Rahmawati, Ida and Dra. Sri Wardhani, M.Si., and Siti Mutrofin,, S.Si., M.Sc., (2021) Sintesis Granul TiO₂-Fe₂O₃ Bentonit/Alginat Untuk Fotodegradasi Metil Jingga dengan Sinar UV. Sarjana thesis, Universitas Brawijaya.
Abstract
Sintesis Granul TiO₂-Fe₂O₃-Bentonit/Alginat dilakukan untuk mendegradasi metil jingga dengan sinar UV. TiO₂ dimodifikasi dengan menambahkan dopan Fe dan diembankan ke bentonit. Sintesis Granul TiO₂-Fe₂O₃-Bentonit/Alginat dibuat dengan komposisi Fe dalam TiO₂-Fe₂O₃ dengan perbandingan mol 97:1, 97:2, dan 97:3 yang diimpregnasikan ke dalam bentonit. Fotokatalis hasil sintesis dikarakterisasi dengan FTIR dan XRD. Fotokatalis sebanyak 100 mg diuji aktivitasnya menggunakan 25 mL larutan metil jingga 10 mg/L. Parameter fotodegradasi yang dilakukan adalah pengaruh konsentrasi Fe (0,001; 0,002; dan 0,003 mol/g), lama penyinaran (1; 1,5; 2; 2,5;, dan 3 jam), dan Variasi pH (2, 3, 5, 7, 9, 11). Filtrat larutan metil jingga setelah degradasi diukur absorbansinya dengan spektrofotometer UV-Vis pada λ = 464 nm untuk menentukan konsentrasi metil jingga. Karakterisasi dengan FTIR menunjukkan adanya serapan Ti—O—Ti pada bilangan gelombang 436,42 cm⁻¹ dan serapan Fe—O bilangan gelombang 517,71 cm⁻¹. Karakterisasi dengan XRD diketahui struktur TiO₂ adalah anatase dan rutil pada 2θ = 25,30° dan 27,43° serta terdapat nilai 2θ = 33,50° yang menunjukkan pola difraksi Fe₂O₃. Uji aktivitas menunjukkan dopan Fe dapat meningkatkan aktivitas degradasi TiO₂. Uji pengaruh konsentrasi Fe, lama penyinaran, dan pH menghasilkan kondisi optimum konsentrasi Fe 0,001 mol/g, lama penyinaran optimun selama 2 jam, dan pH 3. Pada kondisi optimum fotokatalis diperoleh degradasi metil jingga sebesar 44%.
English Abstract
Synthesis TiO₂-Fe₂O₃-Bentonite/Alginate granules were prepared with the composition of Fe in TiO₂-Fe₂O₃ with mole ratios of 97:1, 97:2, and 97:3 impregnated into bentonite. The synthesized photocatalysts were characterized by FT-IR and XRD. The activity of 100 mg of photocatalyst was tested using 25 mL of 10 mg/L methyl orange solution. The photodegradation parameters carried out were the effect of Fe concentration (0.001; 0.002; and 0.003 mol/g), irradiation time (1, 1.5, 2, 2.5, and 3 hours), and pH variations. (2, 3, 5, 7, 9, 11). The methyl orange solution filtrate after degradation was measured for absorbance with UV-Vis spectrophotometer at 464 nm to determine the concentration of methyl orange. Characterization with FTIR showed Ti-O-Ti absorption at 436.42 cm⁻¹ and Fe-O absorption at 517.71 cm⁻¹. Characterization by XRD revealed that the structure of TiO₂ is anatase and rutile there is vaue of 2θ at 25.30° and 27.43° and there is a value of 2θ at 33.50° which shows the diffraction pattern of Fe₂O₃. The activity test showed that Fe dopant could increase TiO₂ degradation activity. The test of the effect of Fe concentration, irradiation time, and pH resulted optimum condition in a Fe concentration of 0.001 mol/g %, an optimal 2-hour irradiation time, and pH 3. At the optimum condition of photocatalysis, degradation of methyl orange was obtained by 44%
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0521090027 |
| Uncontrolled Keywords: | Bentonit, Fotokatalis, Metil Jingga, TiO₂-Fe₂O₃ |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | agung |
| Date Deposited: | 17 May 2022 07:43 |
| Last Modified: | 18 May 2022 03:14 |
| URI: | http://repository.ub.ac.id/id/eprint/190530 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
SKRIPSI_FMIPA_IDA RAHMAWATI_175090200111005.pdf Restricted to Registered users only until 31 December 2023. Download (4MB) |
Actions (login required)
 |
View Item |