registered users only until 31 December 2024. Download (4MB) |
Actions (login required)
 |
View Item |