Perbedaan Kekerasan Permukaan Antara Resin Komposit Nanohybrid dan Resin Komposit Nanohybrid Hidroksiapatit Kitosan

Padmarini, Areta and Dr. drg. M. Chair Effendi,, SU., Sp.KGA (2021) Perbedaan Kekerasan Permukaan Antara Resin Komposit Nanohybrid dan Resin Komposit Nanohybrid Hidroksiapatit Kitosan. Sarjana thesis, Universitas Brawijaya.

Abstract

Latar Belakang: Banyaknya factor yang menyebabkan perubahan kekerasan permukaan komposit. Perkembangan nanoteknologi dalam nanokomposit organic-anorganik. Bahan hidroksiapatit kitosan (HA/Cs) memiliki komposisi dan struktur Kristal apatit yang mirip dengan jaringan keras seperti struktur gigi dan tulang manusia. Beberapa penelitian telah dilakukan untuk mengetahui pengaruh penambahan hidroksiapatit untuk memperbaiki sifat mekanis dari bahan restoratif gigi. Tujuan: Mengetahui perbedaan kekerasan permukaan pada resin komposit nanohybrid dan resin komposit nanohybrid kitosan. Metode: Sampel dibagi menjadi 4 kelompok. Kelompok 1 sebagai kelompok control tanpa penambahan kitosan, kelompok 2 sebagai kelompok dengan penambahan kitosan 3%, kelompok 3 sebagai kelompok dengan penambahan kitosan 5%,kelompok 4 sebagai kelompok dengan penambahan kitosan 7%. Masing-masing kelompok dilakukan uji kekerasan permukaan dengan alat Vickers Microhardness Tester. Data dianalisis menggunakan uji One Way Anova. Hasil: Rata-rata kekerasan permukaan resin komposit nanohybrid tanpa penambahan kitosan (control) adalah 63.70 HV, sedangkan rata-rata kekerasan permukaan resin komposit nanohybrid dengan penambahan kitosan 3%, 5%, dan 7% adalah masing-masing sebesar 78.15 HV, 84.90 HV, dan 90.33 HV. Penambahan siginfikan dimulai dari penambahan hidroksiapatit kitosan (HA/Cs) 3%, 5%, dan 7%. Kesimpulan: Penambahan HA/Cs pada bahan restorasi gigi komposit nanohybrid dapat meningkatkan kekerasan permukaan.

English Abstract

Background: Many factors can caused the changes in surface hardness of composite restorative material. The development of nanotechnology include nanocomposite organic and anorganic. Hydroxyapatite chitosan (HA/Cs) has composition and crystal apatite structure which resembles human’s hard tissues like teeth and bone structures. Few researches have been done to see the result of adding HA/Cs to fix and improve the mechanical characters of composite dental restorative material. Objective: Learning the difference of surface hardness in composite nanohybrid and composite nanohybrid chitosan Method: Samples are grouped by 4 different groups. 1st group is composite nanohybrid without chitosan being added (control group), while 2nd, 3rd, and 4th group are composite nanohybrid with 3%, 5%, and 7% chitosan added respectively. Each groups are tested with Vickers Microhardness Tester to see each group’s surface hardness score. Data is analysed with One Way Anova Test. Result: The mean surface hardness of 1st group which is composite nanohybrid dental restorative material with no HA/Cs added is 63.70 HV, while the mean surface of 2nd, 3rd, and 4th group which consists of composite nanohybrid with 3%, 5%, and 7% chitosan added are 78.15 HV, 84.90 HV, and 90.33 HV respectively. Significant differences began with 3%, 5%, and 7% HA/Cs added. Conclusion: The incorporation of HA/Cs in restorative dental material composite nanohybrid can increase the surface hardness of the material.

Item Type:	Thesis (Sarjana)
Identification Number:	0521140005
Uncontrolled Keywords:	Hidroksiapatit kitosan, resin komposit nanohybrid, Kekerasan permukaan,Hydroxyapatite Chitosan, Nano Hybrid Composite, Surface Hardness
Subjects:	600 Technology (Applied sciences) > 617 Surgery, regional medicine, dentistry, ophthalmology, otology, audiology > 617.6 Dentistry
Divisions:	Fakultas Kedokteran Gigi > Kedokteran Gigi
Depositing User:	soegeng sugeng
Date Deposited:	17 Jun 2022 01:14
Last Modified:	17 Jun 2022 01:14
URI:	http://repository.ub.ac.id/id/eprint/190937

Text (DALAM MASA EMBARGO) Areta Padmarini.pdf Restricted to Registered users only until 31 December 2023. Download (2MB)

Actions (login required)

View Item