Aida, Nur and Dr. Ir. Bambang Dwi Argo,, DEA and Dr. Sasa Sofyan Munawar,, S.Hut., MP. (2021) Pengaruh Variasi Densitas Komposit dan Fraksi Volume Serat Bagasse Sorgum (Sorghum bicolor L. Moench) terhadap Karakteristik Fisik, Mekanik, dan Morfologi Komposit Foam Polyurethane. Sarjana thesis, Universitas Brawijaya.
Abstract
Penggunaan komposit sebagai material rekayasa saat ini mengalami perkembangan yang cukup pesat. Hal ini ditandai oleh luasnya aplikasi penggunaan komposit di berbagai bidang seperti konstruksi dan infrastruktur, otomotif dan transportasi, material biomedis, dan panel dinding. Pada penelitian ini dilakukan pembuatan komposit foam dengan matriks berupa polyurethane dan material reinforcement berupa bagasse sorgum. Poliuretan dipilih karenan memiliki kelebihan berupa ketangguhan yang tinggi dan toksisitas yang sedikit. Sedangkan, bagasse sorgum dipilih oleh karena bagasse yang merupakan limbah pertanian namun berpotensi untuk digunakan sebagai material pengisi foam karena terdapat kandungan selulosa didalamnya. Penelitian dilakukan untuk menganalisis pengaruh variasi densitas dan fraksi serat terhadap karakteristik foam yang dihasilkan. Selain itu, juga dilakukan pengamatan free rise foaming yang ditujukan untuk mengetahui kereaktifan foam polyurethane dimana dalam proses pembuatannya foam dibiarkan berekspansi total tanpa adanya pembatasan. Pada pengamatan free rise foaming komposit dibedakan atas jumlah seratnya yang terdiri dari 0%, 2.5%, 5%, 7.5%, 10% dari total berat komposit foam polyurethane. Foam polyurethane dibuat dengan memvariasikan densitas komposit (40 kg/m³, 50 kg/m³, 60 kg/m³) dan fraksi volume serat (0%, 2.5%, 5%, 7.5%, 10%). Komposit foam dibuat menggunakan metode one-shot process yang mana tiap material penyusun dihomogenkan secara bertahap sebelum dituangkan ke dalam alat cetak dan dibiarkan berekspansi. Selanjutnya, komposit foam polyurethane dilakukan pengujian berupa uji kadar air, daya serap air, pengembangan tebal, kuat lentur, kompresi, dan morfologi. Tiap pengujian sampel dibedakan atas perlakuan foam dengan kulit dan foam tanpa kulit. Hasil yang didapat dari pengujian selanjutnya diolah menggunakan Rancangan Acak Lengkap metode MANOVA dengan uji lanjut DMRT pada taraf signifikan 5%. Berdasarkan hasil analisis uji, diketahui bahwa adanya variasi densitas dan fraksi volume serat memiliki pengaruh signifikan terhadap karakteristik komposit foam polyurethane yang dihasilkan
English Abstract
The application of composite materials as engineering materials is currently being developed. The wide application of composites materials in various fields such as construction and infrastructure, automotive and transportation, biomedical materials, and wall panels proves this point. In this study, a polyurethane foam composite was produced using a matrix of polyurethane and sorghum bagasse fibers as reinforcement materials. Polyurethane chose because of its high toughness, low moisture absorption and low toxicity. Meanwhile, even bagasse sorghum is an agro-waste, but it has the potency to be used as a filler since bagasse contains cellulose within. This study was conducted to analyze the effect of the density of the composite and the fiber fraction on the properties of the foam. In addition, the observation of free rise foaming was conducted to determine the reactivity of polyurethane foam, whereas in the process foam is allowed to expand completely without any restrictions. The free rise foaming of composites was varied by the number of fibers that consist of 0%, 2.5%, 5%, 7.5%, 10% of the total weight of the foam polyurethane. The manufacture of foam polyurethane was carried out by varying the density of the composite (40 kg/m, 50 kg/m, 60 kg/m³) and the volume fraction of the fiber (0%, 2.5%, 5%, 7.5%, 10%). Composite foam polyurethane is made using the one-shot process method, in which each material is homogenized gradually before the molding process and totally expands. Furthermore, polyurethane foam was tested for moisture content, water absorption, thickness swelling, flexural strength, compression and morphology. Each sample was tested by the different treatments of foam with skin and foam without skin. The results were processed using a Completely Randomized Design (CRD) using the MANOVA analysis method and DMRT test with a level significant 5%. Based on the results, the variations of the density and volume fraction of the fibers have a significant effect on the properties of foam polyurethane
Item Type: | Thesis (Sarjana) |
---|---|
Identification Number: | 0521100312 |
Uncontrolled Keywords: | bagasse sorgum, foam polyurethane, free rise foaming, komposit berpenguat serat alam,sorghum bagasse, foam polyurethane, free rise foaming, natural fiber reinforced composite |
Subjects: | 600 Technology (Applied sciences) > 630 Agriculture and related technologies |
Divisions: | Fakultas Teknologi Pertanian > Keteknikan Pertanian |
Depositing User: | soegeng sugeng |
Date Deposited: | 18 Feb 2022 02:38 |
Last Modified: | 23 Feb 2022 05:50 |
URI: | http://repository.ub.ac.id/id/eprint/189823 |
![]() |
Text (DALAM MASA EMBARGO)
175100607111013 -Nur Aida.pdf Restricted to Registered users only until 31 December 2023. Download (9MB) |
Actions (login required)
![]() |
View Item |