Pengaruh Waktu Coldpress Terhadap Sifat Fisik Dan Sifat Mekanik Plywood Berbahan Dasar Kayu Jabon (Anthocephalus cadamba Miq.)

Safitri, Diana (2021) Pengaruh Waktu Coldpress Terhadap Sifat Fisik Dan Sifat Mekanik Plywood Berbahan Dasar Kayu Jabon (Anthocephalus cadamba Miq.). Sarjana thesis, Universitas Brawijaya.

Abstract

Kayu Jabon (Anthocephalus cadamba Miq.) saat ini mulai banyak dibudidayakan di hutan rakyat karena kelebihannya yang cepat tumbuh dan memiliki kualitas yang relatif sama dengan sengon. Namun, kayu jabon dinilai tidak tahan lama. Hasil uji kayu di Indonesia menunjukkan bahwa rata-rata kayu jabon hanya dapat bertahan kurang dari 1,5 tahun apabila dibiarkan diatas tanah. Sehingga perlu adanya inovasi untuk mengolah kayu jabon tersebut agar bisa lebih awet salah satunya adalah dengan dijadikan plywood (kayu lapis). Penelititian ini dilakukan untuk mengetahui karakteristik fisik dan mekanik plywood 3 dan 5 ply berbahan dasar kayu jabon (Anthocephalus cadamba Miq.) dengan variasi waktu coldpress 40, 60 dan 80 menit. Variasi waktu coldpress diberikan dengan tujuan untuk mengetahui waktu optimal untuk coldpress yang dapat menghasilkan kualitas plywood terbaik. Hal tersebut dikarenakan coldpress (pengempaan dingin) merupakan tahapan penting yang dilakukan untuk tercapainya kematangan perekat sebelum dilakukannya hotpress. Karakteristik fisik yang diteliti adalah kadar air dan berat jenis. Sedangkan karakteristik mekanik yang diuji adalah bonding strength, bending strength dan delaminasi. Sifat fisik plywood 3 dan 5 ply dengan waktu coldpress 40, 60, dan 80 menit telah memenuhi standar JAS, EN dan SNI. Sedangkan sifat mekanik plywood yaitu bending strength (keteguhan tekan) dan delaminasi pada plywood 3 dan 5 ply dengan waktu coldpress 40, 60, dan 80 menit telah memenihi standar JAS, EN dan SNI, namun bonding strength (kekuatan rekat) pada plywood 3 ply tidak memenuhi standar sedangkan pada plywood 5 ply telah memenuhi standar. Hal tersebut karena plywood dengan jumlah lapisan sebanyak 3 ply terlalu tipis sehingga ketika diberikan suatu gaya yang besar maka plywood akan dengan mudah rusak sehingga menghasilkan nilai adhesive strength yang rendah. Variasi jumlah ply dan variasi waktu coldpress pada interaksi kedua faktor terhadap massa jenis plywood memberikan pengaruh yang sangat nyata. Waktu pengempaan akan memberikan pengaruh yang berarti pada kadar air dan kerapatan apabila diberikan suhu tinggi. Lama waktu coldpress berpengaruh terhadap sifat mekanik plywood. Waktu yang terlalu singkat (40 menit) kurang cukup untuk membuat lem matang dan masuk ke pori-pori veneer sedangkan waktu yang terlalu lama (80 menti) akan menyebabkan lem mengeras sebelum dilakukannya hotpress sehingga lem tidak dapat meresap secara optimal kedalam pori-pori veneer karena perekat memiliki masa yang disebut curring time atau masa menuju pengerasan. Sehingga 60 menit adalah waktu yang paling tepat untuk proses coldpress pada plywood berbahan dasar kayu jabon.

English Abstract

Jabon (Anthocephalus cadamba Miq.) is starting to be widely cultivated in community forests because of its advantages, which are fast growing and have the same quality as sengon. However, jabon wood is considered not durable. The results of wood testing in Indonesia show that on average Jabon can only survive less than 1.5 years if left on the ground. So there needs to be an innovation to make the jabon can be more durable, one of which is by making it plywood. This research was conducted to determine the physical and mechanical character of plywood 3 and 5 ply made from jabon (Anthocephalus cadamba Miq.) with coldpress time variations of 40, 60 and 80 minutes. The coldpress time variation is given in order to determine the optimal time for coldpress which can produce the best quality plywood. This is because cold pressing is an important step to achieve adhesive maturity before hotpressing. The physical characteristics studied were water content and specific gravity. While the mechanical characteristics tested are bonding strength, bending strength and delamination. The physical properties of 3 and 5 ply plywood with coldpress times of 40, 60, and 80 minutes have complied with JAS, EN and SNI standards. Meanwhile, the mechanical properties of plywood, namely bending strength (compressive strength) and delamination on 3 and 5 ply plywood with coldpress times of 40, 60, and 80 minutes have met the JAS, EN and SNI standards, but the bonding strength of 3 ply plywood is not meet the standard while the 5 ply plywood has met the standard because plywood with 3 ply layers is too thin so that when a large force is applied, the plywood will be easily damaged, resulting in low adhesive strength values. The variation of the number of ply and the variation of coldpress time on the interaction of the two factors on the density of plywood has a very significant effect. The pressing time will have a significant effect on the moisture content and density when given a high temperature. The length of time coldpress affects the mechanical properties of plywood. Short time coldpress (40 minutes) is not enough to make the glue mature and enter the veneer pores while too long time (80 minutes) will cause the glue to harden before hotpressing so that the glue cannot seep optimally into the veneer pores because the adhesive has a period called the curring time or the time leading to hardening. So 60 minutes is the most appropriate time for the coldpress process on plywood made from jabon.

Item Type:	Thesis (Sarjana)
Identification Number:	0521100123
Uncontrolled Keywords:	plywood, kayu jabon, kadar air, berat jenis, bonding strength, bending strength, delaminasi, standar JAS,plywood, jabon wood, moisture content, specific gravity, bonding strength, bending strength, delamination, JAS standard.
Subjects:	600 Technology (Applied sciences) > 630 Agriculture and related technologies
Divisions:	Fakultas Teknologi Pertanian > Keteknikan Pertanian
Depositing User:	Sugeng Moelyono
Date Deposited:	01 Nov 2021 02:02
Last Modified:	23 Feb 2022 07:24
URI:	http://repository.ub.ac.id/id/eprint/186235

Text (DALAM MASA EMBARGO) Diana Safitri.pdf Restricted to Registered users only until 31 December 2023. Download (4MB)

Actions (login required)

View Item