Wahyuni, DiniTri (2011) Sintesis dan Karakterisasi Kristal Tunggal Timbal(II) Oksalat Hidrat (PbC2O4.xH2O) Dalam Gel Metasilikat dengan Supernatan Timbal(II) Nitrat (Pb(NO3)2). Sarjana thesis, Universitas Brawijaya.
Abstract
Kristal tunggal timbal(II) oksalat (PbC2O4.xH2O) memiliki struktur berulang karena adanya ion oksalat yang membentuk khelat ligan jembatan. Teknik media gel metasilikat memungkinkan kristal tunggal PbC2O4.xH2O untuk disintesis dengan keunggulan inti kristal yang terbentuk sedikit dan ukurannya lebih besar. Penelitian ini dilakukan untuk mensintesis kristal tunggal PbC2O4.xH2O dalam gel metasilikat serta mempelajari karakter kristal hasil sintesis pada kondisi optimum. Sintesis kristal tunggal PbC2O4.xH2O dalam media gel metasilikat dilakukan dengan metode tabung-U dengan supernatan Pb(NO3)2 di salah satu sisi dan supernatan Na2C2O4 disisi lain (dengan rasio 1:1) dengan waktu pertumbuhan kristal selama 3 minggu. Variasi pH awal pembentukan gel dilakukan pada rentang pH 4,5-5,1 sedangkan variasi konsentrasi supernatan adalah 0,05-0,20M. Kemudian kristal tunggal hasil sintesis pada kondisi optimum dikarakterisasi dengan SEM, spektrofotometer inframerah, difraktometer sinar-X dan SSA. Kondisi optimum sintesis yang diperoleh meliputi pH optimum awal pembentukan gel yaitu 4,8 dan konsentrasi supernatan Pb(NO3)2 dan Na2C2O4 yaitu 0,10 M. Massa kristal hasil sintesis pada kondisi optimum adalah 0,0133 g dengan efisiensi 23,34%. Kristal hasil sintesis berwarna putih berkilau, rapuh, berbentuk seperti jarum dengan panjang sekitar 678 mikron dan larut dalam HNO3 pekat. Karakterisasi secara kualitatif dengan spektrofotometer inframerah dan difraktometer sinar-X menunjukkan kristal hasil sintesis adalah kristal tunggal timbal(II) oksalat hidrat (PbC2O4.xH2O) dengan sistem kristal triklinik. Karakterisasi secara kuantitatif dengan SSA menunjukkan kadar atom Pb adalah 59,32%.
English Abstract
Lead(II) oxalate (PbC2O4.xH2O) single crystal has repeated structure due to chelated bridging ligand of oxalate. Gel technique is enable for synthesizing PbC2O4.xH2O single crystal with the advantage of forming only few crystal nucleii in large size. The purpose of this research are to synthesize PbC2O4.xH2O single crystal in metasilicate gel and to study the properties of synthesized crystal at optimum conditions. PbC2O4.xH2O single crystal has been syntesized in metasilicate gel with U-tube method in which Pb(NO3)2 as supernatant is placed in one side and Na2C2O4 as supernatant in the other side (in 1:1 ratio) with growth time of three weeks. The pH variation have been done at range pH of 4.5-5.1 and the concentration supernatant was 0.05-0.20 M. The crystals that obtained in the optimum condition were characterized with SEM, infrared spectrophotometer, X-ray difractometer and AAS . The optimum conditions of single crystal synthesis was at pH 4.8 and concentration of Pb(NO3)2 and Na2C2O4 as supernatant was 0.10 M. The mass of synthesized crystal at optimum condition was 0.0133 g with efficiency of 23.34%. The physical properties of synthesized crystal are white shiny, needle-shaped with length 678 micron and soluble in concentrated HNO3. The qualitative characterization with infrared spectophotometer and X-ray difractometer indicate that the synthesized crystal was lead(II) oxalate hydrate (PbC2O4.xH2O) with triclinic system crystal. The quantitative characterization was done with AAS and shows lead content of 59.32%.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2011/223/051103330 |
| Subjects: | 500 Natural sciences and mathematics > 540 Chemistry and allied sciences |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Unnamed user with email repository.ub@ub.ac.id |
| Date Deposited: | 28 Oct 2011 10:38 |
| Last Modified: | 22 Oct 2021 07:53 |
| URI: | http://repository.ub.ac.id/id/eprint/152674 |
Preview |
Text
051103330.pdf Download (4MB) | Preview |
Actions (login required)
 |
View Item |