Rachma, Ai’syah Zahrotul (2019) Pengaruh Lama Penyinaran dan Sumber Sinar Terhadap Aktivitas TiO2/Cu-Zeolit-Alginat pada Fotodegradasi Limbah Cair Organik. Sarjana thesis, Universitas Brawijaya.
Abstract
Fotodegradasi merupakan proses penguraian senyawa dengan bantuan cahaya dan suatu fotokatalis. Proses fotodegradasi dapat diaplikasikan pada penurunan nilai COD limbah cair organik seperti limbah jasa pencuci pakaian (laundry), batik dan tempe. Penelitian ini bertujuan untuk mengetahui aktivitas fotokatalis granul TiO2/Cu-Zeolit- Alginat hasil sintesis terhadap pengaruh lama penyinaran dengan variasi waktu 30, 60, 120, 180, 240 menit dan sumber penyinaran dari sinar matahari dan sinar UV. Sintesis TiO2/Cu dibuat menggunakan metode sonikasi dengan (CuNO3)2 3H2O sebagai sumber Cu, selanjutnya fotokatalis TiO2/Cu dikarakterisasi menggunakan Fourier Transform Infra Red (FTIR). Fotokatalis disintesis dengan alginat kemudian diteteskan menggunakan alat suntik ke dalam larutan CaCl2 3% sehingga terbentuk granul. Hasil karakterisasi dengan FTIR menunjukkan terdapat spektra baru yaitu pada panjang gelombang 1514,02 yang merupakan vibrasi OH tekuk dari Cu-OH. Hasil dari degradasi limbah cair jasa pencuci pakaian (laundry), batik dan tempe pada waktu maksimum yaitu 240 menit menghasilkan penurunan nilai COD yang efektif pada limbah tempe yaitu sebesar 80% dengan sinar UV dan 90% dengan sinar matahari. Hasil data statistik uji F menggunakan taraf signifikan 5% dan uji BNT dapat disimpulkan bahwa lama penyinaran berpengaruh terhadap penurunan nilai COD dan menunjukkan hasil yang beda nyata.
English Abstract
Photodegradation is the decomposition process of compounds with the help of light and a photocatalyst. The photodegradation process can be applied in decreasing the value of organic liquid waste COD such as laundry waste, batik and tempe. This study aims to determine the synthesis of TiO2/Cu-Zeolite-Alginate granule photocatalyst activity against the effect of irradiation duration with time variation of 30, 60, 120, 180, 240 minutes and source of irradiation from sun light and UV light. The synthesis of TiO2/Cu was made using the sonication method with (CuNO3)2.3H2O as a source of Cu, then TiO2/Cu photocatalysts were characterized using Fourier Transform Infra Red (FTIR). The photocatalyst was synthesized with alginate and then dropped using a syringe into a CaCl2 3% solution to form granule. The results of the characterization with FTIR showed that there were new spectra at wavelengths of 1514,02 which were OH vibrations of Cu-OH. The results of the degradation of laundry waste, batik and tempe at the optimum time of 240 minutes resulted in a decrease in COD value effective in tempe waste that is equal to 80% with UV light and 90% with sun light. The results of F test statistic data using a significant level of 5% and BNT test can be concluded that the duration of irradiation affects the decrease in COD value and shows the results of a real difference.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2019/209/051910933 |
| Uncontrolled Keywords: | Fotodegradasi, TiO2/Cu-Zeolit-Alginat, Granul, Fotokatalis, Limbah Cair Organik, Photodegradation, TiO2/Cu-Zeolite-Alginate, Garnule, Photocatalyst, Organic Liquid Waste |
| Subjects: | 500 Natural sciences and mathematics > 547 Organic chemistry |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 10 Aug 2020 07:37 |
| Last Modified: | 10 Aug 2020 07:37 |
| URI: | http://repository.ub.ac.id/id/eprint/178833 |
Actions (login required)
 |
View Item |