Putri, AfridaKurnia (2012) Evaluation of the Extraction Efficiency of Activated Carbon Prepared from Rice Husks as Solid-Phase Extraction Sorbent to Determine Nonylphenol in Water Sample. Magister thesis, Universitas Brawijaya.
Abstract
Telah dilakukan suatu studi mengenai effisiensi ekstraksi karbon aktif (ACs) dari sekam padi sebagai adsorben untuk ekstraksi fasa padat (SPE) terhadap isomer-isomer dari 4-nonylphenol (4-NPs) di dalam sampel air. ACs dari sekam padi akan cenderung memiliki luas permukaan yang randah akibat dari tingginya kadar abu didalamnya, namun dalam kaitan dengan aplikasinya untuk SPE, terdapat beberapa faktor yang perlu diperhatikan, seperti keberadaan dari gugus fungsi permukaan yang mampu meningkatkan interaksi dari ACs (non-polar) dengan analit di dalam air (polar). Pada kasus ini, gugus silanol yang terkandung pada abu sekam diduga akan memberikan efek positif pada efisiensi ekstraksi untuk 4-nonylphenol. ACs pada penelitian ini dibuat dari sekam padi yang diimpreknasi dengan ZnCl 2 dan dikarbonisasi pada 800 o C. Untuk mengetahui peranan dari silika, dibuat tiga buah ACs, yaitu, ACs tanpa perlakuan basa (AC–Si, mengandung silika), ACs yang di perlakukan dengan basa (AC–B–Si, mengandung sejumlah kecil silika), dan ACs dari sekam yang telah diperlakukan dengan basa (AC–B, tidak mengandung silika), dan luas permukaan yang terukur dari ketiga karbon aktif tersebut secara berturut-turut adalah 1352 m 2 /g, 1666 m 2 /g, and 1712m 2 /g. ACs yang diperlakukan dengan basa mempunyai luas permukaan paling tinggi, yang mengindikasikan bahwa proses penghilangan silika dengan basa akan meningkatkan pembukaan sistem pori-pori karbon. Namun, efisiensi ekstraksi (SPE) yang terukur oleh GC-MS menunjukkan hal yang berlainan (yaitu: AC–Si= 32.08%, AC–B–Si= 82.63%, AC–B=51.78%), AC–B–Si menjadi sorbent terbaik untuk SPE. Hal ini mengindikasikan bahwa meskipun silika biasanya dapat megakibatkan penurunkan luas permukaan dari ACs, namun kandungan silika yang terkontrol sebagai gugus polar mempunyai efek positif dalam peningkatan interaksi antara karbon aktif dengan 4-NPs.
English Abstract
Enrichment efficiency of activated carbon (ACs) from rice husks (RHs) as a new sorbent for solid-phase extraction (SPE) to extract 4-nonylphenol isomers (4-NPs) in water samples was evaluated. ACs prepared from RHs usually exhibits low specific surface area due to its high ash content, but in case of its application for SPE, re are o r factors need to be considered, such as existence of functional groups inside sorbent, that can enhance interaction of non-polar sorbent with analyte in water matrices. In this case, silanol groups from ash content may affect extraction efficiency for 4-NPs. ACs made from RHs were chemically impregnated with ZnCl 2 and carbonized at 800 o C. To investigate role of silica, three types of ACs were prepared, i.e., untreated ACs (AC–Si, contain silica), base treated ACs (AC–B–Si, remain some silica inside), and ACs made by base treated RHs (AC–B, no silica), and surface area obtained from se treatments were 1352 m 2 /g, 1666 m 2 /g, and 1712m 2 /g respectively. ACs made by base treatment has a highest surface area (related to BET), which indicated that silica removal process promotes formation of open pore system on ACs and enhances surface area of ACs. However, extraction efficiency measured by GC-MS in SPE process showed reversal trends (i.e., AC–Si= 32.08%, AC–B–Si= 82.63%, AC–B=51.78%), among m AC–B–Si sorbent reveal best performance in SPE process. It is indicated that although silica usually exhibits low specific surface area, but control presence of silica as a polar functional group has a positive influence in interaction between non-polar sorbent and 4-NPs.
| Item Type: | Thesis (Magister) |
|---|---|
| Identification Number: | TES/662.93/PUT/e/041301377 |
| Subjects: | 600 Technology (Applied sciences) > 662 Explosives of explosives, fuels, related products > 662.9 Nonfuel carbons |
| Divisions: | S2/S3 > Magister Matematika, Fakultas MIPA |
| Depositing User: | Endro Setyobudi |
| Date Deposited: | 09 Apr 2013 11:33 |
| Last Modified: | 09 Apr 2013 11:33 |
| URI: | http://repository.ub.ac.id/id/eprint/160119 |
Actions (login required)
 |
View Item |