Wulandari, Ika Oktavia (2014) Studi Pengaruh Konsentrasi ZnO pada Zeolit terhadap Degradasi Methylene Blue secara Fotokatalitik. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini dilakukan untuk mengetahui pengaruh konsentrasi ZnO yang terimpregnasi pada zeolit dalam penentuan konstanta laju fotodegradasi methylene blue, mengetahui efektivitas penggunaan kembali fotokatalis, serta karakterisasi fotokatalis. Fotokatalis disintesis melalui metode impregnasi dengan menggunakan prekursor larutan Zn(NO3)2. Prekursor disintesis dengan melarutkan Zn(NO3)2.4H2O dalam etanol 96% (v/v). Impregnasi ZnO dilakukan pada komposisi 45 ml Zn(NO3)2/3 gram zeolit. Lima variasi konsentrasi fotokatalis ZnO pada zeolit yang dihasilkan dari proses impregnasi adalah 0,3; 0,75; 1,5; 2,25; dan 3,0 mmol ZnO/g zeolit. Hasil karakterisasi dengan DRS menunjukkan energi celah untuk katalis ZnO pada zeolit adalah 3,06 eV. Dari SAA diperoleh luas permukaan zeolit teraktivasi dan ZnO pada zeolit berturut-turut sebesar 113,689 dan 51,144 m2/g. Identifikasi keberadaan ZnO pada zeolit dengan menggunakan FTIR ditunjukkan dengan puncak yang muncul pada bilangan gelombang 470,63 dan 941,26 cm-1. Hasil uji fotokatalitik menunjukkan konsentrasi ZnO berpengaruh terhadap konstanta laju fotodegradasi. Konsentrasi ZnO yang menghasilkan konstanta laju terbesar adalah ZnO 0,75 mmol/g zeolit, dengan nilai konstanta laju sebesar 0,22 menit-1, dan dengan efektivitas empat kali penggunaan kembali (reuse).
English Abstract
The main purpose of this research were to investigate the effect of impregnated ZnO onto zeolite for determining methylene blue photodegradation rate constant, photocatalyst reuse effectivity, as well as it characteristics. Photocatalyst was synthesized using impregnation method with Zn(NO3)2 as precursor. The precursor was made by dissolving Zn(NO3)2.4H2O into 96% ethanol (v/v). ZnO impregnation process was conducted according to 45 ml Zn(NO3)2/3 grams zeolite. Five concentrations generated here were 0.3; 0.75; 1.5; 2.25; and 3.0 mmol ZnO/g zeolite. Photocatalyst characteristics were identified by using DRS, SAA, and FTIR. The band gap value known from DRS was 3.06 eV. Furthermore, activated zeolite and zeolite impregnated with ZnO had 113.689 and 51.144 surface areas respectively. In addition, the peak appeared at 470.63 and 941.26 cm-1 from FTIR spectra indicated that ZnO was impregnated onto zeolite successively. The result showed that 0.75 mmol ZnO/g zeolite gave the highest amounts of rate constant value which is 0.22 minutes-1 with four time reuses. These result concluded that ZnO did gave significant effect to the photodegradation rate constant.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2014/15/051400731 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 07 Feb 2014 10:28 |
| Last Modified: | 11 Apr 2022 05:04 |
| URI: | http://repository.ub.ac.id/id/eprint/153765 |
Preview |
Text
SKRIPSI_IKA_OKTAVIA_WULANDARI.pdf Download (3MB) | Preview |
Actions (login required)
 |
View Item |