Penelitian tentang adsorpsi seng(II) menggunakan biomassa Azolla microphylla yang diesterifikasi dengan asam sitrat telah dilakukan. Tujuan dari penelitian ini adalah untuk menentukan suatu kondisi optimum adsorpsi seng(II) oleh biomassa Azolla microphylla yang telah diesterifikasi dengan asam sitrat dan kapasitas adsorpsi biomassa hasil esterifikasi terhadap seng(II). Esterifikasi biomassa Azolla microphylla dilakukan dengan mensuspensikan 5 g biomassa dalam 50 mL larutan asam sitrat 0,8 M kemudian dikeringkan dalam oven pada 60 oC. Setelah itu, suspensi kering dipanaskan pada 120oC selama 3,5 jam. Percobaan adsorpsi menggunakan sistem batch pada biomassa kering dengan ukuran 120-150 mesh dengan variasi pH 3; 4; 5; 6; dan 7, variasi waktu kontak 30; 45; 60; 75; 90; dan 120 menit, dan variasi konsentrasi seng(II) 100; 125; 150; 175; 200; 225; 250 mg/L. Kemudian konsentrasi seng(II) setelah adsorpsi ditentukan menggunakan spektrofotometer serapan atom. Hasil penelitian menunjukkan bahwa kondisi optimum adsorpsi seng(II) oleh biomassa Azolla microphylla yang telah diesterifikasi menggunakan asam sitrat terjadi pada pH 6 dan waktu kontak 45 menit. Berdasarkan persamaan adsorpsi isotermis Langmuir dapat diperoleh informasi bahwa kapasitas adsorpsi (Qmax) biomassa yang diesterifikasi (21,09 mg/g) memiliki nilai relatif sama dengan kapasitas adsorpsi biomassa yang tidak diesterifikasi (21,14 mg/g).
English Abstract
The research of adsorpsi of zinc(II) using Azolla microphylla biomass esterified with citric acid has been done. The purpose of this research was to determine the optimum conditions of zinc(II) adsorption by Azolla microphylla biomass esterified with citric acid and adsorption capacity of esterified biomass toward zinc(II). Esterification of biomass was conducted by suspending 5 g of biomass in 50 mL of 0.8 M citric acid solution followed by drying the suspension in the oven at 60 oC. Then, the dried suspension was heated at 120oC for 3.5 hours. This experiment has performed using dry biomass of 120-150 mesh with variation in pH 3; 4; 5; 6; and 7, various contact time of 30; 45; 60; 75; 90; and 120 minutes, and various zinc(II) concentration of 100; 125; 150; 175; 200; 225; 250 mg/L. Concentration of zinc(II) after adsorption were determined using atomic absoption spechtrophotometer. The results showed that the optimum conditions for the adsorption of zinc(II) by biomass Azolla microphylla esterified with citric acid occurred at pH 6 and contact time 45 minutes. According to the Langmuir adsorption isotherm equation, it was found that the adsorption capacity (Qmax) of esterified biomass (21,09 mg/g) have the same relative value that of non-esterified biomass (21,14 mg/g).
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2014/342/051405840 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 15 Sep 2014 14:33 |
| Last Modified: | 21 Oct 2021 05:47 |
| URI: | http://repository.ub.ac.id/id/eprint/153977 |
Preview |
Text
SKRIPSI_MEGA_DONA_INDRIANA.pdf Download (3MB) | Preview |
Preview |
Text
SKRIPSI_MEGA_DONA_INDRIANA.pdf Download (3MB) | Preview |
Actions (login required)
 |
View Item |