Lestari, Domas Indri (2018) Kajian Pengaruh pH dan Lama Penyinaran Terhadap Aktivitas Fotokatalis Beads TiO2N/Zeolit-Kitosan dan TiO2/Zeolit-Kitosan Pada Degradasi Limbah Cair Tempe Dengan Sinar UV. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini bertujuan untuk mengetahui aktivitas fotokatalis beads TiO2N/Zeolit-Kitosan dan TiO2/Zeolit-Kitosan dalam penentuan pH optimum dan lama penyinaran optimum terhadap fotodegradasi limbah tempe. Zeolit diaktivasi dengan menggunakan HCl 0,4 M . TiO2-N disintesis dengan metode sonikasi menggunakan TiO2 dan urea. TiO2 dan TiO2N diimpregnasikan pada zeolit teraktivasi dengan rasio massa optimum 0,4 g/g zeolit. Beads fotokatalis dibuat dengan mencampurkan kitosan dalam asam asetat menggunakan pompa jarum suntik yang diteteskan pada NaOH 1M. Fotodegradasi limbah tempe dilakukan menggunakan sinar UV dan ditentukan nilai COD. Penentuan pH optimum dilakukan dengan variasi pH limbah yaitu 6, 8, 10 dan 12 selama 5 jam. Penentuan lama penyinaran optimum dengan variasi waktu 1, 3, 5 dan 7 jam. Karakterisasi luas permukaan spesifik pada serbuk TiO2N/ZeolitKitosan dan TiO2/Zeolit-Kitosan ditentukan oleh Surface Area Analzyer menggunakan metode BET yaitu 0,418 m2/g dan 6,913 m2/g serta analisis isotherm adsorpsi-desorpsi pada kedua fotokatalis memiliki tipe IV dan dengan metode BJH distribusi TiO2 dan TiO2N keduanya terjadi pada daerah mesopori. Hasil FT-IR fotokatalis setelah degrasi tidak terlihat perubahan spektra yang menunjukkan bahwa asam amino terbentuk, namun hanya terjadi pergeseran spektra. Hasil penelitian pada TiO2/Zeolit-Kitosan dan TiO2N/Zeolit-Kitosan menunjukkan degradasi terjadi pada kondisi optimum pH 12. Lama penyinaran optimum TiO2/Zeolit-Kitosan dan TiO2N/Zeolit-Kitosan diperoleh pada waktu optimum penyinaran 3 jam pada pH optimum 12 mampu mendegradasi sebesar 35,85% dan 30,95%
English Abstract
The purpose of this research is the process of beads photocatalyst of TiO2N/Zeolite-Chitosan and TiO2/Zeolite-Chitosan in determination of optimum pH and optimum irradiation time to photodegradation of tempe waste. The zeolite was activated by using 0.4 M HCl. TiO2-N was synthesized by sonication method using TiO2 and urea. TiO2 and TiO2N are impregnated on activated zeolite with optimum mass ratio of 0.4 g/g zeolite. The photocatalyst beads are made by mixing chitosan in acetic acid using a syringe pump fed to 1M NaOH. Tempe waste photodegradation was performed using UV light and determined COD value. Determination of pH optimum was done with pH value of waste that is 6, 8, 10 and 12 for 5 hours. Determination of duration optimum irradiation with time variation 1, 3, 5 and 7 hours. Specific specific characterization of TiO2N/ ZeoliteChitosan and TiO2/Zeolite-Chitosan powders was determined by Surface Area Analzyer using BET method is 0.418 m2/g and 6.913 m2/g and the adsorption-desorption isotherm analysis on both photocatalysts had type IV and with BJH method TiO2 and TiO2N distributions also occur in mesoporous regions. FT-IR photocatalyst results after degration are no larger than the existing spectrum, thus only occurring after the spectra, the results of TiO2 / Zeolite-Chitosan and TiO2N/Zeolite-Chitosan with optimum pH 12 can degrade waste tempe of 33.33% and 25.00%. The optimum radiation time of TiO2 / Zeolite-Chitosan and TiO2N/Zeolite-Chitosan during 3 hours irradiation with optimum pH 12 were able to degrade by 35.85% and 30.95%.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2018/331/051807384 |
| Uncontrolled Keywords: | Fotokatalis, Limbah tempe, TiO2/Zeolit, TiO2N/Zeolit, pH, Photocatalyst, Tempe liquid waste, TiO2/Zeolit, TiO2N/Zeolit, pH |
| Subjects: | 600 Technology (Applied sciences) > 628 Sanitary engineering > 628.4 Waste technology, public toilets, street cleaning > 628.44 Solid wastes (Refuse) |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Nur Cholis |
| Date Deposited: | 09 Jun 2020 03:21 |
| Last Modified: | 22 Oct 2021 13:43 |
| URI: | http://repository.ub.ac.id/id/eprint/168754 |
Preview |
Text
DOMAS INDRI LESTARI.pdf Download (3MB) | Preview |
Preview |
Text
DOMAS INDRI LESTARI.pdf Download (3MB) | Preview |
Actions (login required)
 |
View Item |