Fitriani, Novi Artika (2016) Desain Sistem Plasma Nitrogen Dengan Kontrol Sistem Pendingin Substrat Dan Studi Pengaruh Temperatur Substrat Terhadap Kekasaran Serta Sifat Hidrofobik Lapisan Polistiren Di Atas Substrat Kaca. Sarjana thesis, Universitas Brawijaya.
Abstract
Pada penelitian ini dilakukan desain sistem pengontrol temperatur substrat dengan sistem pendingin termoelektrik pada proses perlakuan permukaan plasma nitrogen. Selanjutnya studi pengaruh temperatur substrat terhadap kekasaran dan sifat hidrofobik lapisan polistiren (PS) di atas substart kaca dengan teknik plasma nitrogen. Lapisan polistiren dilapiskan dengan teknik spin coating dengan kecepatan 2000 rpm. Uji kekasaran permukaan PS sebelum dan sesudah perlakuan permukaan dengan plasma nitrogen diobservasi dengan Topography Measurement System (TMS12000), sedangkan observasi sifat hidrofobik dilakuan dengan mengukur sudut kontak aquades yang diteteskan pada permukaan PS menggunakan pengukur sudut kontak cairan. Plasma nitrogen dibangkitkan dalam reaktor vakum kapasitif di atas substrat kaca yang telah dilapisi lapisan polistiren (PS) dengan variasi temperatur substrat 600C, 700C dan 800C. Hasil yang didapatkan menunjukkan bahwa sistem pendingin substrat bekerja kurang maksimal pada sistem plasma karena terpengaruh oleh karakteristik dari plasma. Hasil observasi TMS didapatkan nilai kekasaran cenderung menurun dengan naiknya temperatur begitupun dengan nilai sudut kontak, kecuali pada temperatur 600C nilai sudut kontaknya meningkat. Dari hasil tersebut dapat disimpulkan bahwa sifat hidrofobisitas permukaan tidak sepenuhnya dipengaruhi oleh kekasaran permukaan.
English Abstract
This research has been conducted design of the temperature substrate control system with a thermo-electric cooling system in the process of nitrogen plasma surface treatment. Anather objective is to study the influence of substrate temperature at roughness and hydrophobicity properties of polystyrene (PS) layer above substart glass with nitrogen plasma technique. A layer of polystyrene was mounted with spin coating technique with a speed of 2000 rpm. Surface roughness observation of PS before and after treated in nitrogen plasma is done by Topography Measurement System (TMS 1200), while observation hydrophobicity test has been done by measure the contact angle of aquades droplet on the PS surface by using Contact Angle Measurement equipment. Nitrogen plasma has been generated in the capasitive reactor at vacuum reactor capacitive over the glass substrate that has been coated with a layer of PS with variations of temperature the substrate 600C, 700C and 800C. The result shows that the cooling substrate system works less maximum in plasma system due to be the plasma characteristics . TMS result shows that the roughness tends to decrease with a rise of temperature and the contact angle down in line with the rise in temperature, except the contact angle is increase at temperature of 600C. From that result it can be concluded that it is not fully hydrophobicity properties is affected by surface roughness.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2016/428/051610365 |
| Subjects: | 500 Natural sciences and mathematics > 530 Physics |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika |
| Depositing User: | Kustati |
| Date Deposited: | 01 Nov 2016 08:42 |
| Last Modified: | 20 Mar 2022 13:37 |
| URI: | http://repository.ub.ac.id/id/eprint/154962 |
Preview |
Text
Novi Artika Fitriani.pdf Download (2MB) | Preview |
Actions (login required)
 |
View Item |