Ashari, Syarifatin Husna (2018) Pengaruh Konsentrasi TiO2N, Rasio Fotokatalis, dan Lama Penyinaran terhadap Aktivitas Fotokatalis TiO2N-Zeolit/Alginat dalam Mendegradasi Limbah Cair Industri Tempe Menggunakan Sinar UV. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini bertujuan untuk mengetahui karakteristik fotokatalis menggunakan Scanning Electron Microscope (SEM) dan Spektrofotometer FT-IR dan mengetahui aktivitas fotokatalis beads TiO2N-zeolit/alginat. Kemampuan aktivitas fotokatalis beads TiO2Nzeolit/alginat dilihat berdasarkan pengaruh konsentrasi TiO2-N, pengaruh rasio fotokatalis, dan lama penyinaran dalam mendegradasi limbah cair industri tempe dengan menggunakan sinar UV. TiO2-N disintesis menggunakan metode sonikasi dengan urea sebagai sumber N. TiO2N-Zeolit beads fotokatalis disintesis dengan mencampurkan TiO2N-Zeolit dan larutan Na-alginat. Kemudian diteteskan menggunakan syringe pump dengan kecepatan 50 mL/jam ke dalam CaCl2 3% (w/v) sehingga terbentuk beads. Variasi konsentrasi TiO2-N yang digunakan adalah 0,3; 0,4; 0,5; dan 0,6 g/g zeolit dan variasi rasio massa fotokatalis yang digunakan adalah 2:1; 3:1; 4:1; dan 6:1 mg/mL dengan lama penyinaran 5 jam. Variasi lama penyinaran yang dilakukan adalah 2, 3, 4, dan 5 jam pada kondisi konsentrasi dan rasio optimum. Hasil karakterisasi SEM terlihat bahwa penambahan dopan N mengubah morfologi dari fotokatalis TiO2. Karakterisasi FT-IR TiO2N menunjukkan serapan Ti-N pada bilangan gelombang 667,91 cm-1. Berdasarkan hasil penelitian diperoleh penurunan nilai COD pada konsentrasi TiO2-N optimum adalah 0,5 (g/g zeolit), rasio fotokatalis dan limbah cair tempe optimum adalah 3:1 dan lama penyinaran optimum adalah 4 jam. Pada kondisi optimum diperoleh penurunan nilai COD sebesar 68,18 %.
English Abstract
The purpose of this research is to know the photocatalyst characteristic using Scanning Electron Microscope (SEM) and FT-IR Spectrophotometer and to know the photocatalyst activity of TiO2Nzeolite/alginate beads. The ability of TiO2N-zeolite/alginate beads photocatalyst activity observed by the influence of TiO2-N concentration, the effect of photocatalyst ratio, and the duration of irradiation in degrading industrial liquid tempe waste by using UV light. TiO2-N was synthesized by sonication method with urea as the source of N. TiO2N-zeolite photocatalyst beads synthesized by mixing TiO2N-zeolite and Na-alginate solution. Then dripped using a syringe pump with a speed of 50 mL/hour into 3% CaCl2 (w/v) to form beads. The variation of TiO2-N concentration used was 0,3; 0,4; 0,5; and 0,6 g/g of zeolite and the variation in the ratio of photocatalyst mass used is 2: 1; 3: 1; 4: 1; and 6: 1 mg/mL with 5 hours irradiation. Variations of radiation duration are 2, 3, 4, and 5 hours at optimum concentration and ratios. The result of SEM Characterization showed that the addition of N dopant will change the morphology of the TiO2 photocatalyst. The characterization of FT-IR TiO2N showed Ti-N peak at wave number 667,91 cm-1. Based on the result of the research, the decreasing of COD value at optimum TiO2-N concentration was 0,5 (g/g zeolite), the optimum photocatalytic ratio and liquid wastewater is 3: 1 and the optimum irradiation time is 4 hours. At the optimum condition, the decreasing value of COD is 68.18%.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2018/344/051807397 |
| Uncontrolled Keywords: | fotokatalis, TiO2N-zeolit, alginat, limbah cair industri tempe, COD, photocatalyst, TiO2N-zeolite, alginate, tempe industrial liquid waste, COD |
| Subjects: | 600 Technology (Applied sciences) > 628 Sanitary engineering > 628.5 Pollution control and industrial sanitation |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Nur Cholis |
| Date Deposited: | 04 Jun 2020 10:11 |
| Last Modified: | 22 Oct 2021 22:19 |
| URI: | http://repository.ub.ac.id/id/eprint/168696 |
Preview |
Text
SYARIFATIN HUSNA ASHARI.pdf Download (2MB) | Preview |
Actions (login required)
 |
View Item |