Lestari, YeniDwi (2015) Pengaruh Komposisi Fotokatalis TiO2-N dalam Zeolit terhadap Degradasi Methylene Blue menggunakan Sinar Matahari. Sarjana thesis, Universitas Brawijaya.
Abstract
Tujuan penelitian ini adalah sintesis fotokatalis TiO2-N/zeolit serta mengkaji pengaruh sinar, komposisi massa TiO2-N dalam zeolit, lama penyinaran dan efektivitas penggunaan kembali (reuse) fotokatalis terhadap degradasi methylene blue. TiO2-N/zeolit dibuat melalui metode sonikasi dengan mencampurkan TiO2 dan urea (10:1) untuk membentuk TiO2-N lalu diimpregnasikan ke dalam zeolit dengan variasi komposisi TiO2-N (0,6; 1,2; 1,8; 2,4; 3,0 g dalam 3g zeolit). Fotokatalis dikarakterisasi dengan spektrofotometer FTIR, UV-Vis Diffuse Reflectance dan Particle Size Analyzer. Jenis sinar yang digunakan adalah sinar UV, sinar matahari dan pembanding kondisi gelap. Proses fotokatalitik dilakukan melalui fotodegradasi 25 mL methylene blue 20 mg/L dengan 50 mg fotokatalis dan disinari selama 50 menit. Variasi lama penyinaran dilakukan selama 5, 10, 20, 30, 40, 50, 60, 90 dan 120 menit menggunakan fotokatalis dengan komposisi optimal (0,6 g TiO2-N/g zeolit). Konsentrasi methylene blue sebelum dan setelah penyinaran diukur menggunakan spektrofotometer UV-Vis pada λ 664nm. Hasil penelitian menunjukkan bahwa dari karakterisasi FTIR terbentuknya TiO2-N pada matriks zeolit ditunjukkan dengan adanya serapan pada bilangan gelombang 1637,45cm-1 dan 680,83cm-1. Berdasarkan karakterisasi DR UV-Vis diperoleh energi band gap TiO2-N/zeolit sebesar 3,33 eV, dari karakterisasi PSA diperoleh ukuran partikel antara (1,04-37,63)?m dengan kadar N sebesar 1,99%. Penyinaran sinar matahari memberikan hasil degradasi paling baik dibandingkan sinar UV. Komposisi massa optimum TiO2-N dalam zeolit adalah (0,4-0,6)g TiO2-N/g zeolit dengan degradasi methylene blue sebesar 96%, lama penyinaran optimum sinar matahari adalah 50 menit dengan degradasi sebesar 96,81% serta efektivitas reuse TiO2-N/zeolit hingga pemakaian keempat memberikan hasil degradasi diatas 50%.
English Abstract
Purpose of this research is synthesis photocatalyst TiO2-N/zeolite and study the effect of light, mass composition of TiO2-N in zeolite, time irradiation and effectiveness of reuse photocatalyst for degradation methylene blue. TiO2-N/zeolite prepared by sonication method by mixing TiO2 and urea (10:1) to form TiO2-N then impregnated into zeolite, with variations mass composition of TiO2-N is (0,6; 1,2; 1,8; 2,4; 3,0 g to 3 g of zeolite). Photocatalysts characterized by FTIR spectrophotometer, UV-Vis Diffuse Reflectance and Particle Size Analyzer. The type of light used is UV light, sunlight and comparison at dark conditions. The photocatalytic process is done through photodegradation in 25 mL of methylene blue 20 mg/L with 50 mg photocatalyst and irradiated for 50 minutes. Variation time radiation performed for 5, 10, 20, 30, 40, 50, 60, 90 and 120 minutes using photocatalysts with optimal composition (0,6 g TiO2-N/g zeolite). The concentration of methylene blue before and after irradiation were measured using a UV-Vis spectrophotometer at λ 664 nm. The results showed that based on FTIR characterization the formation of TiO2-N in zeolite indicated by the absorption at wave numbers 1637,45 cm-1 and 680,83 cm-1. Based on UV-Vis DR characterization obtained band gap energy of TiO2-N/zeolite is 3,33 eV, from PSA characterization the particle size of TiO2-N/zeolite between (1,04-37,63) ?m with content of N is 1,99%. Sunlight irradiation results are best degradation compared to UV light. Mass composition optimum of TiO2-N in zeolite is (0,4-0,6) g TiO2-N/g zeolite with 96% degradation of methylene blue, time irradiation optimum of sunlight is 50 minutes with 96,81% degradation and the reuse effectiveness of TiO2-N/zeolite until the fourth usage results degradation above 50%.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2015/11/051501573 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Endang Susworini |
| Date Deposited: | 25 Feb 2015 08:16 |
| Last Modified: | 25 Feb 2015 08:16 |
| URI: | http://repository.ub.ac.id/id/eprint/154129 |
Actions (login required)
 |
View Item |