Adsorpsi Kadmium(II) oleh Biomassa Azolla microphylla Diesterifikasi dengan Asam Sitrat: Kajian Desorpsi Menggunakan HNO3.

DwikaAdha, Shofi (2015) Adsorpsi Kadmium(II) oleh Biomassa Azolla microphylla Diesterifikasi dengan Asam Sitrat: Kajian Desorpsi Menggunakan HNO3. Sarjana thesis, Universitas Brawijaya.

Abstract

Penelitian tentang desorpsi kadmium(II) oleh biomassa Azolla microphylla diesterfikasi dengan asam sitrat menggunakan agen pendesorpsi larutan asam nitrat telah dilakukan. Tujuan dari penelitian ini yaitu menentukan konsentrasi larutan asam nitrat dan waktu kontak optimum desorpsi kadmium(II). Adsorben disiapkan dengan cara mencampurkan 5 gram biomassa Azolla microphylla ukuran 120 – 150 meshke dalam 50 mLlarutan asam sitrat 0,80 M dan diaduk selama 2 jam. Campuran biomassa-sitrat dikeringkan pada temperatur 60C dan dilanjutkan dengan pemanasan pada temperatur 120C selama 3,5 jam. Percobaan adsorpsi dilakukan dengan mengocok suspensi 0,10 gram adsorben ke dalam 25 mL larutan kadmium(II) 100 mg/L pH 6 selama 60 menit. Percobaan desorpsi dilakukan dengan cara mensuspensikan adsorben yang telah mengikat kadmium(II) ke dalam 25 mL larutan asam nitrat dengan variasi konsentrasi 0,1; 0,5; 1,0; 1,5; dan 2,0 M selama 60 menit dan dilanjutkan dengan variasi waktu kontak 30, 45, 60, 75, dan 90 menit menggunakan larutan asam nitrat dengan konsentrasi optimum. Konsentrasi kadmium(II) setelah adsorpsi dan desorpsi ditentukan menggunakan Spektrofotometer Serapan Atom. Hasil penelitian menunjukkan bahwa konsentrasi larutan asam nitrat dan waktu kontak berpengaruh terhadap desorpsi kadmium(II) yang terikat pada biomassa Azolla microphylla yang diesterifikasi dengan asam sitrat. Kondisi optimum untuk desorpsi kadmium(II) terjadi pada penggunaan larutan asam nitrat 1,0 M dengan waktu kontak selama 60 menit dengan perolehan persentase desorpsi sebesar 99,27±0,08%.

English Abstract

Research about desorption of cadmium(II) bound to Azolla microphylla biomass esterified by citric acid using nitric acid solution as desoprtion agent has done. The purpose of this research are to determine the concentration of nitric acid solution and contact time optimum for desorption of cadmium(II).Adsorbent prepared by mixing 5 gram of Azolla microphylla biomass of 120 – 150 into 50 mL 0,8 M citric acid solution and stirred for 2 hours. Biomass-citrate mixture was dried at 60C followed by heating at 120C for 3,5 hours. Adsorption experiments were done by shaking a suspension of 0,10 gram adsorbent into 25 mL cadmium(II) 100 mg/L pH 6 for 60 minutes. Desorption were performed by suspending the adsorbent that bound cadmium(II) into 25 mL nitric acid solution with concentration variation of 0,1; 0,5; 1,0; 1,5; and 2,0 M for 60 minutes and followed by contact time variation of 30, 45, 60, 75, and 90 minutes using nitric acid solution at the optimum concentration. The concentration of cadmium(II) that was desorpted into desorption solution determined using atomic absorption spectrophotometer. The result showed that nitric acid concentration and contact time influenced the desorption of cadmium(II) bound to Azolla microphylla biomassa esterified by citric acid. Optimum condition of cadmium(II) desorption occurred in the use of 1,0 M nitric acid solution and contact time during 60 minutes with desorption percentage of 99,27±0,08%.

Item Type:	Thesis (Sarjana)
Identification Number:	SKR/MIPA/2015/31/051501593
Subjects:	500 Natural sciences and mathematics > 510 Mathematics
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam > Matematika
Depositing User:	Samsul Arifin
Date Deposited:	24 Feb 2015 12:03
Last Modified:	24 Feb 2015 12:03
URI:	http://repository.ub.ac.id/id/eprint/154350

Full text not available from this repository.

Actions (login required)

View Item