Sutantri, RatihEndah (2014) Studi Pengaruh Laju Pemanasan Pada Penumbuhan Lapisan Zinc Phthalocyanine Znpc) Di Atas Quartz Crystal Microbalance (Qcm) Dengan Metode Evaporasi. Sarjana thesis, Universitas Brawijaya.
Abstract
Quartz Crystal Microbalance merupakan sensor massa berukuran mikro sampai dengan nanogram yang tengah dikembangkan sebagai biosensor. QCM memiliki kelemahan mudah teroksidasi dan permukaannya kurang rata sehingga dapat mengganggu sistem kerjanya. QCM perlu dilapisi permukaannya untuk melindungi dan mengikat biomolekul yang akan dideteksi. Pada penelitian ini dilakukan pelapisan ZnPc pada permukaan QCM yang sebelumnya telah dilapisi polistiren terlebih dahulu. Penumbuhan lapisan ZnPc dilakukan dengan metode evaporasi. Sumber deposisi berupa ZnPc yang dilarutkan dalam dimetilformamida (DMF) yang dimaksudkan untuk mempermudah proses evaporasi. Salah satu parameter yang mempengaruhi proses evaporasi adalah laju pemanasan pada sumber deposisi yang variasi besarnya mempengaruhi morfologi dan komposisi lapisan yang terbentuk. Morfologi lapisan yang ditunjukkan oleh mikroskop optik dan SEM memperlihatkan pada laju pemanasan kondisi 1 terkonsentrasi di tengah, sementara pada laju pemanasan kondisi 2 dan kondisi 3 menghasilkan lapisan yang lebih merata. Hasil EDX menunjukkan komposisi lapisan yang terbentuk pada permukaan QCM bukan merupakan lapisan ZnPc murni karena jumlah atomnya yang belum sesuai dengan rumus molekul ZnPc.
English Abstract
Quartz Crystal Microbalance is a micro and nanogram mass detector which is developed as biosensor. QCM is easyly oxidized and has rough surface. It makes QCM can not work well. QCM surface needs to be coated to protect and bind biomolekul which will be detected. In this research had coated ZnPc onto QCM surface which had been coated by polystirene before. The growth of ZnPc film is by evaporation method. Deposition source is ZnPc which was dissolved in dimetylformamide (DMF) to make evaporation easier. The one of evaporation method parameters is heat rates which is transferred to deposition source. The variations of heat rates have effect to morphologies and compositions of thin film. The morphologies of thin thilm are showed by microscope optic and SEM. Deposition with heat rates at first condition produced films which piled up in one focus, whereas deposition at second condition and third condition produced smooth and flat films. The result of EDX showed that thin film compositions are not pure ZnPc film because numbers of atom of films on the QCM are not as much as empirical molecular of ZnPc.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2013/391/051401319 |
| Subjects: | 500 Natural sciences and mathematics > 530 Physics |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 24 Feb 2014 14:51 |
| Last Modified: | 25 Oct 2021 02:55 |
| URI: | http://repository.ub.ac.id/id/eprint/153658 |
Preview |
Text
1_februari.pdf Download (3MB) | Preview |
Actions (login required)
 |
View Item |