Rusdarto, Muhammad Fajri (2019) Penentuan Ukuran Kristal Zno Nanopartikel Doping Mg Dengan Menggunakan Metode Formula Scherrer Dan Williamson-Hall Serta Penentuan Ukuran Partikel Dengan Scanning Electron Microscopy (SEM). Sarjana thesis, Universitas Brawijaya.
Abstract
Nanomaterial atau material yang berukuran nano partikel (10-9 meter) merupakan material yang sedang hangat dibicarakan di ranah teknologi masa kini, dimana sebuah perwujudan dari perkembangan teknologi yang dikenal dengan istilah nanoteknologi. Telah dilakukan sintesis nanomaterial dengan menggunakan metode kopresipitasi atau pengendapan dengan ditentukan ukuran Kristal dengan teknik XRD menggunakan software Match!3 dan OriginPro. Yang mana didapat data yang kemudian dihitung ukuran kristalnya menggunakan persamaan Scherrer dan metode Williamson-Hall. Kemudian ditentukan pula ukuran partikelnya dengan SEM menggunakan software ImageJ yang mana didapat data kemudian dihitung ukuran partikelnya. Dari tujuan tersebut, telah disintesis sampel campuran Zn(1-x)Mg(x)O dengan variasi doping Magnesium 0%, 3%, 6%, 9%, 12%. Sampel tersebut disintesis menggunakan metode kopresipitasi yang mana merupakan salah satu metode sintesis senyawa anorganik yang didasarkan pada pengendapan lebih dari satu substansi secara bersama – sama ketika melewati titik jenuhnya. Setelah disintesis dengan metode kopresipitasi, maka sampel nanomaterial ini dibuktikan ukuran Kristal dan partikelnya dengan teknik XRD dan metode analisis menggunakan persamaan Scherrer dan Williamson-Hall untuk pengukuran ukuran Kristal dan analisis menggunakan SEM untuk pengukuran partikel. Dari hasil pengukuran didapat ukuran Kristal rata-rata dari keseluruhan sampel berkisar antara 28-31 nm untuk metode Scherrer dan 41-65 nm untuk metode Williamson-Hall, sedangkan pada pengukuran SEM didapat ukuran partikel sebesar 329,8413 nm untuk sampel ZnO murni dan 119,5104 nm untuk ukuran sampel ZnO doping Mg 6%.
English Abstract
Nanomaterials or materials involving nanoparticles (10-9 meters) are materials that are being warmly discussed in the realm of today's technology, where the embodiment of technological development is known as nanotechnology. Synthesis of nano materials has been carried out using the coprecipitation or precipitation method using Crystal size with the XRD technique using Match!3 Software and OriginPro which obtain data which then calculates the crystal size using the Scherrer scheme and the Williamson-Hall method. Then the particle size was determined by SEM using ImageJ software which obtained data then calculated the particle size. From this goal, the samples were synthesized Zn (1-x) Mg (x) O with variations of doping Magnesium 0%, 3%, 6%, 9%, 12%. This sample uses the coprecipitation method which is one of the synthesis methods arranged based on precipitation of more than one complete substance together with compilation passing the saturation point. After being synthesized by the coprecipitation method, the nanomaterial sample was proved by the size of the crystals and particles with the XRD technique and the analysis method used the Scherrer and Williamson-Hall equations for crystal measurements and analysis using SEM to measure particles. From the measurement results, the average crystal size obtained from the overall sample obtained between 28-31 nm for the Scherrer method and 41-65 nm for the Williamson-Hall method, while the SEM measurements obtained the particle size as big as 329,8413 nm for pure ZnO samples and 119.5104 nm for the sample size of 6% ZnO doping Mg.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2019/398/052001553 |
| Uncontrolled Keywords: | kopresipitasi, Scherrer, Williamson-Hall, XRD, SEM |
| Subjects: | 500 Natural sciences and mathematics > 539 Modern physics > 539.7 Atomic and nuclear physics > 539.73 Particle acceleration |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 10 Aug 2020 07:35 |
| Last Modified: | 10 Aug 2020 07:35 |
| URI: | http://repository.ub.ac.id/id/eprint/179961 |
Actions (login required)
 |
View Item |