Wardhani, Lucky (2016) Studi Pengaruh Lama Penyinaran dan Penggunaan Kembali Fotokatalis Beads TiO2-N/Zeolit-kitosan terhadap Degradasi Metilen Biru secara Fotokatalitik. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini bertujuan untuk mensintesis fotokatalis TiO2-N/zeolit-kitosan serta mengetahui pengaruh lama waktu penyinaran dan efektivitas penggunaan kembali (reuse) fotokatalis terhadap degradasi dengan metilen biru. Aktivasi zeolit menggunakan HCl 0,4 M. TiO2N disintesis dengan metode sonikasi menggunakan TiO2 dan urea dengan perbandingan mol 3:20. TiO2N dan zeolit aktivasi dilakukan impregnasi selama 5 jam. Fotokatalis dalam bentuk beads disintesis dari TiO2-N/zeolit dan kitosan kemudian diteteskan menggunakan syringe pump dan ditampung dalam NaOH 0,4 M. Karakterisasi fotokatalis dilakukan menggunakan FT-IR, SAA, dan SEM. Aktivitas fotokatalis diuji pada metilen biru 20 mg/L pH 12 di bawah sinar matahari selama 3 jam. Hasil karakterisasi FT-IR menunjukkan serapan N-H pada bilangan gelombang 3743,57 cm-1 yang merupakan gugus aktif kitosan telah terikat pada fotokatalis. Morfologi SEM TiO2-N/zeolit-kitosan terdapat struktur kitosan menyerupai jarum pada permukaan fotokatalis. Dari data SAA dengan metode BET menunjukkan TiO2-N/zeolit-kitosan memiliki luas permukaan 306,275 m2/g, rerata jejari pori 29,13 Å, dan total volume pori 4,462x10-1 cm3/g. Hasil karakterisasi DRS, fotokatalis TiO2-N/zeolit-kitosan sebelum dan sesudah degradasi memiliki energi band gap yaitu 3,2 eV dan 2,4 eV. Lama penyinaran optimum degradasi yaitu 3 jam dengan kemampuan degradasi 92,84%, efektivitas reuse TiO2-N/zeolit-kitosan dapat digunakan hingga keempat kali dengan kemampuan degradasi 23,63%.
English Abstract
This research purpose to synthesized TiO2-N/zeolite-chitosan and know radiation duration effect and also reuse photocatalyst effectiveness of methylene blue degradation process. Zeolite was activated in HCl 0,4 M. TiO2N synthesized has been done on TiO2 and urea by sonication methods, TiO2 and urea mole ratio is 3:20. Impregnation TiO2N and zeolite has been carried out for 5 hours. TiO2-N/zeolite-chitosan beads photocatalyst was synthesized by mixing TiO2-N/zeolite and chitosan/acetic acid subsequently dripped into a solution of NaOH 0,4 M. Characterization of photocatalyst have been conducted by FTIR, SAA, and SEM. Photocatalyst activity was tested by degradation methylene blue solution 20 mg/L pH 12, then irradiated with sunlight for 3 hours. Photocatalyst with FTIR characterization showed peaks N-H at 3743,57 cm-1 that showing active group of chitosan has been bound to photocatalyst. Morphology of TiO2-N/zeolite-chitosan with SEM caracterization showed chitosan structure like a needle at photocatalyst surface. From the data SAA by the BET method, showed TiO2-N/zeolite-chitosan has a surface area 306,275 m2/g, average radius pore 29,13 Å, and total pore volume 4,462x10-1 cm3/g. The caracterization results of DRS, TiO2-N/zeolite-chitosan photocatalyst before and after degradation has an band gap energy 3,2 eV and 2,4 eV. Irradiation optimum degradation is 3 hours with 92,84% degradation capability, effectiveness of TiO2-N/zeolite-chitosan reuse can be used up to 4 times with 23,63% degradation ability.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2016/381/051610318 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Kustati |
| Date Deposited: | 04 Nov 2016 14:44 |
| Last Modified: | 04 Nov 2016 14:44 |
| URI: | http://repository.ub.ac.id/id/eprint/154910 |
Actions (login required)
 |
View Item |