Buana, Nalendra Wasesa and Moch.Syamsul Ma’arif, ST., MT., and Prof.Dr.Ir.Rudy Soenoko, M.Eng.Sc. (2022) Pengaruh Variasi Konsentrasi Asam Sulfat (H2SO4) Sebagai Elektrolit Pada Proses Anodizing Terhadap Laju Korosi Pada Aluminium Paduan Seri 7075-T651. Sarjana thesis, Universitas Brawijaya.
Abstract
Dalam perkembangan teknologi saat ini menyebabkan timbulnya berbagai macam industri di Indonesia khususnya dalam moda transportasi sehari-hari khususnya penggunaan sepeda sebagai penunjang bepergian ke tempat kerja, sekolah, dan sekedar bepergian dalam kota, hal tersebut didukung dengan adanya wabah cov-19 yang sedang melanda Indonesia dimana hype khalayak umum untuk menjalani hidup sehat kian hari meningkat khususnya pada anak muda (mediaindonesia.com). Dimana bahan dalam pembuatan komponen sepeda untuk era modern saat ini banyak menggunakan Aluminium, dimana Aluminium salah satunya memiliki kelebihan ketahanan korosi yang baik, banyak produsen sepeda menggunakan Aluminium selain untuk pembuatan frame juga digunakan untuk membuat shockbreaker pada sepeda karena selain berat yang ringan dan ketahanan tegangan yang baik, ketahanan korosi juga menjadi faktor pendukung para produsen sepeda menggunakan aluminium sebagai bahan utama dalam pembuatan shockbreaker sepeda. Hal yang disoroti dalam penelitian yang saya lakukan adalah persebaran rata-rata ukuran diameter pori Al2O3 yang terbentuk dan variasi konsentrasi asam sulfat terhadap laju korosi pada Aluminium paduan 7075-T651. Metode dalam penelitian ini dikategorikan sebagai penelitian eksperimental. Dalam penelitian ini, peneliti menggunakan larutan asam sulfat sebagai elekktrolit pada proses anodizing dengan variasi konsentrasi asam sulfat. Prosedur penelitian yang digunakan adalah Uji SEM (Scanning Electron Microscope), dan Uji Laju korosi (AUTOLAB PGSTAT204). Dari hasil Analisa penelitian yang telah dijabarkan, didapatklan bahwa pengaruh konsentrasi asam sulfat sebagai elektrolit dapat menurunkan nilai laju korosi pada aluminium 7075- T651 yang terbaik didapatkan pada konsentrasi asam sulfat 15%
English Abstract
The current technological developments have led to the emergence of various kinds of industries in Indonesia, especially in daily transportation modes, especially the use of bicycles as a support for traveling to work, school, and just traveling within the city, this is supported by the COVID-19 outbreak that is currently hitting Indonesia. where the general public hype for living a healthy life is increasing day by day, especially among young people (mediaindonesia.com). Where the material in the manufacture of bicycle components for the modern era currently uses a lot of Aluminum, where Aluminum one of which has the advantage of good corrosion resistance, many bicycle manufacturers use Aluminum in addition to making frames, it is also used to make shockbreakers on bicycles because in addition to light weight and stress resistance. Good quality, corrosion resistance is also a supporting factor for bicycle manufacturers to use aluminum as the main material in the manufacture of bicycle shockbreakers. The thing that was highlighted in my research was the distribution of the average pore diameter size of Al2O3 formed and the variation of sulfuric acid concentration on the corrosion rate of Aluminum alloy 7075- T651. The method in this research is categorized as experimental research. In this study, researchers used sulfuric acid solution as an electrolyte in the anodizing process with various concentrations of sulfuric acid. The research procedure used was the SEM (Scanning Electron Microscope) test, and the corrosion rate test (AUTOLAB PGSTAT204). From the analysis of the research that has been described, it is found that the effect of the concentration of sulfuric acid as an electrolyte can reduce the value of the corrosion rate on aluminum 7075-T651 which is best obtained at a concentration of 15% sulfuric acid.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0522070019 |
| Uncontrolled Keywords: | Kata kunci: Pengaruh Konsentrasi Asam Sulfat, Besar Diameter Pori AL2O3, Laju Korosi, Aluminium 7075-T651 |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | yulia Chasanah |
| Date Deposited: | 15 Feb 2022 07:14 |
| Last Modified: | 24 Feb 2022 02:56 |
| URI: | http://repository.ub.ac.id/id/eprint/189774 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
175060200111022 - NALENDRA WASESA BUANA.pdf Restricted to Registered users only until 31 December 2024. Download (7MB) |
Actions (login required)
 |
View Item |