Sintesis Komposit Silika-Karbon Dari Gula Pasir Secara Hidrotermal Dengan Template Ganda

Zhafarani, Irsalina Nur (2020) Sintesis Komposit Silika-Karbon Dari Gula Pasir Secara Hidrotermal Dengan Template Ganda. Sarjana thesis, Universitas Brawijaya.

Abstract

Sintesis komposit silika-karbon telah dilakukan dengan prekursor gula pasir dengan hard template natrium silikat/silika gel serta sodium dodecyl benzene sulfonate (surfatan anionik) sebagai soft template. Penelitian ini bertujuan untuk mempelajari pengaruh jenis template terhadap sifat fisik dan kimia produk komposit silika-karbon. Hard template juga berperan sebagai prekursor silika. Sintesis dilakukan pada perbandingan volume larutan gula 200% dan larutan natrium silikat (SiO2 83,02 % ; Na2O 42,71%) atau larutan sodium dodecyl benzene sulfonate (0,0063 M) masing-masing 1:1, serta perbandingan massa silikagel dan larutan gula 200% sebesar 3:1. Sintesis dilakukan pada suhu 80oC selama 4 jam dalam beaker gelas, dilanjutkan pemanasan pada suhu 190oC selama 4 jam di dalam autoclave. Produk hasil sintesis merupakan padatan serbuk halus dan kasar berwarna coklat muda hingga coklat tua. Template silika gel memberikan warna paling gelap (karbonisasi paling baik). Karakterisasi dilakukan dengan menggunakan spektrometri FTIR. Hasil karakterisasi menunjukkan bahwa komposit silika-karbon hasil sintesis memiliki gugus fungsi Si–OH (silanol) dan Si-O-Si (siloksan),-OH hidrat, C-H alifatik, C=O dan C-O.

English Abstract

Synthesis of silica-carbon composites have been carried out with granulated sugar precursors with a hard template of sodium silicate / silica gel and sodium dodecyl benzene sulfonate (anionic surface) as a soft template. This study aims to study the effect of template types on the physical and chemical properties of silica-carbon composite products. Hard templates also act as silica precursors. Synthesis was conducted at volume ratio of sugarcane solution (200%) and each sodium silicate solution (SiO2 83,02 % ; Na2O 42,71%) or Sodium dodecyl benzene sulfonate solution (0.0063M) at 1:1, also at weight ratio of sugarcane solution (200%) and silicagel at 1:3. Synthesis was adjusted at 80oC for 4 hours in a glass beaker, then continued at 190oC for 4 hours in the autoclave. The synthesized product is a fine and coarse powder solid, brown to dark brown. Silica gel template gave the darkest color (best carbonization) of silica-carbon composites. The products were characterized with infrared spectrophotometry (FTIR). The characterization results show that the silica-carbon composite has the Si- OH (silanol) and Si-O-Si (siloxane), - OH hydrate, C-H aliphatic , C=O and C-O functional groups.

Other obstract

-

Item Type:	Thesis (Sarjana)
Identification Number:	0520090142
Uncontrolled Keywords:	komposit silika-karbon, sugarcane, hidrotermal, template ganda
Subjects:	500 Natural sciences and mathematics > 541 Physical chemistry > 541.3 Miscellaneous topics in physical chemistry > 541.39 Hydrolysis
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia
Depositing User:	ismanto
Date Deposited:	07 Feb 2021 04:37
Last Modified:	08 Oct 2024 07:55
URI:	http://repository.ub.ac.id/id/eprint/182707

Text 0520090142 - Irsalina Nur Zhafarani_unlocked (1).pdf Download (2MB)

Actions (login required)

View Item