SeptianiSinaga, Ria (2015) Adsorpsi Seng(II) oleh Biomassa Azolla microphylla Diesterifikasi dengan Asam Sitrat: Kajian Desorpsi Menggunakan HCl. Sarjana thesis, Universitas Brawijaya.
Abstract
Telah dilakukan penelitian tentang desorpsi seng(II) yang terikat oleh biomassa Azolla microphylla diesterifikasi dengan asam sitrat menggunakan agen pendesorpsi larutan HCl. Tujuan penelitian ini adalah menentukan konsentrasi larutan HCl dan waktu kontak optimum terhadap desorpsi seng(II). Esterifikasi dilakukan dengan cara mencampurkan 5 gram biomassa A. microphyllaberukuran 120-150 mesh ke dalam 50 mL larutan asam sitrat 0,8 M dan diaduk selama 2 jam. Campuran biomassa-sitrat dikeringkan pada suhu 60oC hingga kering dan dilanjutkan dengan pemanasan selama 3,5 jam pada suhu 120oC. Percobaan adsorpsi dilakukan dengan cara mengocok suspensi 0,10 g adsorben dalam 25 mL larutan seng(II) 100 mg/L pH 6 selama 45 menit. Percobaan desorpsi dilakukan dengan cara mensuspensikan adsorben yang telah mengikat seng(II) ke dalam 25 mL larutan HCl dengan variasi konsentrasi 0,1 M; 0,5 M; 1 M; 1,5 M; 2 M kemudian dikocok selama 45 menit dan dilanjutkan dengan variasi waktu kontak 30, 45, 60, 75 dan 90 menit menggunakanlarutan HCl dengan konsentrasi optimum. Konsentrasi seng(II) yang terdesorpsi ke dalam larutan pendesorpsi ditentukan menggunakan spektrofotometer serapan atom. Hasil penelitian menunjukkan bahwa konsentrasi HCl dan waktu kontak berpengaruh terhadap desorpsi seng(II) yang terikat oleh biomassa A. microphylla yang diesterifikasi dengan asam sitrat. Kondisi optimum desorpsi seng(II) terjadi pada penggunaan larutan HCl 1,0 M dan waktu kontak 45 menit dengan persentase desorpsi sebesar 97,78%.
English Abstract
Research about desorption of zinc(II) bound by Azolla microphylla biomass esterified by citric acid using HCl solution has been performed. The purpose of this study are to determine the concentration of HCl and contact time optimum for desorption of zinc(II). Esterification was conducted by mixing 5 g of A. microphyllabiomass of 120-150 mesh into 50 mL of 0.8 M citric acid solution and stirred for 2 hours. Biomass-citrate mixture was dried at 60C followed by heating for 3.5 hours at 120C. Adsorption were done by shaking a suspension of 0.10 g biosorbent in 25 mL of zinc(II) 100 mg/L pH 6 for 45 minutes. Desorption was done by suspending the biosorbentthat bound zinc(II) into 25 mL of HNO3 solutions with variation of concentration of 0.1; 0.5; 1.0; 1.5 and 2.0 M, during 45 minutes and followed by variation of the contact time of 30, 45, 60, 75 and 90 minutes using HCl solution with optimum concentration. The concentration of zinc(II) that was desorpted into desorption solution was determined using atomic absorption spectrophotometer. The results showed that HCl concentration and contact time affected the desorption of zinc(II)bound by the biomass of A. microphylla esterified by citric acid. Optimum conditions of zinc(II) desorption occurred in the use of a solution of 1.0 M HCl solution and contact time of 45 minutes gave the percentage of desorption of 97.78%.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2015/30/051501592 |
| Subjects: | 500 Natural sciences and mathematics > 510 Mathematics |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Matematika |
| Depositing User: | Samsul Arifin |
| Date Deposited: | 24 Feb 2015 11:57 |
| Last Modified: | 24 Feb 2015 11:57 |
| URI: | http://repository.ub.ac.id/id/eprint/154339 |
Actions (login required)
 |
View Item |