Wathi, AyuFahimahDiniyah (2014) Pengaruh Perbandingan Massa Ca:P dan Temperatur Kalsinasi terdahap Sintesis Hidroksiapatit dari Tulang Sapi dengan Metode Kering. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini bertujuan untuk mengetahui pengaruh perbandingan massa Ca:P dan temperatur kalsinasi terhadap sintesis biokeramik hidroksiapatit, Ca10(PO4)6(OH)2, dari tulang sapi. Kalsium dan fosfor dalam tulang sapi digunakan sebagai unsur utama pembentuk hidroksiapatit. Sintesis hidroksiapatit dilakukan melalui metode kering, yaitu reaksi antara padatan dengan padatan. Dalam penelitian ini digunakan bahan baku tulang sapi yang telah diabukan dan (NH4)2PO4 sebagai sumber fosfor. Abu tulang sapi dan (NH4)2PO4 dengan variasi perbandingan massa Ca:P sebesar 1:0,065; 1:0,038; dan 1:0,032 diaduk menggunakan magnetic stirrer selama tiga jam. Campuran tersebut dipanaskan dalam furnace selama dua jam dengan variasi temperatur yang digunakan adalah 800, 1000, dan 1250 oC. Hasil penelitian menunjukkan bahwa hidroksiapatit yang optimal diperoleh pada perbandingan massa Ca:P sebesar 1:0,065 dan temperatur kalsinasi 1000 oC. Hasil karakterisasi dengan XRF menunjukkan bahwa kadar fosfor dalam hidroksiapatit meningkat dari kadar fosfor dalam abu tulang sapi sebesar 0,31%, sedangkan kadar kalsium dalam hidroksiapatit menurun dari kadar kalsium dalam abu tulang sapi sebesar 3,6%. Karakterisasi dengan XRD menunjukkan puncak-puncak 2θ yang merupakan puncak khas dari hidroksiapatit. Karakterisasi menggunakan FTIR menunjukkan pita serapan gugus PO4 3-, gugus OH- bending, dan karbonat. Hasil karakterisasi dengan SEM-EDX menunjukkan bahwa hidroksiapatit hasil sintesis metode kering memiliki ukuran partikel sebesar 0,615 μm dan rasio Ca:P sebesar 1,837
English Abstract
This research aims to study the influence of Ca:P mass ratio and calcination temperature on the synthesis of hydroxyapatite, Ca10(PO4)6(OH)2, made from cow bone. Calcium and phosphorus in the bone are used as the main ingredients of hydroxyapatite. The hydroxyapatite is synthesized using dry method, in which the reaction is conducted in solid state. In this research, the bones, which has been made into ashes, and (NH4)H2PO4, as a source of phosphorus, were used. The bone ash and (NH4)H2PO4 were stirred for 3 hours using magnetic stirrer in variation of Ca:P mass ratio of 1:0.065; 1:0.038; and 1:0.032. The mixture was heated in a furnace for 2 hours in calcination temperature variations of 800, 1000, and 1250 °C. The results showed that the optimum hydroxyapatite were obtained from Ca:P mass ratio of 1:0.065 and calcination temperature of 1000°C. XRF analysis showed that the concentration of phosphorus in hydroxyapatite is increasing by 0.31% than those measured in cow bone ash. In contrast, the concentration of calcium in hydroxyapatite is decreasing by 3.6% than those measured in cow bone ash. Furthermore, XRD analysis of the product showed peaks of 2θ, which are typical to hydroxyapatite. FTIR analysis confirms the presence of PO4 3-, bending OH-, and CO3 2- groups, and SEMEDX analysis suggests that particle size of synthesized hydroxyapatite using dry method is 0.615 μm with a Ca:P ratio of 1.837.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2014/97/05141210 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 24 Feb 2014 12:19 |
| Last Modified: | 24 Feb 2014 12:19 |
| URI: | http://repository.ub.ac.id/id/eprint/154114 |
Actions (login required)
 |
View Item |