Pengaruh Tekanan Chamber Dan Laju Alir Gas Pada Proses Modifikasi Permukaan Polistiren Menggunakan Metode Plasma Rf Dengan Dc Bias

Bakar, Abu and Dr. Eng. Masruroh,, S.Si., M.Si and Ir. D. J. Djoko H. Santjojo,, M.Phil., Ph.D (2019) Pengaruh Tekanan Chamber Dan Laju Alir Gas Pada Proses Modifikasi Permukaan Polistiren Menggunakan Metode Plasma Rf Dengan Dc Bias. Magister thesis, Universitas Brawijaya.

Abstract

Telah dilakukan perlakuan plasma nitrogen menggunakan metode plasma RF dengan DC bias di atas permukaan polistiren dengan variasi tekanan chamber dan laju alir gas. Tujuan dari penelitian ini untuk menganalisis pengaruh tekanan dan laju alir terhadap karakter plasma dan sifat hidrofobisitas permukaan polistiren di atas quart crystal microbalance (QCM) sensor. Pelarut toluena digunakan untuk melarutkan polistiren dan larutan polistiren dideposisikan di atas permukaan QCM dengan teknik spin coating. Perlakuan plasma nitrogen dilakukan dengan variasi tekanan chamber 40, 50, 60, 70, dan 80 Pa dengan parameter konstan laju alir 60 ml/menit, tegangan RF 90 volt dan DC bias 400 volt. Sedangkan variasi laju alir 20, 30, 40, 50, 60, dan 70 ml/menit dengan parameter konstan laju alir 60 ml/menit, tegangan RF 90 volt dan DC bias 400 volt. Spesies plasma diukur dengan optical emission spectroscopy (OES) Aurora 400 berupa panjang gelombang dan intensitas.

English Abstract

Nitrogen plasma treatment by means of RF method with DC plasma bias of a polystyrene surface with variation in flow rate has been carried out. The purpose of this analyze was to analyze the effect of the nitrogen pressure and flow rate during the treatment on the hydrophobicity properties of polystyrene surfaces on a quartz crystal microbalance (QCM) sensor. The toluene solvent used to dissolve polytyrene and then a solution polystyrene deposited on the surface of a QCM by a spin coating technique. The plasma treatment was carried out by varying the pressure chamber 40, 50, 60, 70, and 80 Pa with constant parameters the flow rate is 60 ml / minute, 90 volt RF voltage and 400 volt DC

Item Type:	Thesis (Magister)
Identification Number:	TES/530.44/FMIPA/p/2019/041903927
Subjects:	500 Natural sciences and mathematics > 530 Physics > 530.4 States of matter > 530.44 Plasma physics
Divisions:	S2/S3 > Magister Fisika, Fakultas MIPA
Depositing User:	Nur Cholis
Date Deposited:	23 Aug 2022 02:25
Last Modified:	23 Aug 2022 02:30
URI:	http://repository.ub.ac.id/id/eprint/193426

Text ABU BAKAR.pdf Download (4MB)

Actions (login required)

View Item