Malvin, Bryan (2019) Pengaruh Bombardir Partikel Bermuatan Pada Permukaan Plat Aluminium Dengan Gas Nitrogen Menggunakan HVDC Bermuatan Positif. Sarjana thesis, Universitas Brawijaya.
Abstract
Buku skripsi ini menjelaskan hasil penelitian tentang pengaruh bombardir partikel ion pada permukaan plat aluminium dengan dielektrik nitrogen menggunakan HVDC bermuatan positif. Diawali dengan membahas teori terkait penelitian seperti Hukum Coulomb, teorema medan, hingga efek polaritas. Selanjutnya dilakukan pengambilan data berupa nilai tegangan korona (Uc), tegangan tembus (Ud), tegangan uji (Ux) serta nilai arus konduksi (ID) pada variasi nilai tegangan uji, tekanan, dan jarak sela. Selanjutnya dilakukan pengambilan Gambar struktur mikro permukaan plat dengan Scanning Electron Microscope (SEM) untuk menunjukkan kerusakan akibat bombardir ion dengan perbesaran hingga 3000 kali. Setiap satu kali pengukuran dilakukan pergantian elektroda plat untuk melihat struktur mikro permukaan plat akibat bombardir partikel ion pada kondisi yang berbeda, serta dilakukan analisis untuk mengetahui besar energi kinetik partikel ion. Variasi kondisi pengujian yang digunakan dalam pengujian arus konduksi dengan polaritas positif meliputi perubahan jarak sela 2,5 cm dan 5 cm, serta perubahan tekanan dielektrik gas nitrogen yang divariasi mulai dari 558 mBar hingga tekanan normal. Bombardir partikel bermuatan pada suatu kondisi ditemukan terjadi hanya jika nilai tegangan mampu menyebabkan ionisasi pada gas. Bombardir partikel terkuat terjadi dengan kecepatan ion 6.205 m/s dengan energi kinetik partikel 5,59 eV. Terbentuk pola kerusakan yang terpusat akibat bentuk geometris pasangan elektroda yang tidak homogen. Lubang terbesar akibat bombardir terbesar ditemukan sebesar 4,17 μm. Disimpulkan bahwa pada nilai tegangan yang sama, penurunan nilai tekanan menyebabkan jumlah molekul dalam suatu ruang semakin sedikit. Sehingga jarak bebas ion semakin besar dan ion mampu bergerak dengan kecepatan yang lebih tinggi. Kenaikan kecepatan ion berakibat pada kenaikan nilai energi kinetik ion.
English Abstract
This Thesis explained the result of research about charged particle bombardment effect on aluminum plate surface using positive polarity HVDC with nitrogen gas dielectric. Data was collected in values of the corona voltage (Uc), breakdown voltage (Ud), and the conduction current (ID) in condition that varied in test voltage, pressure, and gap distance values. Image taking of the plate surface’s microstructure using Scanning Electron Microscope (SEM) was done to show the damage caused by the ion bombardment with magnification up to 3000 times. The aluminum plate changes everytime a measurement was made due to bombardment of ion particles under different conditions, and an analysis was carried out to determine the kinetic energy of the ion particles. The variation of condition used in the conduction current testing are including the variation of gap distance at 2,5 cm and 5 cm, and the change of Nitrogen gas dielectric pressure from 558 mBar to normal pressure. It was found that ion particle bombardment in a condition only happens only if the test voltage sufficient enough for ionization of gas to occur. The strongest ion particle bombardment occured with an ion velocity at 6.205 m/s with kinetic energy at 5,59 eV. A centralized pattern of damage was formed due to the geometric shape of the non homogeneous electrode pair. The biggest hole due to the bombardment was formed at diameter of 4,17 μm. It was concluded that at the same test voltage, a decrease in the pressure value causes the number of molecules in a space decrease. Causing the ion’s free path to increase making the ion able to move at higher velocity. The higher velocity of an ion corresponds to the increase in the value of ion’s kinetic energy. Resulting in bigger and more destructive ion bombardment.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FT/2019/874/051910653 |
| Uncontrolled Keywords: | Pengaruh bombardir, ion positif, gas nitrogen, polaritas positif. Bombardment effect, positive ion, nitrogen gas, positive polarity. |
| Subjects: | 600 Technology (Applied sciences) > 620 Engineering and allied operations > 620.1 Engineering mechanics and materials > 620.18 Nonferrous metals > 620.186 Alumunium |
| Divisions: | Fakultas Teknik > Teknik Elektro |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 08 Sep 2020 02:41 |
| Last Modified: | 22 Mar 2022 08:59 |
| URI: | http://repository.ub.ac.id/id/eprint/176542 |
Preview |
Text
Bryan Malvin.pdf Download (5MB) | Preview |
Actions (login required)
 |
View Item |