Yusmawanto, Mukhammad (2018) Rancang Bangun Single Redox Flow Battery (Rfbs) Sebagai Alternatif Penyimpanan Energi Dengan Menggunakan Elektroda Pb Dan Pbo2 Serta H2so4 Sebagai Elektrolit. Sarjana thesis, Universitas Brawijaya.
Abstract
Telah berhasil dilakukan penelitian rancang bangun RFB berbasis asam timbal dengan menggunakan elektrolit asam sulfat 30%. RFB dibuat dengan menggunakan pelat timbal (Pb) dan timbal oksida (PbO2) dengan 3 variasi ukuran yakni 14 x 7,5 cm2, 23,4 x 7,5 cm2 dan 32,7 x 7,5 cm2. Pengukuran dilakukan dengan menggunakan alat Turnigy accucell-6 50 w dengan bantuan software ChargeMaster2.02. Pengujian pengisian-pengosongan baterai dilakukan pada arus konstan 1 A denga lama variasi pengisian yang berbeda yakni 2,5 jam; 2,0 jam; 1,5 jam; 1,0 jam dan 0,5 jam secara berturut-turut. Berdasarkan hasil pengujian diperoleh grafik pengisian-pengosongan dengan data tegangan, arus dan kapasitas terhadap waktu. Hasil pengujian menunjukkan bahwa baterai hasil rancang bangun merupakan baterai sekunder yang bisa diisi ulang (rechargable) dengan tegangan open circuit sebesar 2,05 V. Tegangan pengisian naik secara signifikan di awal pengisian, kemudian naik secara perlahandimana tegangan akhir pengisian tercatat sebesar 2,4 V sedangakan saat pengosongan tegangan turun secara signifikan pada 1,99 V yang kemudian turun perlahan hingga mencapai 1,81 V. Kapasitas baterai naik secara konstan pada pengisian dan pengosongan saat arus yang mengalir konstan sebesar 1 A. Semakin luas pelat yang digunakan dan semakin lama durasi pengisian yang diberikan maka semakin tinggi pula kapasitas baterai yang dihasilkan. Baterai dengan kapasitas terbaik adalah baterai dengan ukuran elektroda 32,7 x 7,5 cm2yang berhasil meyimpan muatan 7853 mAh dengan durasi pengisian 2,5 jam.
English Abstract
In this research, a lead acid redox flow battery (RFB) has been developed with 30% sulfuric acid as an electrolyte. The battery system used Pb and PbO2 plate as electrode with 3 different sizes of 14 x 7.5 cm2, 23.4 x 7.5 cm2, and 32.7 x 7.5 cm2. Turnigy accucell-6 was used as battery management system assisted by ChargeMaster2.02. The battery charge-discharge test was carried out at a constant current of 1 A, with different duration of charge of process. The variations of charge duration are 2.5 hours, 2.0 hours, 1.5 hours, 1.0 hours and 0.5 hours. The data obtained are the test result shows that the designed battery is rechargeable, with an open circuit voltage of 2.05 V. The voltage of charge prosess increases significantly at the beginning, then increases slowly until the final voltage of 2.4 V. The voltage of discharge process decrease slowly down to the cut-off voltage of 1.81 V. The duration and capacity of charge process increase along with the increasing of the are of electrode. Battery with the highest capacity is obtained out size of electrode 32.7 x 7.5 cm2 and duration of charge 2.5 hours, with value 7853 mAh.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2018/144/051805290 |
| Uncontrolled Keywords: | baterai, RFB, Asam Timbal, Kapasitas, tegangan battery, RFB, Lead Acid, Capacity, voltage |
| Subjects: | 600 Technology (Applied sciences) > 669 Metallurgy > 669.4 Lead |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 24 Jun 2020 03:03 |
| Last Modified: | 16 Oct 2021 06:29 |
| URI: | http://repository.ub.ac.id/id/eprint/168304 |
Preview |
Text
Mukhammad Yusmawanto (2).pdf - Published Version Download (2MB) | Preview |
Actions (login required)
 |
View Item |