Adhipratiwi, M. Dwi Putri Prabhawanti (2018) Pengaruh Lama Waktu Pemolesan Permukaan Resin Akrilik Heat Cured Dengan Penambahan Glass Fiber Menggunakan Bubuk Pumice Terhadap Kekuatan Transversa. Sarjana thesis, Universitas Brawijaya.
Abstract
Resin akrilik dipilih sebagai bahan basis gigi tiruan karena bersifat non-toksik dan memiliki warna serasi dengan rongga mulut. Sifat porositas yang dimiliki resin akrilik mengakibatkan penurunan kekuatan transversa terhadap beban yang diterima selama proses pengunyahan. Penambahan glass fiber potongan kecil dan pemolesan dengan lama waktu tertentu menggunakan bubuk pumice merupakan upaya meningkatkan kekuatan transversa serta meminimalisir porositas. Tujuan dari penelitian ini adalah mengetahui pengaruh lama waktu pemolesan bubuk pumice terhadap kekuatan transversa pada resin akrilik heat cured dengan penambahan glass fiber. Penelitian ini merupakan penelitian eksperimental laboratoris, dengan pendekatan posttest only control group design. Sampel yang digunakan sebanyak 24 buah yang dibagi menjadi 4 kelompok yaitu pemolesan selama 15 detik menggunakan bubuk pumice tanpa penambahan glass fiber (kelompok kontrol), waktu pemolesan menggunakan bubuk pumice selama 15, 30, dan 45 detik dengan penambahan glass fiber (kelompok eksperimen A, B dan C). Data dari jumlah pengukuran rerata kekuatan transversa dianalisis menggunakan Oneway Anova dan post hoc Tukey. Hasil penelitian menunjukkan kelompok eksperimen A, B dan C mengalami penurunan kekuatan transversa secara bermakna pada masing-masing kelompok serta mengalami peningkatan kekuatan transversa secara bermakna pada kelompok eksperimen dibanding dengan kelompok kontrol. Kesimpulan penelitian ini adalah kekuatan transversa tertinggi didapat pada pemolesan selama 15 detik menggunakan bubuk pumice pada permukaan resin akrilik heat cured dengan penambahan glass fiber.
English Abstract
Acrylic resin was chosen as a denture base material because it is nontoxic and has a color matching with the oral cavity. The porosity properties of acrylic resin resulted in a decrease in transverse strength to the load received during the mastication process. Addition of small pieces of glass fiber and polishing for a certain period of time using pumice powder is an effort to increase transverse strength and minimize porosity. The purpose of this study was to determine the effect of the polishing time of pumice powder on the transverse strength of heat cured acrylic resin with the addition of glass fiber. This research is a laboratory experimental study, with a post-test only control group design approach. 24 samples were divided into 4 groups, there are polishing for 15 seconds using pumice powder without the addition of glass fiber (control group), polishing time using pumice powder for 15, 30 and 45 seconds with the addition of glass fiber (experimental group A, B and C). Data from the number of measurements of mean transverse strength were analyzed using Oneway Anova and post hoc Tukey. The results showed that the experimental groups A, B and C experienced a significantly increased transverse strength in the experimental group compared to the control group. The conclusion of this study was that the highest transverse strength was obtained by polishing for 15 seconds using pumice powder on the surface of the heat cured acrylic resin with the addition of glass fiber.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FKG/2018/87/051900436 |
| Uncontrolled Keywords: | Bubuk pumice, glass fiber, kekuatan transversa, resin akrilik heat cured, waktu pemolesan Pumice powder, glass fiber, transverse strength, Heat cured acrylic resin, polishing time |
| Subjects: | 600 Technology (Applied sciences) > 617 Surgery, regional medicine, dentistry, ophthalmology, otology, audiology > 617.6 Dentistry > 617.69 Prosthodontics > 617.695 Materials / Dental materials |
| Divisions: | Fakultas Kedokteran Gigi > Kedokteran Gigi |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 18 May 2020 00:25 |
| Last Modified: | 22 Oct 2021 14:37 |
| URI: | http://repository.ub.ac.id/id/eprint/167760 |
Preview |
Text
M. Dwi Putri Prabhawanti Adhipratiwi (4).pdf Download (16MB) | Preview |
Actions (login required)
 |
View Item |