Purba, Aristo (2019) Pengaruh variasi holding time pemanasan awal accumulative roll bonding terhadap kekuatan tarik-geser plat aluminium A1100. Sarjana thesis, Universitas Brawijaya.
Abstract
Kemampuan meningkatkan kualitas bahan mentah dengan biaya yang rendah adalah hal yang terus dikembangkan agar dapat bersaing di zaman sekarang ini, terutama industri logam seperti aluminium. Paduan aluminium berlapis memberikan keuntungan besar dibandingkan paduan aluminium tunggal untuk berbagai aplikasi. Sebagai contoh, struktur mobil listrik pabrikan Tesla Corporation menggunakan paduan aluminium berlapis karena paduan aluminium berlapis memiliki specific strength yang tinggi agar dapat memenuhi kekuatan maksimal di setiap area mobil. Salah satu metode untuk meningkatkan kualitas paduan aluminium berlapis adalah dengan menggunakan metode hot rolling dengan proses accumulative roll bonding. Dalam proses accumulative roll bonding, energi tekan digunakan untuk menggabungkan dua atau lebih lapisan logam secara berulang. Tujuan penelitian ini adalah untuk mengetahui pengaruh waktu holding pemanasan awal terhadap nilai kekuatan tarik-geser pada penggabungan 2 lembar plat aluminium A1100 dengan proses accumulative roll bonding. Variabel bebas yang digunakan dalam penelitian ini adalah waktu holding pemanasan awal 2 lembar plat aluminium A1100 yang telah diberikan persiapan permukaan dan diikat dengan kawat bendrat, dimana variasi waktu holding pemanasan awal adalah 90 menit, 120 menit, dan 150 menit. Variabel terikat yang digunakan dalam penelitian ini adalah nilai kekuatan tarik-geser dari spesimen accumulative roll bonding. Variabel yang terkontrol adalah kecepatan roll: 25rpm, suhu pemanasan awal: 500℃, proses rol: hot rolling, dan rolling ratio: 50%. Hasil dari penelitian ini menunjukkan nilai kekuatan tarik-geser tertinggi adalah 150 MPa pada spesimen dengan waktu holding pemanasan awal 120 menit, dan nilai kekuatan tarik terendah adalah 140 MPa pada spesimen dengan waktu holding pemanasan awal 90 menit. Peningkatan nilai kekuatan tarik-geser disebabkan oleh waktu holding pemanasan awal yang meningkat dan menyebabkan butir semakin seragam ukurannya.
English Abstract
The ability to improve the quality of raw material with low cost is a developed continuously thing to join in the competition nowadays, especially metal industry like aluminium. Multi-layered aluminium alloys offer great benefits over single-aluminium alloys for various applications. For example, the structure of Tesla Corporation fabricated electric car is mostly made of multi-layered aluminium alloy as multi-layered aluminium alloy has high specific strength so it is capable of fulfilling maximum strength on every area of the car. One of the methods to improve the quality of multi-layered aluminium alloy is by using the hot rolling method with the accumulative roll bonding process. In the accumulative roll bonding process, compressive energy is used to bond two or more layers of metal repetitively. The purpose of this research is to know the effect of preheating holding time to the value of tensile-shear strength on the bonding of 2 sheets of aluminium A1100 plate with the accumulative roll bonding process. The independent variables used in this research are the preheating holding time of 2 sheets of aluminium A1100 which have been given surface preparation and tied using steel wire, in which the variation of preheating holding time are 90 minutes, 120 minutes, and 150 minutes. The dependent variable used in this research is the tensile-shear strength value of the accumulative roll bonding specimen. The controlled variables are the roll speed: 25 rpm, preheating temperature: 500℃, roll process: hot rolling, and rolling ratio: 50%. The result of this research showed the highest tensile-shear strength value is 150 MPa for the specimen with preheating holding time of 120 minutes, and the lowest tensile-shear strength value is 140 MPa for the specimen with preheating holding time of 90 minutes. The increment of tensile-shear strength value is caused by the increment of preheating holding time that caused the grain getting uniform in size.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FT/2019/462/051905058 |
| Uncontrolled Keywords: | alumunium A1100, kekuatan tarik-geser, accumulative roll bonding, waktu holding pemanasan awal, aluminium A1100, tensile-shear strength, accumulative roll bonding, preheating holding time |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 13 Nov 2020 16:15 |
| Last Modified: | 13 Nov 2020 16:15 |
| URI: | http://repository.ub.ac.id/id/eprint/173037 |
Actions (login required)
 |
View Item |