Pengaruh Kecepatan Rotasi Planetary Ball Mill Terhadap Struktur Kristal Dan Ukuran Partikel Camno3 Sebagai Bahan Termoelektrik Tipe N

Fauzy, Ananda Ilham Muhammad (2021) Pengaruh Kecepatan Rotasi Planetary Ball Mill Terhadap Struktur Kristal Dan Ukuran Partikel Camno3 Sebagai Bahan Termoelektrik Tipe N. Sarjana thesis, Universitas Brawijaya.

Abstract

"CaMnO3 (Calcium Manganese Oxide) merupakan material keramik dari material oksida yang menjajikan sebagai termoelektrik tipe N. Sintesis CaMnO3 (Calcium Manganese Oxide) dapat dilakukan dengan solid state reaction dengan alat planetary ball mill yaitu mencampurkan material dan mereduksi ukuran partikel memanfaatkan tumbukan bola dengan serbuk di dalam tabung. Gerakan bola di dalam planetary ball mill mempengaruhi tumbukan bola terhadap serbuk, salahsatu parameter yang penting di dalam planetary ball mill adalah kecepatan rotasi. Pada paper ini akan didiskusikan tentang pegaruh kecepatan rotasi planetary ball mill terhadap struktur kristal dan ukuran partikel CaMnO3. Variasi kecepatan rotasi yang digunakan adalah 70%, 80%, 90% dan 100% dari kecepatan kritis. Struktur kristal CaMnO3 dikarakterisasi dengan X-Ray Diffraction dan ukuran partikel diukur dengan Particle Size Analyzer. Hasil karakterisasi XRD menunjukkan fase CaMnO3 terbentuk dengan sistem kristal cubic dengan model kristal FCC (Face Centered Cubic) dengan parameter kisi α 4,5736 Å dan ukuran kristal 36,691 nm. Ukuran partikel paling kecil sebesar 17,27 µm pada kecepatan rotasi 70% dari kecepatan kritis atau 148 rpm."

English Abstract

CaMnO3(Calcium Manganese Oxide) is a ceramic material made from an oxide material that promises to be a type N thermoelectric. Synthesis of CaMnO3 (Calcium Manganese Oxide) can be carried out by solid state reaction with a planetary ball mill, which is mixing materials and reducing particle size using ball collisions with powder in the tube. The motion of the ball in the planetary ball mill affects the impact of the ball against the powder, one of the important parameters in the planetary ball mill is the rotational speed. This paper will discuss the effect of the rotation speed of the planetary ball mill on the crystal structure and particle size of CaMnO3.The variations in rotational speed used were 70%, 80%, 90% and 100% of the critical speed. The crystal structure of CaMnO3 was characterized by X-Ray Diffraction and the particle size was measured by a Particle Size Analyzer. The results of XRD characterization showed that the CaMnO3 phase was formed is a cubic with crystal model is FCC (Face Centered Cubic) with has lattice parameter α 4.5736 Å and the value of grain size is 36.691 nm. The smallest particle size is 17.27 µm at a rotation speed of 70% of the critical speed or 148 rpm

Other obstract

-

Item Type:	Thesis (Sarjana)
Identification Number:	052109
Uncontrolled Keywords:	CaMnO3, Calcium Manganese Oxide, Planetary Ballmill, Kecepatan Rotasi, Struktur Kristal, Ukuran Partikel,, CaMnO3, Calcium Manganese Oxide, Planetary Ballmill, Rotational Speed, Crystal Structure, Particle Size
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika
Depositing User:	Unnamed user with username dedyiskandar
Date Deposited:	19 Oct 2021 09:07
Last Modified:	23 Sep 2024 03:10
URI:	http://repository.ub.ac.id/id/eprint/184098

Text ANANDA ILHAM MUHAMMAD FAUZY.pdf Download (2MB)

Actions (login required)

View Item