SilviaPermatasari, Oda (2015) Pengaruh Komposisi N Pada Fotokatalis TiO2-N dan Volume H2O2 30% terhadap Degradasi Methyl Orange Secara Fotokatalitik. Sarjana thesis, Universitas Brawijaya.
Abstract
Fotokatalis merupakan material semikonduktor yang mampu mempercepat laju reaksi oksidasi maupun reduksi melalui reaksi fotokimia. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh variasi komposisi N pada fotokatalis TiO2-N, pengaruh variasi volume penambahan H2O2 30%, serta pengaruh lama penyinaran terhadap degradasi zat warna methyl orange 10 mg/L. Karakterisasi fotokatalis dilakukan dengan menggunakan Spektroskopi FTIR, UV- Vis Diffuse Reflactance, dan Particle Size Analyzer. Penentuan konsentrasi methyl orange hasil degradasi diukur dengan spektrofotometer UV Visible pada panjang gelombang 464,3 nm. Sintesis fotokatalis TiO2-N, dilakukan dengan perbandingan mol TiO2:urea 10:0,5; 10:1,0; 10:1,5; 10:2,0; dan 10:2,5. Variasi volume penambahan H2O2 30% adalah 0, 0,25; 0,5; 0,75; dan 1,0 mL. Uji aktivitas fotokatalis dilakukan menggunakan 80 mg fotokatalis TiO2-N dalam 25 mL methyl orange 10 mg/L pada kondisi sinar matahari dan sinar UV (352 nm) sebagai sumber energi photon selama 3 jam. Hasil karakterisasi menunjukkan penambahan dopan N menyebabkan peningkatan ukuran partikel dan penurunan band gap TiO2 sebesar 0,014 eV. Spektra IR menunjukkan adanya serapan khas N pada bilangan gelombang 1637,45 cm-1. Hasil penelitian menunjukkan komposisi TiO2:urea 10:1,0 paling optimum pada kondisi sinar matahari dengan degradasi sebesar 90,41%. Volume penambahan optimum 0,75 mL H2O2 30% dapat meningkatkan aktivitas fotokatalitik sebesar 18,96%. Variasi lama penyinaran berbanding lurus dengan degradasi methyl orange. Lama penyinaran optimum terjadi pada 180 menit pada kondisi sinar matahari dan 360 menit pada kondisi sinar UV.
English Abstract
Photocatalyst is a material semiconductor that can accelerate the rate of oxidation and reduction reactions through a photochemical reaction. The purposes of this study are determine effect of variation N in TiO2-N, effect of volume variation of H2O2 30%, and effect of time irradiation to the degradation of methyl orange 10 mg/L. Photocatalyst characterizations by FTIR, UV Visible Diffuse Reflectance, and Particle Size Analyzer. The concentration of methyl orange after degradation is determined by UV Visible Spectrophotometer at 464, 3 nm. Synthesis TiO2-N is performed with the mole ratio of TiO2:urea 10:0,5; 10:1,0; 10:1,5; 10:2,0; and 10:2,5. Volume variation of H2O2 30% are 0; 0,25; 0,5; 0,75; and 1,0 mL. Photocatalytic activity test is performed using 80 mg of photochatalyst TiO2-N in 25 mL methyl orange 10 mg/L with sun light and UV rays (352 nm) as a source of photon energy in 3 hours irradiation. The results are showed that addition N increase the particle size of TiO2 and band gap energy decrease 0,014 eV. IR spectra is showed the presence of characteristic absorption of N in TiO2 at wave number 1643,24 cm-1. The results are showed optimum composition of TiO2: urea 10: 1,5 in sun rays condition with degradation methyl orange is 90,41%. Addition 0,75 mL H2O2 30% can increase photocatalytic up to 18,96%. Time irradiation is linier with degradation methyl orange. Optimum irradiation is 360 minutes in VU rays condition and 180 minutes in sun light condition.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2015/101/051501534 |
| Subjects: | 500 Natural sciences and mathematics > 510 Mathematics |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Matematika |
| Depositing User: | Samsul Arifin |
| Date Deposited: | 25 Feb 2015 12:11 |
| Last Modified: | 25 Feb 2015 12:11 |
| URI: | http://repository.ub.ac.id/id/eprint/154120 |
Actions (login required)
 |
View Item |