Pengaruh Arus Listrik dan Pulse-On Time Pada Electrical Discharge Machining (EDM) Sinking Terhadap Nilai Kekasaran Permukaan Aluminium 6061

Zuandika, Oki and Moch. Syamsul Ma’arif, ST., MT. and Redi Bintarto, ST., M.Eng.Pract (2021) Pengaruh Arus Listrik dan Pulse-On Time Pada Electrical Discharge Machining (EDM) Sinking Terhadap Nilai Kekasaran Permukaan Aluminium 6061. Sarjana thesis, Universitas Brawijaya.

Abstract

Proses permesinan EDM sinking menghasilkan erosi yang terjadi karena adanya loncatan bunga api listrik yang terjadi secara periodik dengan frekuensi yang tinggi pada celah sempit diantara benda kerja dan elektroda di dalam cairan dielektrik, dengan variabel arus listrik 4A, 7A, 10A dan Pulse-On Time sebesar 50μs, 75μs, 100μs maka dihasilkan nilai kekasaran permukaaan yang berbeda pada material aluminium 6061. Pengambilan data setiap variabel dilakukan pengulangan sebanyak tiga kali dengan jarak sudut 120° dan jarak dari tepi sebesar 3mm, 6mm, 9mm dan didapatkan nilai ratarata dari ketiga pengulangan tersebut. Sehingga didapatkan nilai kekasaran permukaan 3,33 μm, 3,94 μm, 4,13 μm, 4,40 μm, 5,47 μm, 6,47 μm, 7,66 μm, 7,93 μm, 8,38 μm. Nilai kekasaran permukaan yang paling kecil terjadi pada parameter arus 4A, pulse-on time 50 μs dengan rata rata nilai kekasaran permukaan 3,33 μm. Sedangkan untuk nilai kekasaran paling besar terjadi pada parameter arus 10A, pulse-on time 100 μs dengan rata rata nilai kekasaran permukaan 8,38 μm. Hal ini menunjukkan bahwa arus listrik dan pulse-on time berpengaruh terhadap besarnya nilai kekasaran permukaan yang dihasilkan. Arus listrik berbanding lurus dengan Pulse-On Time, dimana semakin lama Pulse-On Time semakin besar arus listrik yang akan memperbesar energi listrik yang dilepaskan sehingga kawah – kawah yang terbentuk akan semakin curam yang menyebabkan nilai kekasaran permukaan semakin tinggi

English Abstract

The process of machining EDM sinking results in erosion that occurs due to periodic jumping of electric sparks with high frequencies in narrow gaps between workpieces and electrodes in dielectric liquids, with variable electric currents of 4A, 7A, 10A and Pulse-On Time of 50 μs, 75μs, 100μs resulting in different surface roughness values in aluminum materials 6061. Data retrievalof each variabell is repeated three times with an angle distance of 120° and a distance from the edge of 3mm, 6mm, 9mm and obtained the average value of the three repetitions. Thus obtained surface roughness values of 3,33 μm, 3,94 μm, 4,13 μm, 4,40 μm, 5,47 μm, 6,47 μm, 7,66 μm, 7,93 μm, 8,38 μm. The smallest surface roughness value occurs in the current parameter 4A, pulse-on time 50 μs with an average surface roughness value of 3,33 μm. As for the largest roughness value occurs in the current parameter 10A, pulse-on time 100 μs with an average surface roughness value of 8.38 μm. This indicates that electric current and pulse-on time affect the magnitude of the resulting surface roughness value. Electric current is directly proportional to Pulse-On Time, where the longer Pulse-On Time, the greater the electric current that will enlarge the electrical energy released so that the craters that are formed will be steeper which causes the value of surface roughness is higher

Other obstract

-

Item Type:	Thesis (Sarjana)
Identification Number:	0'521070151
Uncontrolled Keywords:	Kata Kunci: Electrical Discharge Machine Sinking, Arus Listrik, Pulse-On Time, Kekasaran Permukaan, Aluminium A6061
Subjects:	600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	yulia Chasanah
Date Deposited:	27 Dec 2021 03:35
Last Modified:	26 Sep 2024 01:10
URI:	http://repository.ub.ac.id/id/eprint/187459

Text OKI ZUANDIKA.PDF Download (5MB)

Actions (login required)

View Item