Zafirah, Tyas Nurul (2019) Studi Pengaruh Mikrostruktur Dan Jenis Buffer Terhadap Efek Swelling Pada Lapisan Tipis Zinc Phthalocyanine (ZnPc) Dan Polistiren (PS). Magister thesis, Universitas Brawijaya.
Abstract
Pada penelitian ini dilakukan pengamatan efek swelling pada lapisan tipis Zinc phthalocyanine (ZnPc) dan Polistiren (PS) karena pengaruh mikrostruktur dan jenis buffer yang digunakan. Lapisan tipis PS dideposisikan dengan metode spin coating, sedangkan lapisan tipis ZnPc dideposisikan dengan metode evaporasi termal. Setelah proses deposisi, masing-masing lapisan tipis akan dideposisi pada temperatur yang berbeda-beda yaitu 100 oC, 150 oC, dan 200/220 oC, dengan tujuan untuk menghasilkan kekasaran permukaan yang berbeda. Selanjutnya, lapisan tipis akan dikarakterisasi menggunakan Topography Measurement System (TMS), X-Ray Diffraction (XRD), dan Scanning Electron Microscopy (SEM). Pengamatan swelling dilakukan menggunakan frequency counter dan dilakukan selama 60 menit. Adapun jenis buffer yang digunakan yaitu aquades, Phosphate Buffered Saline (PBS) pH 7,4 , dan Tris-Hydrochloride (Tris-Cl) 1M. Lapisan tipis dengan kekasaran permukaan yang tinggi akan menyebabkan efek swelling yang lebih besar. Hal ini disebabkan oleh luas permukaan yang semakin besar, sehingga memungkinkan lebih banyak molekul buffer untuk berdifusi. Selain itu, buffer dengan berat molekul dan kekuatan ionik yang lebih besar juga akan menyebabkan terjadinya efek swelling yang lebih besar. Hal ini disebabkan molekul tersebut memiliki driving force yang lebih besar untuk berdifusi maupun berinteraksi dengan lapisan. Terjadi penurunan nilai kekasaran pada PS dan ZnPc serta ditemukan unsur P dan Cl yang merupakan atom penyusun buffer pada lapisan ZnPc setelah mengalami efek swelling. Hal ini disebabkan oleh adanya difusi dari molekul tersebut maupun adanya interaksi antara molekul buffer dengan lapisan tipis.
English Abstract
The swelling effect on Zinc phthalocyanine (ZnPc) and Polistiren (PS) thin films due to different microstructure and buffers was observed. PS thin film deposited by spin coating method, while ZnPc deposited by thermal evaporation method. After deposition, the film was annealed at 3 different temperatures, are 100 oC, 150 oC, and 200/220 oC to obtain different surface roughness. The film was characterized using Topography Measurement System (TMS), X-Ray Diffraction (XRD), dan Scanning Electron Microscopy (SEM). Swelling effect was observed using frequency counter for 1 hour. There are 3 different buffer used in this experiment, are distilled water, Phosphate Buffered Saline (PBS) pH 7.4, and Tris-Hydrochloride (Tris-Cl) 1M. Rough surface causing more swelling than smooth surface. Because it has larger surface area that allowed more molecules to diffuse into the film. The buffer affected the swelling effect occured on thin film as well. The weigher molecular weight and stronger ionic strength of buffer lead more swelling occured. Because the molecule has bigger driving force to diffuse and interacting with the film. After swelling, the surface roughness of ZnPc and PS film was decreased and atom Cl and P were detected on ZnPc film. It was caused by the molecules diffusion or even the interaction among the buffer molecules and film.
Other obstract
-
| Item Type: | Thesis (Magister) |
|---|---|
| Identification Number: | TES/547/ZAF/s/2019/041904855 |
| Uncontrolled Keywords: | PHTHALOCYANINES, ORGANIC COMPUNDS |
| Subjects: | 500 Natural sciences and mathematics > 547 Organic chemistry |
| Divisions: | S2/S3 > Magister Fisika, Fakultas MIPA |
| Depositing User: | Endang Susworini |
| Date Deposited: | 12 Mar 2020 05:08 |
| Last Modified: | 12 Mar 2020 05:08 |
| URI: | http://repository.ub.ac.id/id/eprint/180336 |