Nurfitriningsih, LatifahDwiKartika (2014) Adsorpsi Kadmium(II) Menggunakan Biomassa Azolla microphylla Diesterifikasi dengan Asam Sitrat. Sarjana thesis, Universitas Brawijaya.
Abstract
Telah dilakukan penelitian adsorpsi kadmium(II) menggunakan biomassa Azolla microphylla diesterifikasi dengan asam sitrat. Tujuan penelitian ini untuk menentukan kondisi optimum adsorpsi kadmium(II) oleh biomassa A. microphylla yang diesterifikasi dengan asam sitrat dan kapasitas adsorpsinya. Biomassa A. microphylla diesterifikasi dengan cara menambahkan 50 mL larutan asam sitrat 0,8 M ke dalam 5 gram biomassa. Suspensi yang terbentuk dikeringkan di dalam oven pada temperatur 60 oC. Selanjutnya suspensi kering dipanaskan pada 120 oC selama 3,5 jam. Karakterisasi biomassa setelah diesterifikasi dilakukan menggunakan FT-IR dan SEM-EDX. Adsorpsi dilakukan dengan sistem batch menggunakan biomassa kering ukuran 120-150 mesh. Percobaan dilakukan dengan variasi pH 3; 4; 5; 6; dan 7, waktu kontak 30; 45; 60; 75; 90; dan 120 menit, serta konsentrasi kadmium(II) 50; 75; 100; 125; 150; 175; 200; 225; dan 250 mg/L. Penentuan konsentrasi kadmium(II) setelah adsorpsi dilakukan menggunakan spektrofotometer serapan atom. Hasil penelitian menunjukkan bahwa kondisi optimum adsorpsi kadmium(II) oleh biomassa A. microphylla esterifikasi adalah pada pH 6 dengan waktu kontak 60 menit. Persamaan isotermis Langmuir menunjukkan bahwa biomassa A. microphylla yang diesterifikasi mempunyai kapasitas adsorpsi (Qmax) lebih besar (58,1395 mg/g) dibanding kapasitas adsorpsi biomassa yang tidak diesterifikasi (46,7290 mg/g).
English Abstract
Research on the adsorption of cadmium(II) using A. microphylla biomass esterified with citric acid has been performed. The aims of research to determine the optimum conditions of cadmium(II) adsorption by biomass A. microphylla esterified with citric acid and adsorption capacity. A. microphylla esterified by added 50 mL 0,8 M of citric acid solution into 5 grams of biomass. The suspension was dried in the oven at 60 oC. Then, dried suspension was heated at 120 oC for 3,5 hours. Esterified biomass was characterized using FT-IR and SEM-EDX. Adsorption was performed using batch system with a mesh size of 120-150 dry biomass. Variation of pH used are 3, 4; 5; 6; and 7, contact time used are 30; 45; 60; 75; 90; and 120 minutes, concentration of cadmium(II) used are 50; 75; 100; 125; 150; 175; 200; 225; and 250 mg/L. Determination of the concentration of cadmium(II) after adsorption was measured using atomic absorption spectrophotometer. The results showed optimum conditions of cadmium(II) adsorption by A. microphylla esterified with citric acid at pH 6 with 60 minutes contact time. Adsorption capacity from Langmuir isotherm equation shows the adsorption capacity of the esterified A. microphylla biomass was more (Qmax) larger (58,1395 mg/g) than the adsorption capacity of the biomass non esterified (46,7290 mg/g).
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2014/328/051405826 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 15 Sep 2014 09:12 |
| Last Modified: | 21 Oct 2021 05:33 |
| URI: | http://repository.ub.ac.id/id/eprint/153961 |
Preview |
Text
SKRIPSI_LATIFAH_DWI_KARTIKA_NURFITRININGSIH.pdf Download (3MB) | Preview |
Actions (login required)
 |
View Item |