Pratama, OkyYoga (2014) Pengaruh pH, Waktu Kontak, dan Konsentrasi pada Adsorpsi Zn(II) Menggunakan Kitin Terikat Silang Glutaraldehid. Sarjana thesis, Universitas Brawijaya.
Abstract
Telah dilakukan penelitian tentang pengaruh pH, waktu kontak, dan konsentrasi pada adsorpsi Zn(II) menggunakan kitin terikat silang glutaraldehid. Penelitian diawali dengan pembuatan kitin terikat silang glutaraldehid. Kitin yang dihasilkan kemudian dikarakterisasi menggunakan FT-IR dan SEM-EDX untuk mengetahui gugus-gugus fungsional dan bentuk morfologi pada kitin yang terikat silang glutaraldehid. Penentuan pH optimum dilakukan pada variasi pH 2, 3, 4, 5, 6, dan 7. Penentuan lama kontak optimum dilakukan dengan variasi lama waktu kontak 20, 40, 60, 80, 100, dan 120 menit. Penentuan kapasitas adsorpsi kitin terikat silang glutaraldehid dilakukan dengan memvariasikan konsentrasi ion logam Zn(II) pada 200, 250, 300, 350, dan 400 ppm. Hasil karakterisasi kitin terikat silang glutaraldehid menunjukkan bentuk morfologi permukaan yang lebih rapat, meningkatnya persentase unsur karbon, munculnya serapan gugus C=N pada bilangan gelombang 1627,81 cm-1 dan menurunnya nilai derajat deasetilasi dari 35,34% menjadi 24,05%. Kondisi optimum adsorpsi Zn(II) terjadi pada pH 6 dengan persen Zn(II) teradsorpsi sebesar 86,61% dan waktu kontak 60 menit dengan persen Zn(II) teradsorpsi sebesar 84,38%. Kapasitas adsorpsi kitin terikat silang glutaraldehid terhadap Zn(II) sebesar 53,45 mg/g.
English Abstract
Research about the effect of pH, contact time, and concentration on the adsorption of Zn(II) using chitin cross-linked glutaraldehyde has done. This research was started by making chitin cross-linked glutaraldehyde. Chitin was characterized using FT-IR and SEM-EDX to determine functional group and morphology of chitin cross-linked glutaraldehyde. Determining pH has done in variation pH 2, 3, 4, 5, 6, and 7. Determining optimum time has done in variation contact time 20, 40, 60, 80, 100, and 120 minute. Determining capacity adsorption of chitin cross-linked glutaraldehyde has done in variation concentration of Zn(II) solution at 200, 250, 300, 350, and 400 ppm. The results of characterization chitin cross-linked glutaraldehyde showed that the surface morphology more dense, the increased percentage of carbon, appeared absorption of C=N at waves number 1627.81 cm-1 and decreased the value of deacetylation degree from 35.34% to 24.05%. The optimum condition of adsorption Zn(II) happened at pH 6 with percent adsorption 86.61 % and contact time optimum at 60 minute with percent adsorption 84.38 %. Capacity adsorption of chitin crosslinked glutaraldehyde on Zn(II) adsorption is 53.45 mg/g.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2014/367/051406264 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 17 Sep 2014 07:44 |
| Last Modified: | 21 Oct 2021 06:18 |
| URI: | http://repository.ub.ac.id/id/eprint/154004 |
Preview |
Text
OKY_YOGA_PRATAMA_0810920058.pdf Download (2MB) | Preview |
Actions (login required)
 |
View Item |