Alfian, Faiz (2019) Pengaruh Suhu Aging Treatment Terhadap Kekuatan Tarik A6061/Al2O3 Pada Proses Squeeze Casting. Sarjana thesis, Universitas Brawijaya.
Abstract
Pada komponen mesin industri dituntut untuk memiliki kualitas yang baik dimana memiliki berat yang ringan namun memiliki sifat material yang kuat, tahan terhadap korosi dan dapat menahan beban yang besar, sehingga dapat menunjang produksi industri tersebut. Salah satu cara yaitu dengan pengecoran logam, banyak jenis pengecoran logam salah satunya yaitu squeeze casting. Dipilihnya squeeze casting karena pada pengecoran logam biasa banyak terjadi cacat porositas, sedangkan pada squeeze casting logam cair dituangkan kedalam cetakan kemudian diberikan tekanan sehingga dapat meminimalisir terjadinya cacat porositas pada logam. Pada penelitian ini menggunakan bahan A6061 diperkuat dengan Al2O3. Dari spesimen hasil squeeze casting diberikan perlakuan panas yaitu dengan proses aging treatment dengan tujuan untuk meningkatkan sifat spesimen tersebut. Aging treatment adalah suatu proses penuaan material dengan cara memanaskan spesimen pada suhu tertentu dan pada waktu tertentu. Pada penelitian ini mengvariasikan suhu aging treatment 100oC, 175oC, 200oC, 250oC, dan 300oC. Pada penelitian ini didapatkan hasil nilai kekuatan tarik paling tinggi yaitu pada variasi suhu aging treatment 300oC yaitu sebesar 240.42 MPa sedangkan untuk nilai kekuatan Tarik paling rendah yaitu pada variasi suhu aging treatment 100oC yaitu sebesar 177.72 MPa. Pada penelitian ini didapatkan hasil semakin tinggi suhu aging treatment maka akan meningkatkan nilai kekuatan tarik pada spesimen tersebut hal tersebut disebabkan karena semakin tinggi suhu aging treatment maka akan menyebabkan terjadi difusi pada struktur dari atom-atom lebih merata. Hal tersebut menunjukkan bahwa suhu aging treatment dapat mempengaruhi nilai kekuatan tarik spesimen.
English Abstract
Industrial machinery components are required to have good quality which have not only a light weight but also strong material properties that are resistant to corrosion and can withstand the large loads, so it can support industrial production. One of the way is by metal casting. There are many types of metal casting, one of them is squeeze casting. Squeeze casting was chosen because porosity defects occured in many ordinary metal casting process. However, in the squeeze casting process, molten metal was poured into the mold and then it was given pressure to minimize the occurrence of defects in metal porosity. This study used A6061 material that was reinforced with Al2O3. From the specimens produced by the squeeze casting, heat treatment was given by the aging treatment process with the aim of increasing the properties of the specimen. Aging treatment is a process of aging material by heating a specimen at a certain temperature and at a certain time. This study varied the aging treatment temperature of 100oC, 175oC, 200oC, 250oC, dan 300oC. In this study, the highest tensile strength values were obtained at the aging treatment temperature variation of 300oC, which was 240.42 MPa while the lowest tensile strength value was at the temperature variation of aging treatment 100oC, which was 177.72 MPa. In this study, it can be concluded that the higher the temperature of aging treatment, the higher the value of tensile strength in the specimen because the higher the temperature of aging treatment will cause diffusion in the structure of the atoms more evenly. This shows that the temperature of aging treatment can affect the value of tensile strength of the specimen.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FT/2019/798/051907681 |
| Uncontrolled Keywords: | squeeze casting, aging treatment, kekuatan tarik, squeeze casting, aging treatment, tensile strength |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 16 Nov 2020 17:36 |
| Last Modified: | 16 Nov 2020 17:36 |
| URI: | http://repository.ub.ac.id/id/eprint/173686 |
Actions (login required)
 |
View Item |