Las gesek (Friction Welding) merupakan metode pada proses menyambungkan antara dua material logam. Pada metode las gesek ini panas berasal dari gesekan yang terjadi pada gerak putar disertai tekanan sehingga mengakibatkan adanya panas yang terjadi sampai pada fase solid sehingga menyebabkan terjdinya proses pengelasan. Penelitian ini bertujuan untuk mengetahui pengaruh variasi sudut chamfer dan burn-off length terhadap distribusi suhu dan luas flash pada sambungan las gesek Al6061 dan ST41. Metodologi penelitian ini menggunakan metode simulasi komputer dengan perangkat lunak berbasis metode elemen hingga, Ansys Workbench 19.2. Menggunakan model material bilinear isotropic hardening, dengan Analisis transient thermal untuk mendapatkan suhu dan static structural digunakan untuk memperoleh flash. Sudut chamfer divariasikan dengan 30º, 45º, 60º, dan 90º (tanpa chamfer) dan burn-off length 10 mm, 15 mm, dan 20 mm. Spesimen Al6061 diputar dengan rotational speed sebesar 1600 rpm dan specimen ST41 ditekan dengan friction pressure sebesar 7000 N, upset pressure sebesar 14000 N. Hasil yang diperoleh dari penelitian ini bahwa pada variasi sudut chamfer 30º burn-off length 15 mm terjadi distribusi suhu pada interface yang rendah yaitu 65,24 ºC dan luas flash sebesar 141,89 m2.Pada variasi sudut chamfer 90º burn-off length 20 mm terjadi distribusi suhu pada interface tertinggi yaitu 455,71 ºC dan luas flash sebesar 170,57 m2. Hasil dari penelitian ini menunjukkan bahwa besar sudut chamfer dan panjang burn-off length sangat berpengaruh terhadap distribusi suhu dan luas flash. hal ini disebabkan jika semakin besar sudut chamfer dan burn-off length maka heat input besar dikarenakan semakin luas bidang kontak dan semakin lama friction time.
English Abstract
Friction welding is a method in the process of connecting two metal materials. In this friction welding method, heat comes from friction that occurs in rotary motion accompanied by pressure, resulting in heat that occurs to the solid state, causing welding process to occur. The purpose of this study was to determine the effect of variations in chamfer angle and burn-off length on temperature distribution and flash area at friction welding joints Al6061 and ST41. This research methodology uses a computer simulation method with software based on the finite element method, Ansys Workbench 19.2. Using a bilinear isotropic hardening material model, transient thermal analysis is used to get the temperature and static structural is used to get the flash. The chamfer angle is varied with 30º, 45º, 60º, and 90º (without chamfer) and burn-off lengths of 10 mm, 15 mm, and 20 mm. The Al6061 specimen was rotated with a rotational speed of 1600 rpm and the ST41 specimen was pressed with a friction pressure of 7000 N, an upset pressure of 14000 N. The results obtained from this study were that at a variation of the chamfer angle of 30º burn-off length 15 mm, the temperature distribution at the interface was different. low, namely 65.24 ºC and flash area of 141.89 m2. At the variation of the 90º burn-off length of the chamfer angle of 20 mm, the temperature distribution at the highest interface is 455.71 ºC and the flash area is 170.57 m2. The results of this study indicate that the chamfer angle and burn-off length greatly affect the temperature distribution and flash area. This is because the larger the chamfer angle and the burn-off length, the larger the heat input due to the wider contact area and the longer the friction time.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0522070021 |
| Uncontrolled Keywords: | Kata kunci: Friction Welding, Chamfer, Burn-off length, Ansys Workbench 19.2. |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | yulia Chasanah |
| Date Deposited: | 18 Feb 2022 08:14 |
| Last Modified: | 24 Feb 2022 03:28 |
| URI: | http://repository.ub.ac.id/id/eprint/189848 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
175060207111023 -MUHAMMAD ICHLASUL AMAL RAMADHAN.pdf Restricted to Registered users only until 31 December 2024. Download (6MB) |
Actions (login required)
 |
View Item |