Perbedaan Kapasitas Penyerapan Air (Swelling) Membran Nanohidroksiapatit Magnesium Oksida (nHA/MgO) dan Membran Hidroksiapatit Magnesium Oksida (HA/MgO) dengan Metode Gravimetri.

Aziz, Shaffiratul and drg. Ariyati Retno Pratiwi,, M.Kes (2020) Perbedaan Kapasitas Penyerapan Air (Swelling) Membran Nanohidroksiapatit Magnesium Oksida (nHA/MgO) dan Membran Hidroksiapatit Magnesium Oksida (HA/MgO) dengan Metode Gravimetri. Sarjana thesis, Universitas Brawijaya.

Abstract

Latar Belakang: Kehilangan gigi dapat menyebabkan perubahan bentuk anatomis tulang alveolar dan merupakan proses yang irreversible sehingga diperlukan socket grafting. Salah satu biomaterial untuk socket grafting adalah alloplast. Salah satu bahan yang termasuk alloplast adalah hidroksiapatit yang mana memiliki laju degradasi yang lambat. Karena kelemahan yang dimilikinya maka diperlukan perbaikan melalui nanoteknologi serta penambahan magnesium oksida. Laju degradasi berkaitan dengan kapasitas penyerapan air yang mana peningkatan kapasitas penyerapan air selalu diikuti oleh peningkatan laju degradasi. Tujuan: Mengetahui perbedaan kapasitas penyerapan air (swelling) membran NanoHidroksiapatit – Magnesium Oksida (nHA/MgO) dengan membran Hidroksiapatit – Magnesium Oksida (HA/MgO). Metode: Penelitian ini menggunakan metode gravimetri yang mana sampel direndam dalam larutan PBS selama 15 menit. Kemudian data dianalisis menggunakan uji One Way Anova. Hasil: Pada membran HA/MgO semakin besar konsentrasi MgO maka terjadi penurunan kapasitas penyerapan air (swelling). Sedangkan pada membran nHA/MgO semakin besar konsentrasi MgO maka terjadi peningkatan kapasitas penyerapan air. Kesimpulan: Pada membran HA/MgO kapasitas penyerapan air (swelling) cenderung menurun. Sedangkan, pada membran nHA/MgO cenderung meningkat.

English Abstract

Background: Tooth loss can lead to changes in the alveolar bone that require socket grafting. One of the biomaterials for socket grafting is alloplast. One of the materials including alloplast is hydroxyapatite which has a slow degradation rate. Because of its weaknesses, it is necessary to be improved through nanotechnology and the addition of magnesium oxide. The degradation rate is related to water absorption capacity. The increasing of water absorption capacity (swelling) always followed by the enhancement of degradation rate. Objective: To determine the difference of water absorption capacity (swelling) of NanoHydroxyapatite membrane - Magnesium Oxide (nHA / MgO) with Hydroxyapatite membrane - Magnesium Oxide (HA / MgO). Method: This study used gravimetric method in which the sample was immersed in PBS solution for 15 minutes. Then the data were analyzed using One Way Anova test. Results: The higher concentration of MgO in HA / MgO membrane shows a decrease in water absorption capacity. Whereas on the nHA / MgO the higher concentration of MgO shows an increase in water absorption capacity. Conclusion: HA / MgO membrane water absorption capacity (swelling) tends to decrease. Meanwhile, the nHA / MgO membrane tends to increase.

Item Type:	Thesis (Sarjana)
Identification Number:	0520140090
Uncontrolled Keywords:	Swelling, Hidroksiapatit, Nanohidroksiapatit, Magnesium Oksida, Gravimetri,swelling, hydroxyapatite, nanohydroxiapatite, magnesium oxide, gravimetry
Subjects:	600 Technology (Applied sciences) > 617 Surgery, regional medicine, dentistry, ophthalmology, otology, audiology > 617.6 Dentistry
Divisions:	Fakultas Kedokteran Gigi > Kedokteran Gigi
Depositing User:	Sugeng Moelyono
Date Deposited:	05 Jul 2022 02:02
Last Modified:	05 Jul 2022 02:02
URI:	http://repository.ub.ac.id/id/eprint/191524

Text (DALAM MASA EMBARGO) Shaffiratul Aziz.pdf Restricted to Registered users only until 31 December 2023. Download (2MB)

Actions (login required)

View Item