Putra, SusantoDwi (2014) Pemanfaatan Silica Fume Limbah Sandblasting Untuk Meningkatkan Kuat Tekan Batako Pejal Dengan Taguchi Quality Engineering (Studi Kasus: Pt Boma Bisma Indra Persero). Sarjana thesis, Universitas Brawijaya.
Abstract
Sandblasting merupakan salah satu proses produksi PT. Boma Bisma Indra (Persero) yang menghasilkan limbah pasir silica fume. Karakteristik pasir silica fume limbah sandblasting memiliki bulir yang lebih kecil dari semen sehingga memungkinkan adanya reaksi kimia apabila bercampur dengan semen sehingga mempunyai kemampuan mengikat. Karakteristik dari pasir silica fume tersebut dapat dimanfaatkan menjadi bahan tambah untuk produk beton. Batako merupakan salah satu produk beton yang tersusun dari komposisi material yang meliputi agregat (pasir dan kerikil), semen, dan air. Material – material yang memiliki kemiripan karakteristik dapat menjadi bahan tambah, termasuk yang berasal dari limbah seperti pasir silica fume limbah sandblasting Metode yang digunakan dalam penelitian ini adalah Metode Taguchi. Metode Taguchi merupakan metode perbaikan kualitas untuk percobaan baru serta dapat menekan biaya seminimal mungkin. Penelitian ini dimulai dengan mencari faktor – faktor terkontrol untuk pembentukan batako dengan bahan tambah silica fume limbah sandblasting. Faktor – faktor terkontrol tersebut terdiri dari rasio faktor air semen (f.a.s) dan agregat, rasio faktor air dan semen (f.a.s), rasio agregat kasar (kerikil) dan agregat halus (pasir), serta rasio silica fume limbah sandblasting dan semen. Kemudian menentukan matriks orthogonal array sesuai dengan degree of freedom maka orthogonal array yang digunakan yaitu L9 (34). Karakteristik pada penelitian ini merupakan Large The Better dengan respon yang dicari yaitu kuat tekan batako dengan bahan tambah pasir silica fume limbah sandblasting. Berdasarkan pengujian kuat tekan batako dengan bahan tambah pasir silica fume limbah sandblasting didapatkan bahwa faktor yang signifikan yaitu dari rasio faktor air semen (f.a.s) dan agregat, rasio faktor air dan semen (f.a.s), rasio agregat kasar (kerikil) dan agregat halus (pasir), serta rasio silica fume limbah sandblasting dan semen. Berdasarkan uji ANOVA menunjukkan bahwa komposisi bahan yang digunakan pada eksperimen tidak menyebabkan penurunan pada kuat tekan batako. Sehingga silica fume limbah sandblasting dapat digunakan sebagai bahan tambah. Pengujian kuat tekan batako eksperimen konfirmasi menunjukkan rata – rata kuat tekan sebesar 10,72 Mpa yang merupakan tingkat mutu I (> 9,00) dalam SNI 03-0349-1989.
English Abstract
Sand blasting is a production process done by PT. Boma Bisma Indra (Persero) which produces waste named silica fume sand. The silica fume sand has smaller grains than the grains of cement. It allows the chemical reaction when silica fume is mixed with cement. In addition, it also has the ability to bind other components. Based on the characteristics mentioned, the silica fume sand can be utilized as a material added to concrete products. Cocrete block is one of concrete product which is composed material composition including aggregate (sand and gravel), cement, and water. Materials having similar characteristics of the material can be added as additional meterials, including those derived from waste such as fume silica sand. The method used in this study is the Taguchi Method. Taguchi method is a method of quality improvement for a new trial and for minimize production costs. The study began by searching for a controlled factor in the production process of cocrete block with silica fume material, the waste of sand blasting, as addional materials. The controled factors were the ratio of water & agregate and aggregate, ratio of water and cement, ratio of coarse aggregate (gravel) and smooth aggregate (sand), and the ratio of silica fume and cement. Then, the orthogonal array matrix based on the degree of freedom. Thus, the orthogonal array used was L9 (34). The characteristics of this study was Large The Better while the analyzed response was compressive strength of cocrete block with silica fume sand as additional materials. Based on the compressive strength test of cocrete block with silica fume sand as additional materials, it was found out that the significant factors were the ratio of water and cement and aggregate, ratio of water and cement, ratio of coarse aggregate (gravel) and smooth aggregate (sand), and the ratio of silica fume and cement. Moreover, the results of ANOVA test showed that the composition of the materials used in the experiment did not cause any reduction in the compressive strength of batako. Therefore, silica fume derived from sand blasting waste could be used as additional materials. The compressive strength of experimental batako showed 10,72 Mpa compressive strength in average which belonged to the first quality level of SNI 03-0349-1989 that was > 9,00.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FT/2014/418/051404985 |
| Subjects: | 600 Technology (Applied sciences) > 670 Manufacturing |
| Divisions: | Fakultas Teknik > Teknik Industri |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 03 Sep 2014 08:28 |
| Last Modified: | 22 Oct 2021 06:56 |
| URI: | http://repository.ub.ac.id/id/eprint/142713 |
Preview |
Text
BAB_III_-_SUSANTO_DWI_PUTRA.pdf Download (1MB) | Preview |
Preview |
Text
BAB_IV_-_SUSANTO_DWI_PUTRA.pdf Download (2MB) | Preview |
Preview |
Text
BAB_V_-_SUSANTO_DWI_PUTRA.pdf Download (1MB) | Preview |
Preview |
Text
cover_sampai_summary_-_SUSANTO_DWI_PUTRA.pdf Download (2MB) | Preview |
Preview |
Text
DAFTAR_PUSTAKA_-_SUSANTO_DWI_PUTRA.pdf Download (1MB) | Preview |
Preview |
Text
LAMPIRAN_-_SUSANTO_DWI_PUTRA.pdf Download (4MB) | Preview |
Preview |
Text
BAB_I_-_SUSANTO_DWI_PUTRA.pdf Download (1MB) | Preview |
Preview |
Text
BAB_II_-_SUSANTO_DWI_PUTRA.pdf Download (2MB) | Preview |
Actions (login required)
 |
View Item |