Firdaus, Abu Risal and Moch Syamsul Ma’arif, ST., MT. and Redi Bintarto, ST., M.Eng.Pract. (2021) Pengaruh Pulse-On Time Dan Pulse-Off Time Pada Electrical Discharge Machining (EDM) Terhadap Nilai Kekerasan Permukaan Aluminium 7075. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini melihat hasil nilai kekerasan paduan Alumunium 7075 pada permesinan EDM yang menggunakan pengaruh parameter pulse-on time dan pulse-off time. Penelitian ini menggunakan Mesin Electrical Discharge Machining (EDM) merek dengan Seri CTEK ZNC 320 dan mesin Rockwell Hardness Tester. Bahan yang digunakan Aluminium 7075 dikarenakan EDM sendiri tidak memerlukan gaya deformasi untuk melakukan permesinan, sebagai alat untuk material pemesinan yang bersifat elastis, mudah dibentuk dan konduktivitas thermal tinggi sepereti aluminium 7075. Elektroda yang digunakan tembaga (Cu) dengan diameter 25,4 mm dan panjang 50 mm. Parameter proses yang digunakan adalah pulse-on time: 50 μs, 75 μs, 100 μs dan pulse-off time: 4 μs, 6 μs, 9 μs. Hasil pengolahan data ada 9 percobaan. Penelitian ini menunjukkan pemesinan yang signifikan pada kekerasan (HBR). Hasil dari pengukuran kekerasan rata-rata dari percobaan 1 dan 9 adalah: 28,03 HBR, dan 50,80 HBR. Analisis varians (Anova) menunjukkan nilai F hitung adalah 71.55, Nilai α sebesar 0,05 adalah 5,14. Kenaikan nilai pulse-on time dan pulse-off time memberikan pengaruh yang besar terhadap kekerasan permukaan, dikarenakan pulse-on time yang besar akan menimbulkan percikan api yang lama dan memberikan energi panas yang tinggi pada permukaan benda kerja, sehingga akan menjadikan nilai kekerasan lebih besar. Pulse-off time yang besar akan mengakibatkan pendinginan yang lama, sehingga menjadikan permukaan benda kerja semakin keras.
English Abstract
This study looked at the results of the hardness value of the Aluminum alloy 7075 on EDM machining using the influence of the pulse-on time and pulse-off time parameters. This study uses a branded Electrical Discharge Machining (EDM) Machine with the CTEK ZNC 320 Series and a Rockwell Hardness Tester machine. The material used is Aluminum 7075 because EDM itself does not require defomation forces to perform machining, as a tool for machining materials that are elastic, easy to shape. and high thermal conductivity such as aluminum 7075. The electrode used is copper (Cu) with a diameter of 25.4 mm and a length of 50 mm. The process parameters used are pulse-on time: 50 μs, 75 μs, 100 us and pulse-off time: 4 μs, 6 μs, 9 us. The results of data processing there are 9 experiments. This research shows significant machining on hardness (HBR). The results of the measurement of the average hardness of experiments 1 and 9 are: 28.03 HBR and 50 80 HBR Analysis of variance (Anova) shows the calculated F value is 71 55, the a value of 0.05 is 5.14. The increase in the value of pulse-on time and pulseof time has a big effect on surface hardness because a large pulse-on time will cause a long spark and give high heat energy to the surface of the workpiece so that the hardness value is greater. Large pulse-off time will result in a long cooling time, thus making the workpiece surface even harder.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0521070073 |
| Uncontrolled Keywords: | Electrical Discharge Machine, Pulse-On Time, Pulse-Off Time, Hardness, Aluminium 7075 |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | yulia Chasanah |
| Date Deposited: | 01 Nov 2021 04:17 |
| Last Modified: | 26 Sep 2024 06:57 |
| URI: | http://repository.ub.ac.id/id/eprint/186257 |
![[thumbnail of - Abu Risal firdaus.PDF]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text
- Abu Risal firdaus.PDF Download (3MB) |
Actions (login required)
 |
View Item |