Fraditasari, Risca (2015) Pengaruh Konsentrasi Fotokatalis TiO2-N terhadap Fotodegradasi Methyl Orange Menggunakan Sinar UV dan Sinar Matahari. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini bertujuan untuk mengetahui degradasi methyl orange menggunakan fotokatalis TiO2-N dengan mempelajari pengaruh sinar UV dan sinar matahari, variasi konsentrasi TiO2-N yang digunakan, lama penyinaran, serta efektivitas penggunaan kembali (reuse) fotokatalis TiO2-N. Sintesis fotokatalis TiO2-N dilakukan dengan perbandingan mol TiO2:urea 10:0,1 menggunakan metode sonikasi. Karakterisasi fotokatalis dilakukan dengan menggunakan spektrofotometer FTIR, UV-DRS, dan Particle Size Analyzer. Aktivitas fotokatalis TiO2-N diuji menggunakan 25 mL larutan methyl orange 10 mg/L dengan variasi konsentrasi TiO2-N sebesar 1,6; 3,2; 4,8; 6,4; dan 8,0 g/L pada penyinaran sinar UV dan sinar matahari selama 3 jam. Pada variasi lama penyinaran, waktu yang digunakan adalah 15, 30, 45, 60, 120, 180, dan 240 menit dengan konsentrasi fotokatalis TiO2-N optimum sebesar 3,2 g/L. Konsentrasi larutan methyl orange setelah penyinaran ditentukan menggunakan spektrofotometer UV-Vis pada panjang gelombang 464,3 nm. Hasil karakterisasi dengan FTIR menunjukkan bahwa pada TiO2-N terdapat serapan khas dari Ti-N pada bilangan gelombang 509,17 cm-1 dan N-H bending pada 1643,24 cm-1. Energi band gap dari TiO2-N sebesar 3,34 eV dengan ukuran partikel sebesar 0,68 hingga 30,22 μm. Dari hasil penelitian, diperoleh bahwa penyinaran dengan sinar matahari menghasilkan degradasi lebih baik daripada sinar UV. Berdasarkan hasil uji statistika, konsentrasi TiO2-N yang paling optimum untuk degradasi methyl orange adalah sebesar 3,2 g/L dengan persen degradasi sebesar 93,93% dan lama penyinaran paling optimum pada 120 menit dengan persen degradasi sebesar 89,46% di bawah sinar matahari. Fotokatalis TiO2-N dapat digunakan kembali hingga pemakaian ke-3 pada sinar UV dan ke-2 pada sinar matahari, dengan adanya peningkatan persen degradasi pada pemakaian ke-2.
English Abstract
This research aims to determine the degradation of methyl orange using TiO2-N photocatalyst by studying the effect of UV light and solar light irradiation, the variations of TiO2-N concentration, the irradiation time, and the reusability of TiO2-N photocatalyst. TiO2-N photocatalyst was synthesized by sonication method with a mol ratio of TiO2:urea is 10:0,1. Characterization of photocatalyst was investigated using FTIR spectrophotometer, UV-DRS, and Particle Size Analyzer. Activity of TiO2-N photocatalyst was tested on 25 mL of methyl orange at concentration 10 mg/L through variations of TiO2-N concentration are 1,6; 3,2; 4,8; 6,4; and 8,0 g/L using UV light and solar light irradiation for 3 hours. Time was used on variation of irradiation time are 15, 30, 45, 60, 120, 180, dan 240 minutes using 3,2 g/L TiO2-N which is the most optimum concentration of TiO2-N. The concentration of methyl orange which had been exposured was measured using UV-Vis spectrophotometer at 464,3 nm. The result of characterization using FTIR showed that there was a characteristic absorption of Ti-N at 509,17 cm-1 and N-H bending at 1643,24 cm-1. Band gap energy of TiO2-N is 3,34 eV and its particle size is 0,68 until 30,22 μm. This research concluded that solar light irradiation obtained higher degradation of methyl orange than UV light irradiation. Based on statistical test, the most optimum concentration of TiO2-N for methyl orange degradation is 3,2 g/L TiO2-N which gave 93,93% of precent degradation and the most optimum irradiation time is 120 minutes which gave 89,46% of percent degradation under the solar light irradiation. TiO2-N photocatalyst could be used until three cycles on UV light irradiation and two cycles on solar light irradiation. Keywords: degradation, methyl orange, photocatalyst, solar light, TiO2-N
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2015/77/051501548 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Endang Susworini |
| Date Deposited: | 23 Feb 2015 11:22 |
| Last Modified: | 23 Feb 2015 11:22 |
| URI: | http://repository.ub.ac.id/id/eprint/154571 |
Actions (login required)
 |
View Item |