Sukoyo, Agung (2019) Pengaruh Konsentrasi Dan Jenis Aktivator Terhadap Karakteristik Karbon Aktif Mikroalga Chlorella Vulgaris Dengan Aktivasi Kimia Menggunakan Iradiasi Gelombang Mikro. Magister thesis, Universitas Brawijaya.
Abstract
Mikroalga Chlorella vulgaris telah digunakan sebagai bahan baku dalam sintesis serbuk karbon aktif. Mikroalga kering dikarbonisasi pada suhu 5000C selama 30 menit dengan laju kenaikan temperatur 100C per menit untuk mendapatkan arang mikroalga. Kombinasi perlakuan aktivasi kimia menggunakan KOH, H3PO4 dan ZnCl2 dengan konsentrasi 10, 30, dan 50% dibantu oleh iradiasi gelombang mikro telah digunakan untuk membuatkan karbon aktif. Sifat-sifat karbon aktif dianalisis meliputi hasil rendemen, kadar abu, kandungan zat volatil, kandungan karbon aktif murni, daya serap larutan iodin, luas permukaan BET, dan pencitraan karbon aktif menggunakan SEM- EDX. Hasil penelitian menunjukkan bahwa mikroalga Chlorella vulgaris memiliki kandungan unsur karbon 16,09% yang memiliki potensi untuk digunakan sebagai bahan baku karbon aktif. Aktivasi yang dilakukan mampu menurunkan kandungan kadar abu dibandingkan dengan arang mikroalga tanpa perlakuan, kadar zat teruap cenderung lebih tinggi diduga karena pori-pori karbon ditempati oleh zat volatile, kadar karbon secara umum lebih tinggi dibandingkan dengan arang mikrolga tanpa perlakuan dengan hasil terbaik menggunaka aktivator asam. Karakteristik perlakuan terbaik pada rendemen diperoleh dengan aktivasi menggunakan ZnCl2 dengan nilai rendemen 66.51%, kadar abu terendah diperoleh dengan aktivasi menggunakan H3PO4 30% dengan nilai kadar abu 11.19%, kadar zat teruap terendah diperoleh dengan aktivasi menggunakan H3PO4 10% dengan nilai kadar zat teruap 19.79%, kandungan karbon aktif murni tertinggi dan daya serap iodin diperoleh dengan aktivasi menggunakan H3PO4 50% dengan kandungan karbon aktif murni 56.66%, dan daya serap iodin 330.39 mg/g hasil pengujian luas permukaan BET pada perlakuan yang memiliki daya serap iodin tertinggi menunjukan luas permukaan 109.273 m²/g dan rerata diameter pori 5.50 nm. Hasil pencitraan SEM EDX menunjukkan pembentukan pori pada permukaan karbon aktif, dengan unsur karbon mencapai 72.31%
English Abstract
Microalgae Chlorella vulgaris has been used as a raw material in the synthesis of activated carbon powder. Dry microalgae is carbonized at a temperature of 5000C for 30 minutes to obtain microalgae charcoal. The combination of chemical activation treatments using KOH, H3PO4 and ZnCl2 with concentrations of 10, 30, and 50% assisted by microwave irradiation has been used to prepare activated carbon. The properties of activated carbon were analyzed included yield, ash content, volatile substance content, pure activated carbon content, iodine solution absorbency, BET surface area and activated carbon imaging using SEM EDX. The results showed that Chlorella vulgaris microalgae has a carbon element content of 16.09% which has the potential to be used as an activated carbon feedstock. Activation carried out was able to reduce the content of ash compared to microalgae charcoal without treatment, the level of volatile substances tends to be higher because the pores of carbon are occupied by volatile substances. The best treatment characteristics in the yield were obtained by activation using ZnCl2 with a yield value of 66.51%, the lowest ash content was obtained by activating using 30% H3PO4 with ash content of 11.19%, the lowest level of volatile substances obtained by activation using 10% H3PO4 with volatile substance values 19.79 %, the highest pure activated carbon content and iodine absorption was obtained by activating using 50% H3PO4 with 56.66% pure activated carbon content, and iodine absorption capacity of 330.39 mg / g as a result of testing BET surface area in the treatment which had the highest iodine absorption capacity showing surface area 109,273 m² / g and the average pore diameter is 5.50 nm. SEM EDX imaging results show pore formation on the surface of activated carbon, with carbon elements reaching 72.31%.
| Item Type: | Thesis (Magister) |
|---|---|
| Identification Number: | TES/579.8/SUK/p/2019/041901532 |
| Uncontrolled Keywords: | ALGAE |
| Subjects: | 500 Natural sciences and mathematics > 579 Natural history of microorganisms, fungi, algae > 579.8 Algae / Algae culture / Microalgae--Cultures and culture media |
| Divisions: | S2/S3 > Doktor Teknik Industri Pertanian, Fakultas Pertanian |
| Depositing User: | Nur Cholis |
| Date Deposited: | 04 Apr 2019 02:22 |
| Last Modified: | 22 Oct 2021 06:12 |
| URI: | http://repository.ub.ac.id/id/eprint/166469 |
Preview |
Text
AGUNG SUKOYO.pdf Download (2MB) | Preview |
Actions (login required)
 |
View Item |