Anggraeny, BaiqOctavianaDwi (2014) Pembuatan Kitosan Makropori Menggunakan Garam Dapur Sebagai Porogen Dan Aplikasinya Terhadap Adsorpsi Methyl Orange. Sarjana thesis, Universitas Brawijaya.
Abstract
Telah dilakukan kajian mengenai adsorpsi kitosan makropori terhadap methyl orange dengan tujuan untuk menentukan pH optimum, waktu kontak optimum, dan pengaruh jumlah porogen terhadap kemampuan adsorpsi kitosan makropori terhadap methyl orange pada kondisi optimum. Pembuatan kitosan makropori dilakukan dengan penambahan agen ikat silang epichlorohydrin 80 mg dan porogen dari NaCl (garam dapur) dengan komposisi 5, 10, dan 15 g. Adsorpsi oleh kitosan makropori sebanyak 0,2 g dalam 100 ml larutan methyl orange 20 ppm pada kondisi pH3-8, dan lama pengocokan 1-180 menit dengan kecepatan pengocokan 100 rpm. Karakterisasi untuk mengetahui perbedaan karakter fisik dari kitosan makropori dan kitosan tanpa porogen sebagai kontrol dilakukan dengan menggunakan SEM (Scanning Electron Microscopy) dan FTIR. Hasil penelitian menunjukkan bahwa pH optimum terjadi pada pH 3 dengan persentase terserap 91,5%. Sedangkan waktu kontak optimum terjadi pada menit ke-180 dengan konstanta laju adsorpsi sebesar 0,0531 menit-1. Kitosan makropori dengan komposisi porogen 15 g memiliki persentase terserap yang lebih besar yaitu 94,0% berbeda jauh dengan kitosan tanpa porogen yang menghasilkan persentase terserap sebesar 39,2%
English Abstract
The study of methyl orange adsorption onto chitosan macroporous was performed in order to determine the optimum pH, optimum contact time, and the effect of porogen amount of adsorben to absorb methyl orange in optimum condition. Chitosan macroporous was prepared by adding epichlorohydrin 80 mg as crosslinker and NaCl 5, 10, and 15 g as porogen. Chitosan macroporous adsorption was carried by 0.2 g of chitosan into 100 ml of 20 ppm methyl orange solution at pH about 3 - 8, and contact time 1-180 minutes with agitation speed was 100 rpm. Characterization process used SEM (Scanning Electron Microscopy) and FTIR, to determine the physical character difference of chitosan as a control and chitosan macroporous. The results showed that the optimum pH occured at pH 3 with adsorption percentage was 91.5 %. While the optimum contact time occured at 180 minutes with adsorption rate constant (k) 0.0531 minutes-1. The chitosan macroporous contain 15 g of porogen has greater adsorption than others, with adsorption percentage was 94.0%. It was very different than chitosan without porogen which has adsorption percentage 39.2 %
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2014/63/051400908 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 11 Feb 2014 09:47 |
| Last Modified: | 11 Feb 2014 09:47 |
| URI: | http://repository.ub.ac.id/id/eprint/154078 |
Actions (login required)
 |
View Item |