Reduksi Kadar Tembaga (Cu) Dengan Metode Elektrolisis Pada Pengolahan Limbah Cair Priting Circuit Board (PCB).

Arini, Silfi (2015) Reduksi Kadar Tembaga (Cu) Dengan Metode Elektrolisis Pada Pengolahan Limbah Cair Priting Circuit Board (PCB). Sarjana thesis, Universitas Brawijaya.

Abstract

Industri Elektronika Merupakan Salah Satu Industri Prioritas Nasional Yang Terus Tumbuh Dan Berkembang. Pertumbuhan Industri Elektronika Nasional Sebesar 10,9% Dan Memiliki Nilai Ekspor Sebesar US $ 9,084 Miliar Menduduki Tempat Kedua Setelah Ekspor TPT (Tekstil Produk Tekstil) Serta Tingkat Produksi Rata-Rata Sebesar 65-70%. Beberapa Industri Komponen Elektronika Turut Mendukung Tumbuh Kembangnya Salah Satunya PCB. Industri Printing Circuit Board (PCB). Jika Ditinjau Dari Sumbernya, Limbah Industri PCB Dihasilkan Dari Tiga Sumber Cemaran . Pertama Adalah Limbah Cair Dengan Kandungan Alkali (Naoh). Jumlah Limbah Ini Tidak Hanya Karakteristiknya Saja Yang Alkali, Warna Limbah Cair Ini Umumnya Berwarna Putih Kebiruan. Limbah Cair Kedua Adalah Cucian Lembaran PCB Dan Limbah Terakhir Adalah Larutan Bekas Rendaman PCB Yang Telah Pekat. Air Cucian Lembaran PCB Yang Telah Di Printing Memiliki Karakteristik Kandungan Ion Tembaga Dengan Ph Kisaran 4, Namun Larutan Bekas Rendaman PCB Ini Memiliki Karakteristik Yang Jauh Lebih Pekat Dan Korosif Daripada Air Cucian. Berdasarkan Kandungan Material B3 Yang Tinggi Terutama Pada Buangan Larutan Bekas Rendaman PCB Atau Cairan Pekat Maka Limbah Cair Industri PCB Wajib Dilakukan Pengolahan Sebelum Limbah Cair Dilepas Ke Lingkungan.Tujuan Penelitian Ini Adalah Untuk Mengetahui Tembaga (Cu) Yang Terlarut Dalam Limbah Cair PCB Menjadi Deposit Tembaga, Untuk Mengetahui Jenis Elektroda Yang Memberikan Effisiensi Yang Tinggi Pada Elektrodaposisi Tembaga (Cu) Pada Limbah Cair Industry PCB, Untuk Mengetahui Waktu Antara Elektroda Yang Diperlukan Pada Proses Elektrodaposisi Tembaga (Cu) Dalam Limbah Cair Industry PCB. Metode Ini Digunakan Dengan Elektrolisis Dengan Tegnagan 7,5 Volt. Jenis Penilitian Ini Adalah Eksperimen Laboratorium. Sampel Ini Berupa Elektrodaposisi Tembaga (Cu) Dengan Mengalirkan Arus Listrik Searah Pada Elektroda Yang Dicelup Dalam Limbah Cair (Proses Etcing) Pembuatan PCB. Adapun Pendekatan Yang Digunakan Dalam Penilitian Ini Adalah Pendekatan Kuantitatif Dan Menggunakan Analisis Matematik, Dengan Maksud Menganalisa Data Yang Dinyatakan Dengan Nominal. Data Kuantitatif Tersebut Diperoleh Dari Variasi Durasi Proses, Jarak Antar Elektroda, Dan Jenis Elektroda Yang Digunakan Kemudian Dari Data Akan Diturunkan Dengan Menggunakan Rumus Matematik. Berdasarkan Hasil Penelitian Maka, Tembaga (Cu) Yang Terlarut Dalam Limbah Cair PCB Dapat Menjadi Deposit Tembaga Dengan Removal 70 % - 90% Yang Dapat Dilihat Pada Lampiran 4. Elektroda Yang Memberikan Effisiensi Yang Tinggi Pada Elektrodaposisi Tembaga (Cu) Pada Limbah Cair Industry PCB Adalah Plat Baja Dengan Pada Jarak 1 Cm. Berdasarkan Hasil Pada Plat Baja Ini Mengalami Penurunan Removal 88%. Waktu Antara Elektroda Yang Diperlukan Pada Proses Elektrodaposisi Tembaga (Cu) Dalam Limbah Cair Industry PCB Pada Waktu 60 Menit, Hal Ini Dilakukan Karena Tidak Ada Lagi Peningkatan Yang Signifikan Terjadi Pada Deposit Tembaga Di Katoda. Massa Tembaga Dalam Larutan Elektrolit Telah Hampir Habis Pada Massa Tersebut.

English Abstract

Electronics Industry Is One Of The National Priorities Industry Continues To Grow And Evolve. National Electronics Industry Growth Of 10.9% And Export Value Of US $ 9.084 Billion, Second Only To The Export Of Textile (Textile Products Textile) And An Average Production Rate Of 65-70%. Some Of The Electronic Components Industry Also Contributed To The Growth Of One PCB. Printing Circuit Board (PCB). If Viewed From The Source, The PCB Industrial Waste Generated From Three Sources Of Contamination. The First Is A Liquid Waste Containing Alkali (Naoh). The Amount Of This Waste Is Not Only Characteristics Are Alkaline, Liquid Waste Color Is Usually White And Blue. The Second Is The Laundry Wastewater And Waste Pcbs Last Sheet Is A Solution That Has Been Soaked Thick PCB. PCB Sheet Washing Water That Has Been In The Printing Has The Characteristics Of A Copper Ion Content With A Ph Range Of 4, But The Solution Was Soaked PCB Has The Characteristics Of A Much More Concentrated And Corrosive Than Dishwater. Based On B3 Material Content Is High, Especially In The Waste Solution Soaked Concentrated Liquid Pcbs Or PCB Industry, The Liquid Waste Must Be Performed Prior To Treatment Of Wastewater Released Into Lingkungan.Tujuan Of This Study Was To Determine Copper (Cu) Were Dissolved In The Liquid Waste Pcbs Into Copper Deposit , To Determine The Type Of Electrode That Provides High Efficiency At Elektrodaposisi Copper (Cu) In The PCB Industry Wastewater, To Determine The Time Between The Electrodes Required To Process Elektrodaposisi Copper (Cu) In The Wastewater Industry PCB. This Method Is Used By Electrolysis With Tegnagan 7.5 Volt. Type Of This Research Is A Laboratory Experiment. This Sample Form Elektrodaposisi Copper (Cu) By Passing Electric Current To The Electrodes Are Dipped In Liquid Waste (Process Etcing) PCB Manufacture. The Approach Used In This Research Is A Quantitative Approach And Using Mathematical Analysis, With The Intention Of Analyzing The Data That Is Expressed With Nominal. Quantitative Data Were Obtained From The Variation Of The Duration Of The Process, The Distance Between The Electrodes, And The Type Of Electrode Used Then The Data Will Be Derived Using Mathematical Formulas. Based On The Research Results, Copper (Cu) Were Dissolved In The Liquid Waste PCB May Be Copper Deposit With The Removal Of 70% - 90% Of Which Can Be Seen In Appendix 4. The Electrodes That Provide High Efficiency At Elektrodaposisi Copper (Cu) In The Wastewater Industry PCB Is A Steel Plate With At A Distance Of 1 Cm. Based On The Results Of This Steel Plate Decreased 88% Removal. The Time Between The Electrodes Required To Process Elektrodaposisi Copper (Cu) In The Wastewater Industry Pcbs At 60 Minutes, This Is Done Because There Is No Longer A Significant Increase Occurred In The Copper Deposit At The Cathode. Mass Of Copper In The Electrolyte Solution Has Been Nearly Exhausted In The Mass.

Item Type:	Thesis (Sarjana)
Identification Number:	SKR/FTP/2015/99/051503164
Subjects:	300 Social sciences > 338 Production > 338.1 Agriculture
Divisions:	Fakultas Teknologi Pertanian > Keteknikan Pertanian
Depositing User:	Budi Wahyono Wahyono
Date Deposited:	08 May 2015 07:22
Last Modified:	23 Oct 2021 06:28
URI:	http://repository.ub.ac.id/id/eprint/150618

Text PENDAHULUAN_A5.docx_perbaharui.pdf Restricted to Registered users only Download (3MB)

Actions (login required)

View Item